Moisture-curing, polyurethane hot-melt compositions

• US 5,173,538 A
• Filed: 10/17/1989
• Issued: 12/22/1992
• Est. Priority Date: 11/15/1988
• Status: Expired due to Term

• Current Assignee: Bostik Incorporated The Corporation Trust Company Corporate Trust Center
• Original Assignee: Bostik Incorporated (Totalenergies Se)
• Inventors: Gilch, Heinz G., Rath, Walter
• Primary Examiner(s): WOODWARD, ANA LUCRECIA
• Application Number:
  US07/422,932
• Time in Patent Office: 1,162 Days
• Field of Search: 525/458, 525/460, 525/130, 525/131, 525/440, 525/454, 525/455, 525/409, 525/403, 525/404, 525/408, 538/67, 538/60, 538/66
• US Class Current: 525/130
• CPC Class Codes: C08G 18/12 using two or more compounds having active hydrogen in the first polymerisation step
• CPC Class Codes: C08G 18/307 Atmospheric humidity
• CPC Class Codes: C08G 18/4018 Mixtures of compounds of group C08G18/42 with compounds of group C08G18/48
• CPC Class Codes: C08G 18/4804 Two or more polyethers of different physical or chemical nature
• CPC Class Codes: C08G 18/698 Mixtures with compounds of group C08G18/40
• CPC Class Codes: C08G 2170/20 Compositions for hot melt adhesives

Abstract

A quick-setting, moisture-curing hot-melt polyurethane composition having a first polyether-based polyurethane prepolymer having a Tg above room temperature and a second polyurethane prepolymer with a Tg below room temperature, the first prepolymer being prepared from a low molecular weight polyether; preferably the second prepolymer is also polyether based and prepared from a high molecular weight polyether.

Claims

1. A hot-melt polyurethane composition, comprising:

a mixture comprising a first polymer and second polymer, wherein the first polymer is a polyether-based polyurethane prepolymer having a glass transition point above room temperature, and which is prepared from an isocyanate and a polyether, the polyether polyol having a molecular weight between about 250 and 800, the mole ratio of the isocyanate groups to the hydroxyl groups of the isocyanate and the polyether polyol being from about 1.1 to 2.5, and wherein the second polymer is a polyurethane or polyurethane prepolymer and has a glass transition point below room temperature.

2. A hot-melt polyurethane composition according to claim 1, wherein the first polymer is prepared from linear or branched polyether polyols selected from the group of polypropylene oxide, polyethylene oxide, polyoxybutylenes or copolymers thereof.

3. A hot-melt polyurethane composition according to claim 1 wherein said mole ratio of the isocyano groups to the hydroxyl groups of the isocyanate and the polyether polyol is from about 1.15 to 1.5.

4. A hot-melt polyurethane composition according to claim 1 wherein the ratio of the first polymer to the second polymer in the mixture is between about 99:

1 and 50;

50.

5. A hot-melt polyurethane composition according to claim 1 wherein the first polymer is prepared from an aromatic diisocyanate.

6. A hot-melt polyurethane composition according to claim 1 wherein the first polymer is prepared from an aliphatic diisocyanate.

7. A hot-melt polyurethane composition according to claim 1 wherein the first polymer is prepared from (a) 4.4'"'"'-diphenylmethane diisocyanate (4,4'"'"'-MDI), (b) a derivative of 4,4'"'"'-MDI with a functionality higher than two, (c) 2,4-toluene diisocyanate (2,4-TDI), or (d) a derivative of 2,4-TDI with a functionality higher than two.

8. A hot-melt polyurethane composition according to claim 1 wherein the second polymer is a polyether based polyurethane prepolymer.

9. A hot-melt polyurethane composition according to claim 8 wherein the second polymer is prepared from linear or branched polyether polyols selected from the group of polypropylene oxide, polyethylene oxide, polyoxybutylenes, or copolymers thereof have a molecular weight of greater than 1000.

10. A hot-melt polyurethane composition according to claim 8 wherein the second polymer is prepared at a NCO/OH ratio between 1.1 and 2.5.

11. A hot-melt polyurethane composition according to claim 8 wherein the first polymer and the second polymer are prepared together in a single process.

12. A hot-melt polyurethane composition according to claim 1 wherein the first polymer and the second polymer are prepared separately and then combined.

13. A hot-melt polyurethane composition according to claim 1 where the polyether polyol has a molecular weight of about 400.

14. A hot-melt polyurethane composition according to claim 1 where the first polymer is formed from reagents consisting essentially of a polyether polyol and an isocyanate.

15. A hot-melt polyurethane composition according to claim 1 where the first polymer is formed from reagents comprising an isocyanate and a polyether polyol and is substantially free from other chain extenders.

16. A hot-melt polyurethane composition according to claim 1 wherein said mole ratio of the isocyano groups to hydroxyl groups of the isocyanate and the polyether polyol is from about 1.1 to 2.0.

17. A hot-melt polyurethane composition according to claim 1 wherein the second polymer is selected from the group consisting of a polyester-based polymer, a polyether-based polymer and a polybutadiene-based polymer.

18. A hot-melt polyurethane composition according to claim 1 wherein the second polymer is prepared from a polyester polyol.

19. A hot-melt polyurethane composition according to claim 1 wherein the second polymer is prepared from a polybutadiene polyol.

23. A hot-melt polyurethane composition according to claim 1 wherein the second polymer is selected from the group consisting of a polyester-based polymer, a polyether-based polymer and a polybutadiene-based polymer.

20. A hot-melt polyurethane composition, comprising:

a mixture comprising a first polymer and second polymer, wherein the first polymer is a polyether-based polyurethane prepolymer having a glass transition point above room temperature, the first polymer formed from reagents comprising an isocyanate and a polyether polyol and is substantially free from other chain extenders, the mole ratio of isocyano groups to hydroxyl groups of the isocyanate and polyether polyol being from about 1.1 to 2.5, and wherein the second polymer is a polyurethane or polyurethane prepolymer and has a glass transition point below room temperature.

21. A hot-melt polyurethane composition according to claim 20 wherein said mole ratio of isocyanate groups to hydroxyl groups of the isocyanate and the polyether polyol is from about 1.1 to 2.0.

22. A hot-melt polyurethane composition according to claim 20 wherein said mole ratio of the isocyano groups to the hydroxyl groups of the isocyanate and the polyether polyol is from about 1.15 to 1.5.

24. A hot-melt polyurethane composition according to claim 20 wherein the second polymer is prepared from a polyether polyol.

25. A hot-melt polyurethane composition according to claim 20 wherein the second polymer is prepared from linear or branched polyether polyols selected from the group consisting of polypropylene oxide, polyethylene oxide, polyoxybutylenes, and copolymers thereof having a molecular weight of greater than 1000.

26. A hot-melt polyurethane composition according to claim 20 wherein the second polymer is prepared from an isocyanate and a polyether polyol and the mole ratio of the isocyanate groups to the hydroxyl groups of the isocyanate and the polyether polyol is from about 1.1 to 2.5.

27. A hot-melt polyurethane composition according to claim 20 wherein the second polymer is a prepared from a polyester polyol.

28. A hot-melt polyurethane composition according to claim 20 wherein the second polymer is prepared from a polybutadiene polyol.