Process for forming colorless chromate coating film on bright aluminum wheel

• US 5,259,937 A
• Filed: 12/16/1992
• Issued: 11/09/1993
• Est. Priority Date: 12/27/1991
• Status: Expired due to Fees

• Current Assignee: Nihon Parkerizing Company Limited, Nissan Motor Co., Ltd.
• Original Assignee: Nihon Parkerizing Company Limited, Nissan Motor Co., Ltd.
• Inventors: Oyama, Kazuyuki, Hatano, Norifumi, Hasebe, Akihiko, Yamamoto, Katsuya
• Primary Examiner(s): Niebling, John
• Assistant Examiner(s): Mayekar, Kishor
• Application Number:
  US07/991,426
• Time in Patent Office: 328 Days
• Field of Search: 205/149, 205/196, 205/286, 205/319
• US Class Current: 205/149
• CPC Class Codes: C25D 11/38 Chromatising

Abstract

A colorless chromate coating film is formed on a bright aluminum wheel by subjecting the surface of an aluminum wheel to a cathodic electrolytic treatment in an acidic aqueous solution containing not less than 2 g/l of hexavalent chromium ions, 20 to 2,000 ppm of sulfate ions, 10 to 400 ppm of fluorine (F) as fluoride and not less than 20 ppm of zirconium ions at a pH of 0.6 to 1.7 at a current density of 0.5 to 15 A/dm² for at least 30 seconds, thereby forming a coating film with a chromium coating amount of 50 to 250 mg/m².

Claims

1. A process for forming a colorless chromate coating film on an aluminum wheel, which comprises subjecting a surface of the aluminum wheel to a cathodic electrolytic treatment in an acidic aqueous solution containing not less than 2 g/l of hexavalent chromium ions, 20 to 2,000 ppm of sulfate ions, 10 to 400 ppm of fluorine (F) as fluoride and not less than 20 ppm of zirconium ions at a pH of 0.6 to 1.7 at a current density of 0.5 to 15 A/dm² for at least 30 seconds, thereby forming a coating film with a chromium coating amount of 50 to 250 mg/m².

2. A process according to claim 1, wherein the hexavalent chromium ions are ions from at least one member selected from the group consisting of chromic acid anhydride, alkali chromates and alkali bichromates.

3. A process according to claim 1, wherein the sulfate ions are ions selected from the groups consisting of sulfuric acid or alkali metal sulfates.

4. A process according to claim 1, wherein the fluorine (F) are F in the form of one member selected from the group consisting of hydrofluoric acid, hydrozircofluoric acid, hydrosilicofluoric acid and hydroborofluoric acid.

5. A process according to claim 1, wherein the zirconium ions are ions from at least one member selected from the group consisting of hydrozircofluoric acid, sodium, potassium and ammonium salts of hydrozircofluoric acid and zirconium sulfate.

6. A process according to claim 1, wherein the acidic aqueous solution further contains colloidal silica, dry process silica or alkali metal silicates.