Method for preparation of dense ceramic products

• US 5,188,780 A
• Filed: 04/18/1991
• Issued: 02/23/1993
• Est. Priority Date: 04/18/1991
• Status: Expired due to Term

• Current Assignee: Regents of the University of California (University of California)
• Original Assignee: Regents of the University of California (University of California)
• Inventors: Lange, Frederick F., Velamakanni, Bhaskar V.
• Primary Examiner(s): DERRINGTON, JAMES H
• Application Number:
  US07/687,251
• Time in Patent Office: 677 Days
• Field of Search: 264/63, 264/311, 264/56, 501/1
• US Class Current: 264/660
• CPC Class Codes: C04B 35/622 Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products

Abstract

A method of preparing dense ceramic product is described, wherein a coagulated network of ceramic powder particles in water is formed and then treated to increase the volume fraction of particles, thereby forming a water-saturated powder compact. The compact is formed into a desired shape and fired to provide the dense ceramic product. A coagulated network may advantageously be formed by mixing a ceramic powder with water at a pH that produces a net surface charge, to form a dispersed slurry and adding a sufficient amount of salt to the dispersed slurry to cause particles within the slurry to form the coagulated network. In view of the unique rheological properties of the powder compacts prepared from coagulated networks of ceramic powder particles, the compact may be processed into complex, near-net-shaped forms by introducing the compact into a mold and subjecting the mold to vibration, whereby the compact adopts the shape of the mold; once removed from the mold, the compact retains its shape without distortion.

Claims

1. A method of preparing a dense ceramic product, comprising:

(1) forming a coagulated network of ceramic powder particles in water by adjustment of the pH of a dispersed slurry of said ceramic powder particles in water to a pH that produces a net surface charge and addition of a sufficient amount of a salt to the dispersed slurry to form said coagulated network;

(2) treating said coagulated network of ceramic powder particles in water to increase the volume fraction of said powder particles, thereby forming a water saturated powder compact; and

(3) firing the compact to provide said dense ceramic product.

2. A method according to claim 1, wherein the compact is formed into a desired shape prior to firing.

3. A method according to claim 2, wherein said desired shape is formed by introducing the compact into a mold and subjecting the mold to vibration sufficient to induce flow of the compact, whereby the compact adopts the shape of the mold.

4. A method according to claim 1, wherein said coagulated network is formed by:

mixing a ceramic powder with water at a pH that produces a net surface charge, to form a dispersed slurry; and

adding a sufficient amount of salt to the dispersed to cause particles within the slurry to form a coagulated network.

5. A method according to claim 1, wherein the dispersed slurry comprises less than about 30 volume % ceramic powder.

6. A method according to claim 1, wherein said salt is selected from the group consisting of organic salts, inorganic salts and mixtures thereof.

7. A method according to claim 6, wherein said salt is an inorganic salt.

8. A method according to claim 7, wherein said inorganic salt is selected from the group consisting of alkali halides, alkali earth halides, ammonium halides and mixtures thereof.

9. A method according to claim 1, wherein the ceramic powder is selected from the group consisting of oxides, nitrides, carbides, borides and tellurides.

10. A method according to claim 9, wherein the ceramic powder is selected from the group consisting of alumina, zirconia, titania, silica, silicon carbide, silicon nitride, yttria, lead oxide and mixtures thereof.

11. A method according to claim 1, wherein the volume fraction of particles is increased by pressure filtration.

12. A method according to claim 1, wherein the volume fraction of particles is increased by centrifugation.

13. A method according to claim 1, wherein said firing comprises a first heating step at a first temperature sufficient to evaporate water and pyrolyze salt from the shaped compact, followed by a second heating step at a second temperature sufficient to densify the shaped compact.

14. A method according to claim 1, wherein said coagulated network is formed by:

dispersing the ceramic particles in water at a pH that produces a net surface charge, to form a dispersed slurry;

ultrasonicating the slurry to break apart agglomerates;

sedimenting the slurry to separate remaining strong agglomerates and inclusions;

siphoning off supernatant containing desired colloidal particles; and

adding a sufficient amount of salt to the supernatant to form a coagulated network.

15. A method according to claim 1, wherein said coagulated network of ceramic powder particles in water comprises at least two different types of ceramic powder particles.

16. A method according to claim 15, wherein said coagulated network is formed by:

mixing each ceramic powder separately with water at a pH that produces a net surface charge with that powder, to form a plurality of dispersed slurries;

combining said plurality of dispersed slurries to form a mixed slurry; and

adding a sufficient amount of salt to the mixed slurry to cause particles within the slurry to form a coagulated network.

17. A method according to claim 15, wherein said coagulated network is formed by:

mixing each ceramic powder separately with water at a pH that produces a net surface charge with that powder, to form a plurality of dispersed slurries;

adding a sufficient amount of salt to each of said plurality of dispersed slurries to cause particles within each slurry to form a coagulated network, thereby forming a plurality of coagulated slurries; and

combining said plurality of coagulated slurries at a high shear rate sufficient to break apart said coagulated networks and form a new coagulated network.