Method for inhibiting significant oxidation of a film on a substance during heating

• US 5,185,182 A
• Filed: 12/10/1990
• Issued: 02/09/1993
• Est. Priority Date: 12/10/1990
• Status: Expired due to Fees

• Current Assignee: Ford Motor Company
• Original Assignee: Ford Motor Company
• Inventors: Brown, Franklin I.
• Primary Examiner(s): Lusignan, Michael
• Assistant Examiner(s): NOT, DEFINED
• Application Number:
  US07/624,823
• Time in Patent Office: 792 Days
• Field of Search: 427/377, 427/383.1, 427/383.3, 427/383.5, 427/126.1, 427/162, 427/164, 427/165, 427/166, 65/107, 65/32.1
• US Class Current: 427/126.2
• CPC Class Codes: C03C 17/3423 at least one of the coatings comprising a suboxide
• CPC Class Codes: C03C 17/3429 at least one of the coatings being a non-oxide coating
• CPC Class Codes: G02F 1/1524 Transition metal compounds

Abstract

The present invention relates to a method for inhibiting significant oxidation of a film on a substrate during heating of the substrate. The method includes providing a metal or metal oxide film on a substrate and providing a material adjacent to the film. The substrate is then heated to a temperature sufficient to cause the substrate to bend and the material adjacent to the film reacts in such a way as to protect the metal or metal oxide film on the substrate from further significantly oxidizing.

Claims

1. A process for making an electrochromic device, comprising the steps of:

A) providing a glass substrate, including an electrochromic layer thereon;

B) placing a powder on the electrochromic layer, the powder capable of releasing a gas which substantially prevents oxidation of the electrochromic layer upon heating; and

C) heating and bending the glass substrate and associated electrochromic layer;

the powder being effective to substantially prevent oxidation of the electrochromic layer.

2. The process for making an electrochromic device according to claim 1, wherein during the step of heating and bending, the powder material releases a gas selected from the group consisting of an inert and a reducing gas adjacent the electrochromic layer.

3. The process for making an electrochromic device according to claim 1, wherein prior to step C, a second substrate including an electrode layer thereon is positioned adjacent the powder material.

4. The process for making an electrochromic device according to claim 1, wherein step C includes heating the substrate to a temperature greater than 1000°

F.

5. The process for making an electrochromic device according to claim 1, wherein the powder is selected from the group consisting of carbonyls, carbonates, hydrides, formates, borohydrides, sulfates, sulfites, ammonia compounds, hydrazine compounds, W, Mo, Cu, Ti, Ni, No, Au, Fe, V, and mixtures thereof.

6. The process for making an electrochromic device according to claim 1, wherein the glass substrate includes a conducting layer.

7. The process for making an electrochromic device according to claim 6, wherein the conducting layer is selected from the group consisting of doped tin oxide, undoped tin oxide, indium oxide, indium tin oxide, zinc oxide and mixtures thereof.

8. The process for making an electrochromic device according to claim 1, wherein the electrochromic material is a metal oxide.

9. The process for making an electrochromic device according to claim 8, wherein the metal oxide is a non-stoichiometric metal oxide.

10. The process for making an electrochromic device according to claim 9, wherein the non-stoichiometric metal oxide is selected from the group consisting of non-stoichiometric tungsten oxide, molybdenum oxide, copper oxide, nickel oxide, cobalt oxide and mixtures thereof.

11. The process for making an electrochromic device according to claim 1, wherein the electrochromic layer includes a metal film.

12. The process for making an electrochromic device according to claim 11, wherein the metal film is selected from the group consisting of Al, Ag, Cu, Ta, Zr, Mo, Zn, Sn, Ti, Cr, In, W, Mg, Ni, Fe, Si and mixtures thereof.

13. The process for making an electrochromic device according to claim 5, wherein the powder is selected from the group consisting of calcium carbonate, tungsten hexacarbonyl, and mixtures thereof.

14. A process for making an electrochromic device, comprising the steps of:

A) providing a glass substrate including a conducting layer selected from the group consisting of doped tin oxide, undoped tin oxide, indium oxide, indium tin oxide, zinc oxide, and mixtures thereof, the glass substrate having thereon an electrochromic layer selected from the group consisting of non-stoichiometric tungsten oxide, molybdenium oxide, copper oxide, nickel oxide, cobalt oxide, and mixtures thereof, the electrochromic layer optionally including a metal film selected from the group consisting of Al, Ag, Cu, Ta, Zr, Mo, Zn, Sn, Ti, Cr, In, W, Mg, Ni, Fe, Si, and mixtures thereof;

B) placing a powder selected from the group consisting of carbonyls, carbonates, hydrides, formates, borohydrides, sulfates, sulfites, ammonia compounds, hydrazine compounds, W, Mo, Cu, Ti, Ni, No, Au, Fe, V, and mixtures thereof on the electrochromic layer;

C) positioning a second glass substrate including an electrode layer thereon adjacent the powder; and

D) heating to a temperature greater than 1000°

F. and bending the glass substrate and associated electrochromic layer;

the powder being effective to substantially prevent oxidation of the electrochromic layer.

15. The process for making an electrochromic device according to claim 14, wherein the powder is selected from the group consisting of calcium carbonate, tungsten hexacarbonyl, and mixtures thereof.