Clay composites for removal of SO.sub.x from flue gas streams

• US 5,160,715 A
• Filed: 10/21/1991
• Issued: 11/03/1992
• Est. Priority Date: 07/16/1990
• Status: Expired due to Term

• Current Assignee: The Board of Trustees of Michigan State University (Michigan State University)
• Original Assignee: The Board of Trustees of Michigan State University (Michigan State University)
• Inventors: Pinnavaia, Thomas J., Amarasekera, Jayantha, Polansky, Christine A.
• Primary Examiner(s): HELLER, GREGORY
• Application Number:
  US07/779,645
• Time in Patent Office: 379 Days
• Field of Search: 423/244 A, 423/244 R
• US Class Current: 423/244.08
• CPC Class Codes: B01D 53/508 by treating the gases with solids
• CPC Class Codes: B01J 20/12 Naturally occurring clays or bleaching earth
• CPC Class Codes: C01B 33/44 Products obtained from layered base-exchange silicates by ion-exchange with organic compounds such as ammonium, phosphonium or sulfonium compounds or by intercalation of organic compounds, e.g. organoclay material

Abstract

A method for preparing smectite clay alkaline earth metal hydroxide and carbonate composite materials is described. The method uses low amounts of the clay added to water to which is added calcium oxide or calcium hydroxide. Optionally the calcium carbonate is formed in situ by exposure to air or to carbon dioxide in the solution. The product is dried to form the composite material which is used to remove SO_x from flue gases.

Claims

1. A method for removing SO_x from a gas stream which comprises:

(a) providing a dry physical mixture of a basic material selected from the group consisting of an alkaline earth metal oxide and an alkali metal hydroxide and a smectite clay;

(b) mixing the dry physical mixture to insure homogeneity of the mixture;

(c) adding a minimum amount of water to the dry physical mixture to make a paste;

(d) blending the paste in a carbon dioxide atmosphere to promote the formation of an alkaline earth metal carbonate from the basic material;

(e) drying the paste at a temperature up to about 100°

C. to provide the composite material, wherein when the composite material is heated to a temperature of 500°

C. or above, the SO_x components from a gas stream are removed by the composite material upon contacting with the said gas stream at that temperature.

2. The method of claim 1 wherein the weight ratio of basic material to clay in the composite is between 1:

1 and 10;

1.

3. A method in accordance with claim 1 wherein the composite material is dried in a cake, crushed, and then sieved to separate the desired mesh sizes.

4. A method in accordance with claim 1 wherein the smectite clay is selected from the group consisting of montmorillonite, fluorohectorite, bentonite, nontronite, hectorite, saponite, and beidellite, including in Na⁺ exchange form.

5. A method in accordance with claim 1 wherein the alkaline earth is selected from the group consisting of magnesium and calcium.

6. A method in accordance with claim 1 wherein the composite is substantially calcium carbonate with minor amounts of calcium hydroxide as the basic material.