Aluminum brazing sheet

• US 5,232,788 A
• Filed: 02/12/1992
• Issued: 08/03/1993
• Est. Priority Date: 02/12/1992
• Status: Expired due to Fees

• Current Assignee: Alcan Incorporated (Rio Tinto Limited)
• Original Assignee: Alcan Incorporated (Rio Tinto Limited)
• Inventors: Janeway, Benjamin J., Timsit, Roland S.
• Primary Examiner(s): Walsh, Donald P.
• Assistant Examiner(s): MAI, NGOCLAN THI
• Application Number:
  US07/835,203
• Time in Patent Office: 538 Days
• Field of Search: 428/654, 428/546, 428/551, 428/552, 428/555, 428/560
• US Class Current: 428/560
• CPC Class Codes: B23K 35/0238 layered
• CPC Class Codes: B23K 35/286 Al as the principal constituent
• CPC Class Codes: B23K 35/3605 Fluorides
• CPC Class Codes: Y10T 428/12049 Nonmetal component
• CPC Class Codes: Y10T 428/12076 Next to each other
• CPC Class Codes: Y10T 428/12111 Separated by nonmetal matrix or binder [e.g., welding electrode, etc.]
• CPC Class Codes: Y10T 428/12764 Next to Al-base component

Abstract

An aluminum alloy composite sheet is described for use in brazing. It includes an aluminum alloy core sheet clad on at least one face thereof with a sheet of aluminum or aluminum alloys including those containing magnesium. The composite sheet is useful for brazing when the cladding is coated with a mixture of (i) metal particles, e.g. silicon, capable of forming a eutectic alloy with aluminum and (ii) brazing flux, e.g. a potassium fluoro-aluminate. To be effective for brazing, the magnesium must be present in such quantity that at the time of brazing, the surface being brazed contains less than 0.1% by weight magnesium.

Claims

1. An aluminum alloy composite sheet containing magnesium and suitable for use in brazing comprising:

(a) an aluminum alloy core sheet, (b) a clad layer on at least one face of said core sheet, said clad layer being a sheet of aluminum or aluminum alloy other than a brazing alloy and (c) a coating on said clad layer comprising a mixture of brazing flux material and metal particles capable of forming in situ a eutectic alloy with aluminum and the magnesium being present such that it provides an amount of less than 0.1 % by weight magnesium at the point of brazing at the time of brazing.

6. A composite sheet as claimed in claim 1 wherein the flux is a composition containing by weight:

20 to 45% potassium, 10 to 25% aluminum and 45 to 60% fluorine.

7. A composite sheet as claimed in claim 1 wherein the flux is a composition containing by weight:

40 to 70% AlF₃ and 30 to 60% KF.

2. An aluminum alloy composite sheet containing magnesium and suitable for use in brazing comprising:

(a) an aluminum alloy core sheet, (b) a clad layer on at least one face of said core sheet, said clad layer being a sheet of aluminum or aluminum alloy other than a brazing alloy and (c) a coating on said clad layer comprising a mixture of brazing flux material and metal particles capable of forming in situ a eutectic alloy with aluminum and the magnesium being present such that the metal present at the physical point of filler metal generation resulting from the reaction of the metal particles capable of forming a eutectic alloy with the metal of the cladding at the time of the brazing has a magnesium content of less than 0.1% by weight.

3. A composite sheet as claimed in claim 2 wherein the core sheet is formed of an aluminum alloy containing magnesium.

4. A composite sheet as claimed in claim 2 wherein the metal particles are particles of Si, Cu or Ge.

5. A composite sheet as claimed in claim 4 wherein the coating contains silicon and flux in the ratio of silicon:

flux in the range of 0.1;

1 to 5;

1.

8. A composite sheet as claimed in claim 5 wherein the flux is a potassium fluoroaluminate.

9. A composite sheet as claimed in claim 5 wherein the silicon particles have sizes in the range of 4 to 80 μ

m.

10. A composite sheet as claimed in claim 9 wherein the silicon particles have sizes in the range of about 5-50 μ

m.

11. A composite sheet as claimed in claim 10 wherein the coating is applied in an amount of 10 to 130 g/m².

12. A composite sheet as claimed in claim 9 wherein the coating mixture also contains additional metal particles of generally the same particle size distribution as the eutectic alloy forming metal particles, said additional metal particles being adapted to modify the properties of the brazed product.

13. A composite sheet as claimed in claim 12 wherein the additional metal particles are copper particles adapted to enhance the mechanical strength of the brazed product.

14. A composite sheet as claimed in claim 12 wherein the additional metal particles are selected from Fe, Mn, Ni, Cu, excess Si and Zn powders to provide enhanced mechanical strength, elevated temperature strength and heat treatability to the brazed product.

15. A composite sheet as claimed in claim 12 wherein the additional metal particles are selected from Cu, Zn, Ni, Co and Mn powders to provide enhanced formability properties.