Method for manufacturing lenses using thin coatings

• US 5,219,497 A
• Filed: 10/18/1991
• Issued: 06/15/1993
• Est. Priority Date: 10/30/1987
• Status: Expired due to Term

• Current Assignee: Essilor International SA
• Original Assignee: Innotech, Inc. (Bimeda Holdings Ltd.)
• Inventors: Blum, Ronald D.
• Primary Examiner(s): Thurlow, Jeffery
• Assistant Examiner(s): VARGOT, MATHIEU D
• Application Number:
  US07/779,317
• Time in Patent Office: 606 Days
• Field of Search: 264/1.4, 264/1.7, 264/2.2, 264/2.5, 264/2.7, 264/22, 264/1.8, 264/162, 264/40.6, 425/808, 357/160, 357/161
• US Class Current: 264/1.38
• CPC Class Codes: B29C 2035/0827 using UV radiation
• CPC Class Codes: B29C 2035/0855 using microwave
• CPC Class Codes: B29C 2791/001 Shaping in several steps
• CPC Class Codes: B29C 35/04 using liquids, gas or steam
• CPC Class Codes: B29C 35/0888 using transparant moulds
• CPC Class Codes: B29C 39/006 Monomers or prepolymers by reaction injection moulding B29C67/246
• CPC Class Codes: B29C 39/38 Heating or cooling
• CPC Class Codes: B29C 43/18 incorporating preformed parts or layers, e.g. compression moulding around inserts or for coating articles B29C43/206 takes precedence
• CPC Class Codes: B29C 43/206 by pressing the material between two preformed layers, e.g. deformable layers
• CPC Class Codes: B29C 70/78 Moulding material on one side only of the preformed part
• CPC Class Codes: B29C 70/84 by moulding material on preformed parts to be joined joining plastic parts by moulding B29C65/70
• CPC Class Codes: B29D 11/00 Producing optical elements, e.g. lenses or prisms grinding or polishing of optical elements B24B; constructional form of optical elements G02B; optical parts of spectacles G02C7/00
• CPC Class Codes: B29D 11/00028 Bifocal lenses; Multifocal lenses
• CPC Class Codes: B29D 11/00317 Production of lenses with markings or patterns
• CPC Class Codes: B29D 11/00413 made by moulding between two mould parts which are not in direct contact with one another, e.g. comprising a seal between or on the edges B29D11/00019 - B29D11/00355, B29D11/00423, B29D11/00432 take precedence
• CPC Class Codes: B29D 11/00442 Curing the lens material
• CPC Class Codes: B29D 11/00528 Consisting of two mould halves joined by an annular gasket
• CPC Class Codes: B29D 11/0073 Optical laminates
• CPC Class Codes: B29K 2105/0002 monomers or prepolymers
• CPC Class Codes: B29K 2995/002 Coloured
• CPC Class Codes: B29L 2011/0033 : Multifocal lenses
• CPC Class Codes: Y10S 425/808 : Lens mold

Abstract

A fast, relatively inexpensive and simple method for producing a finished plastic aspheric multifocal or progressive lens from a preformed lens which has a predetermined lens correction (i.e., curvature or prescription) at its optical center. The method includes providing a mold; providing an optical photoactivated resin composition; providing a preformed plastic lens; contacting the preformed lens with the mold such that the surfaces of the preformed lens and the mold form a cavity enclosing the resin composition; and curing the resin composition upon application of heat and ultraviolet radiation. The cavity formed by the preformed lens and the mold is shaped to correspond to the desired change in curvature of the mold surface. The preformed lens may also be cast with a thin non-prescription layer which acts as a carrier for the multifocal or progressive region of the finished lens. This allows casting of lenses without employing either expensive conventional optical gaskets or back molds. The methods also allow for simpler relocation of the optical center to the proper position with respect to the multifocal or progressive prescription, without using conventional optical gaskets.

Claims

1. A method for manufacturing lens blanks comprising:

molding semi-finished lens blanks having a bonding surface of optical quality and a rear surface for grinding and polishing in a subsequent step;

said bonding surface having a known curvature;

providing a mold having a molding surface;

providing an optical quality resin composition containing an initiator activated by ultraviolet radiation, said resin composition being substantially free of thermal initiators;

providing a preformed lens backing having a lens bonding surface and a rear surface for grinding and polishing;

arranging said lens backing with said mold such that the bonding surface of said lens backing and said mold form a cavity enclosing said resin composition;

said cavity having a relatively thin space throughout and cooperating with said lens backing to form an outer surface of optical quality;

placing said resin in said cavity such that said resin has an unequal thickness between said mold and said lens backing;

curing said resin composition by applying ultraviolet radiation and heat to said resin composition, wherein said resin is cured while remaining substantially free of thermal initiators, and wherein said heat is provided in a controlled manner to equalize the degree of cure over portions of the resin having unequal thickness;

wherein the lens surface curvature of resulting lens is of substantially the same curvature as the mold used and grinding said rear portion of said lens blank and polishing said rear surface to arrive at a lens of a desired power.

2. The method according to claim No. 1, wherein said resin is of similar composition as said lens backing.

3. The method according to claim No. 2, wherein said resin comprises at least one of scratch resistant, anti-reflective or photochromatic material.

4. The method according to claim No. 2, wherein said backing comprises a scratch resistant material.

5. The method according to claim No. 2, wherein said lens backing comprises a scratch resistant material and said resin comprises a scratch resistant material.

6. The method according to claim No. 2, wherein said lens backing has a hard coat surface layer and said resin comprises a scratch resistant material.

13. The method of claim 1 wherein said resin has an index of refraction different from that of said preformed lens.

19. The method of claim 1 wherein said resin composition is devoid of a thermal initiator.

7. A method for making a finished lens having an aspheric, multifocal or progressive region, said method comprising:

a. providing a mold having a molding surface;

b. providing an optical quality resin composition containing an initiator activated by ultraviolet radiation, said resin composition being substantially free of thermal initiators;

c. providing a pre-formed plastic lens having a bonding surface;

d. said mold having a first complementary surface of a curvature different than that of the bonding surface on the preformed lens and a second surface corresponding to an aspheric, multifocal or progressive region to be added;

e. said aspheric, multifocal or progressive region constituting a portion of the mold;

placing said resin composition in said mold, arranging said preformed lens with said mold such that the bonding surface in said preformed lens and said mold form a cavity enclosing said resin composition, such that said resin has an unequal thickness between said mold and said preformed lens;

f. said cavity having a first portion cooperating with said mold to form a space therebetween of a changing thickness and a second portion cooperating with said mold to form said aspheric, multifocal or progressive region;

g. curing said resin composition by applying ultraviolet radiation and heat to said resin composition, wherein said resin is cured while remaining substantially free of thermal initiators, and wherein said heat is provided in a controlled manner to equalize the degree of cure over portions of the resin having unequal thickness; and

h. wherein the added lens curvature of said resulting lens substantially corresponds to that of the molding surface of said mold.

8. The method according to claim 7 wherein said curing step includes raising the temperature of said resin to about 160°

F.

14. The method of claim 7 wherein said resin has an index of refraction different from that of said preformed lens.

20. The method of claim 7 wherein said resin composition is devoid of a thermal initiator.

9. The method of making a finished lens, said method comprising:

a. providing a mold having a molding surface;

b. providing an optical quality resin composition containing an initiator activated by ultraviolet radiation, said resin composition being substantially free of thermal initiators;

c. providing a preformed plastic lens having a bonding surface;

d. placing said resin composition in said mold, arranging said preformed lens in said mold such that the bonding surface of said preformed lens and said mold form a cavity of non-uniform thickness enclosing said resin composition, such that said resin has an unequal thickness between said mold and said preformed lens;

e. curing said resin composition by applying ultraviolet radiation and heat to said resin composition, wherein said resin is cured while remaining substantially free of thermal initiators, and wherein said heat is provided in a controlled manner to equalize the degree of cure over portions of the resin having unequal thickness; and

f. wherein said resin when cured forms a non-uniform surface optical layer over the bonding surface of the preformed lens.

15. The method of claim 9 wherein said resin has an index of refraction different from that of said preformed lens.

21. The method of claim 9 wherein said resin composition is devoid of a thermal initiator.

10. A method for making a finished lens having an aspheric, multifocal or progressive region, said method comprising:

a. providing a mold having a molding surface;

b. providing an optical quality resin composition containing an initiator activated by ultraviolet radiation, said resin composition being substantially free of thermal initiators;

c. providing a pre-formed plastic lens having a bonding surface;

d. said mold having a first complementary surface of a curvature substantially the same as that of the bonding surface on the preformed lens and a second surface corresponding to an aspheric, multifocal or progressive regions to be added.

e. said aspheric, multifocal or progressive region constituting a portion of the mold;

placing said resin composition in said mold, arranging said preformed lens with said mold such that the bonding surface in said preformed lens and said mold form a cavity enclosing said resin composition;

f. said cavity having a first portion forming a thin space between said mold and said preformed lens; and

a second portion forming said aspheric, multifocal or progressive region such that said resin has an unequal thickness between said mold and said preformed lens;

g. curing said resin composition by applying ultraviolet radiation and heat to said resin composition, wherein said resin is cured while remaining substantially free of thermal initiators, and wherein said heat is provided in a controlled manner to equalize the degree of cure over portions of the resin having unequal thickness; and

h. wherein the added lens curvature of said resulting lens substantially corresponds to that of the molding surface of said mold.

16. The method of claim 10 wherein said resin has an index of refraction different from that of said preformed lens.

22. The method of claim 10 wherein said resin composition is devoid of a thermal initiator.

11. A method for making a lens, said method comprising:

a. providing a mold having a molding surface;

b. providing an optical quality resin composition containing an ultraviolet initiator, said resin composition being substantially free of thermal initiators;

c. providing a pre-formed plastic lens having a bonding surface thereon;

d. said mold having a first complementary surface of a curvature different than that of the bonding surface on the preformed lens;

e. placing said resin composition on said mold, arranging said preformed lens with said mold such that the bonding surface in said preformed lens and said mold form a cavity enclosing said resin composition, such that said resin has an unequal thickness between said mold and said preformed lens;

f. curing said resin composition by applying ultraviolet radiation and heat to said resin composition, wherein said resin is cured while remaining substantially free of thermal initiators, and wherein said heat is provided in a controlled manner to equalize the degree of cure over portions of the resin having unequal thickness; and

g. wherein the added lens curvature of said resulting lens substantially corresponds to that of the molding surface of said mold.

17. The method of claim 11 wherein said resin has an index of refraction different from that of said preformed lens.

23. The method of claim 11 wherein said resin composition is devoid of a thermal initiator.

12. A method for making a lens, said method comprising:

a. providing a mold having a molding surface;

b. providing an optical quality resin composition containing an ultraviolet initiator, said resin composition being substantially free of thermal initiators;

c. providing a pre-formed plastic lens having a bonding surface thereon;

d. said mold having a first complementary surface of a curvature substantially the same as that of the bonding surface on the preformed lens;

e. placing said resin composition on said mold, arranging said preformed lens with said mold such that the bonding surface in said preformed lens and said mold form a cavity enclosing said resin composition, such that said resin has an unequal thickness between said mold and said preformed lens;

f. curing said resin composition by applying ultraviolet radiation and heat to said resin composition, wherein said resin is cured while remaining substantially free of thermal initiators, and wherein said heat is provided in a controlled manner to equalize the degree of cure over portions of the resin having unequal thickness; and

g. wherein the added lens curvature of said resulting lens substantially corresponds to that of the molding surface of said mold.

18. The method of claim 12 wherein said resin has an index of refraction different from that of said preformed lens.

24. The method of claim 12 wherein said resin composition is devoid of a thermal initiator.