Processes for producing porous polymer films and composite films

• US 5,238,636 A
• Filed: 09/30/1991
• Issued: 08/24/1993
• Est. Priority Date: 03/07/1988
• Status: Expired due to Fees

• Current Assignee: Kyowa Hakko Kogyo Company Limited (Kirin Holdings Company Limited), Rikagaku Kenkyusho
• Original Assignee: Kyowa Hakko Kogyo Company Limited (Kirin Holdings Company Limited), Rikagaku Kenkyusho
• Inventors: Furukawa, Takeo, Inaba, Yukio
• Primary Examiner(s): Timm, Catherine
• Application Number:
  US07/769,169
• Time in Patent Office: 694 Days
• Field of Search: 264/41, 264/216, 264/45.1, 264/45.8, 264/46.4, 264/48, 264/78, 264/299, 264/298
• US Class Current: 264/41
• CPC Class Codes: C08J 2201/05 Elimination by evaporation or heat degradation of a liquid phase
• CPC Class Codes: C08J 2201/0542 from an organic solvent-based polymer composition
• CPC Class Codes: C08J 9/28 by elimination of a liquid phase from a macromolecular composition or article, e.g. drying of coagulum

Abstract

A process for forming a porous polymer film formed by allowing a solvent to evaporate from a solution of polymer containing water and alcohol. It is possible to form a porous polymer film in which the size and distribution of the pores are uniformalized. Also described is a process for producing a composite film in which the pores of the porous polymer film are filled with a functional low molecular substance such as liquid crystal or dye so that the dispersion diameter of the functional low molecular substance and the distribution of the same are uniformalized. In the production of the above-mentioned porous polymer film, the size of the pores on the porous polymer film can be controlled by controlling the humidity of the forming atmosphere or the water content in the solution of polymer. It is therefore possible to obtain a fixed film having superior electrical and optical characteristics, by forming a composite film through filling the pores of the thus obtained porous polymer film with a functional low molecular substance such as liquid crystal or dye and providing electrodes on the composite film.

Claims

1. A process for producing a composite polymer film comprising;

(a) preparing a first solution of polymer by dissolving a polymer in a first solvent in which said polymer is readily dissolved;

(b) uniformly dispersing a second solvent, in which said polymer is only poorly dissolved, consisting essentially of either ethanol or methanol and water, into said first solution of polymer to form a uniform dispersion of said second solvent in said first solution of polymer;

(c) evaporating said first solvent from said uniform dispersion;

(d) producing a porous polymer film by evaporating said second solvent by drying under heat over 10°

C.; and

(e) filling said porous film with a substance.

2. A process according to claim 1, wherein said substance is liquid crystal.

3. A process according to claim 1, wherein said substance is dye.

4. A process according to claim 1, wherein said substance is a mixture system of a liquid crystal and a dye.

5. A process according to claim 1, wherein the pore size of said porous polymer film is controlled by controlling the amount of said water in said second solvent.

6. A process according to claim 5, wherein said pore size is controlled to be 10 μ

m or smaller by controlling the amount of said water.

7. The process according to claim 1, wherein said first solvent is selected from the group consisting of tetrahydrofuran, cyclohexanone, methylethylketone and dimethyl formamide;

and

said polymer is polyvinyl chloride.

8. The process according to claim 1, wherein said first solvent is selected from the group consisting of chloroform, methanol, acetone and butyl acetate;

and

said polymer is polyvinyl acetate.

9. A process according to claim 1, wherein said first solvent is selected from the group consisting of acetone, ethylacetate, tetrahydrofuran and toluene;

and

said polymer is selected from the group consisting of polyacrylate ester and polymethacrylate ester.

10. The process according to claim 1, wherein said first solvent is dimethylformamide;

and

said polymer is polyacrylonitrile.

11. The process according to claim 1, wherein said first solvent is selected from the group consisting of benzene and dimethyl formamide;

and

said polymer is polyethylene oxide.

12. The process according to claim 1, wherein said first solvent is selected from the group consisting of acetone, methylethylketone, cyclohexanone ketone, methyl acetate, methyl acrylate, ethylene oxide, propylene oxide, tetrahydrofuran, dioxane, n-butylamine, dimethylformamide, and dimethylacetoamide;

and

said polymer is selected from the group consisting of vinylidene fluoride and vinylidene cyanate or a mixture thereof.

13. The process of claim 1, wherein said substance is selected from the group consisting of a liquid crystal, a dye and a mixture thereof.