Method and apparatus for drawing optical fibers

• US 5,284,499 A
• Filed: 05/01/1992
• Issued: 02/08/1994
• Est. Priority Date: 05/01/1992
• Status: Expired due to Term

• Current Assignee: Corning Incorporated
• Original Assignee: Corning Incorporated
• Inventors: Hawtof, Daniel W., Harvey, Jill A., Spicer, Henry A.
• Primary Examiner(s): LINDSAY JR, ROBERT
• Application Number:
  US07/877,626
• Time in Patent Office: 648 Days
• Field of Search: 65/2, 65/3.11, 65/3.12, 65/12, 65/13
• US Class Current: 65/435
• CPC Class Codes: C03B 37/02718 Thermal treatment of the fibre during the drawing process, e.g. cooling coating C03C25/10
• CPC Class Codes: C03B 37/029 Furnaces therefor

Abstract

A method and apparatus for drawing an optical waveguide fiber which minimizes fiber bow caused by differential stresses in the cladding layer of the fiber are disclosed. The fiber is drawn from a preform which is heated in a draw furnace. Gases introduced at the top of the furnace form a boundary layer adjacent to the fiber which passes through the furnace, along with the fiber, into a tube. The tube isolates the fiber from the ambient atmosphere so that the boundary layer of gases established in the furnace remains substantially uniform until the viscosity of the cladding layer of the fiber is high enough to minimize differential stresses around the circumference of the fiber.

Claims

1. An apparatus for drawing an optical waveguide fiber from an optical waveguide preform, comprising:

a. means for heating one end of said preform to its softening temperature;

b. means for supporting said preform, said supporting means allowing relative movement between said preform and said heating means;

c. means for introducing gas into said heating means above said one end of said preform; and

d. means for cooling said fiber, said cooling means attached to said heating means to provide substantially unobstructed fluid communication between said heating means and said cooling means for the gas introduced into said heating means, wherein a boundary layer of said gas formed adjacent to said fiber is substantially uniform in the region where said fiber is substantially cooled to a temperature at which the viscosity of the cladding layer of the fiber is high enough to substantially prevent differential stresses in the cladding layer of the fiber,

wherein said cooling means further comprises a tube attached to said heating means such that the fiber is drawn through said heating means into said tube and out a fiber outlet of said tube, said tube including an isolating means to substantially prevent exposure of the fiber therein to a current of ambient atmosphere.

2. The apparatus of claim 1, wherein said isolating means comprises an adjustable iris at the fiber outlet of said tube.

3. The apparatus of claim 1, wherein the inside diameter of said tube is substantially the same as the inside diameter of said heating means.

4. The apparatus of claim 1, wherein the inside diameter of said tube is substantially smaller than the inside diameter of said heating means.

5. The apparatus of claim 1, wherein the temperature of the fiber at which the fiber is exposed to ambient atmosphere is in the range of about 1,000°

C. to about 1,300°

C.

6. An apparatus for drawing an optical waveguide fiber from an optical waveguide preform, comprising:

a. means for heating one end of said preform to its softening temperature;

b. means for supporting said preform, said supporting means allowing relative movement between said preform and said heating means;

c. means for introducing gas into said heating means above said one end of said preform; and

d. means for cooling said fiber, said cooling means attached to said heating means to provide substantially unobstructed fluid communication between said heating means and said cooling means, wherein said cooling means substantially prevents different cooling of said fiber,

wherein said cooling means further comprises a tube attached to said heating means such that the fiber is drawn through said heating means into said tube and out a fiber outlet of said tube, said tube including an isolating means to substantially prevent exposure of the fiber therein to a current of ambient atmosphere.

7. The apparatus of claim 6, wherein said isolating means comprises an adjustable iris at the fiber outlet of said tube.

8. The apparatus of claim 6, wherein the inside diameter of said tube is substantially the same as the inside diameter of said heating means.

9. The apparatus of claim 6, wherein the inside diameter of said tube is substantially smaller than the inside diameter of said heating means.

10. The apparatus of claim 6, wherein the temperature of the fiber at which the fiber is exposed to ambient atmosphere is in the range of about 1,000°

C. to about 1300°

C.

11. A method for drawing an optical waveguide fiber from an optical waveguide preform, comprising the steps of:

a. heating, in a furnace, one end of said preform to its softening temperature;

b. exposing said heated preform to a gas in the furnace;

c. drawing a fiber from the softened end of the preform into a cooling chamber attached to the furnace and out a fiber outlet of said cooling chamber, said cooling chamber fluidly communicating with the furnace;

d. utilizing the gas flow between the furnace and said cooling chamber to symmetrically cool the fiber to a temperature at which the viscosity of the cladding layer of the fiber is high enough to substantially prevent differential stresses in the cladding layer of the fiber; and

e. isolating the atmosphere of said cooling chamber from the ambient atmosphere by constricting the opening at the fiber outlet of said cooling chamber and by utilizing the gas flow between the furnace and the cooling chamber.

12. The method of claim 11, wherein said isolating step further comprises adjusting an adjustable iris attached to the fiber outlet of said cooling chamber to constrict the opening at the fiber outlet of the cooling chamber.

13. The method of claim 11, wherein the gas to which the preform is exposed comprises helium.

14. The method of claim 11, wherein the gas is introduced at the top of the furnace and is heated as it passes through said furnace with the fiber.