Porous, polymer beads and process of their preparation

• US 5,288,763 A
• Filed: 12/23/1992
• Issued: 02/22/1994
• Est. Priority Date: 12/23/1992
• Status: Expired due to Fees

• Current Assignee: Johns Hopkins University
• Original Assignee: Johns Hopkins University
• Inventors: Leong, Kam W., Li, Nai-Hong
• Primary Examiner(s): Foelak, Morton
• Application Number:
  US07/995,793
• Time in Patent Office: 426 Days
• Field of Search: 521/60, 521/61, 521/149, 521/150, 521/134, 521/140, 521/59
• US Class Current: 521/61
• CPC Class Codes: B01J 20/261 obtained by reactions only involving carbon to carbon unsaturated bonds macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds per se C08F
• CPC Class Codes: B01J 20/264 derived from different types of monomers, e.g. linear or branched copolymers, block copolymers, graft copolymers
• CPC Class Codes: B01J 20/267 Cross-linked polymers
• CPC Class Codes: B01J 20/268 Polymers created by use of a template, e.g. molecularly imprinted polymers
• CPC Class Codes: B01J 20/28078 Pore diameter
• CPC Class Codes: B01J 20/285 based on polymers
• CPC Class Codes: B01J 20/286 Phases chemically bonded to a substrate, e.g. to silica or to polymers
• CPC Class Codes: B01J 20/3057 Use of a templating or imprinting material molecularly imprinted polymers B01J20/268; filling pores of a substrate or matrix followed by the removal of the substrate or matrix
• CPC Class Codes: B01J 20/3064 Addition of pore forming agents, e.g. pore inducing or porogenic agents
• CPC Class Codes: B01J 20/3085 Chemical treatments not covered by groups B01J20/3007 - B01J20/3078
• CPC Class Codes: B01J 20/3092 Packing of a container, e.g. packing a cartridge or column of chromatography columns B01D15/206
• CPC Class Codes: B01J 2220/54 Sorbents specially adapted for analytical or investigative chromatography
• CPC Class Codes: B01J 2220/58 Use in a single column
• CPC Class Codes: C08J 9/26 by elimination of a solid phase from a macromolecular composition or article, e.g. leaching out
• CPC Class Codes: G01N 2030/524 structural properties

Abstract

Porous, polymer particles comprising a functionalized cross-linked copolymer having microporous regions and macroporous regions in the polymer matrix thereof, wherein the functional groups are essentially present only within the macroporous regions, as well as processes for preparing these particles based on a template polymerization technique followed by removal of the template polymer from the particles are disclosed. The particles of the invention are useful in chromatography, and in various analytical, diagnostic techniques and solid state peptide, DNA synthesis.

Claims

1. A method of preparing porous, functionalized polymer particles which comprises a cross-linked copolymer having microporous regions and macroporous regions in the polymer matrix thereof, wherein the functional groups are essentially present only within the macroporous regions, comprising the steps of:

(a) providing a polymerizable mixture containing a functional monomer, a cross-linker and a template polymer in an aqueous medium to form a suspension, the template polymer being capable of forming an ionic or covalent bond with the functional monomer;

(b) copolymerizing the monomer and the cross-linker with or without a polymerization catalyst in the suspension to form a cross-linked copolymer;

(c) removing the aqueous medium and the template polymer from the copolymer to recover porous, functionalized polymer particles, the particles having microporous regions and macroporous regions in the polymer matrix thereof, wherein the functional groups are essentially present only within the macroporous regions.

2. The method according to claim 1, wherein the functional groups are polar.

3. The method according to claim 2, wherein the polar group is selected from the group consisting of hydroxyl, amino, carboxyl, sulfonyl, pyridiyl and phenol.

4. The method according to claim 1, wherein the functional monomer is a monoethylenically unsaturated monomer.

5. The method according to claim 4, wherein the unsaturated monomer is selected from the group consisting of vinylpyridine, vinylphenol, vinyl-p-toluenesulfonic acid, acrylic acid, methacrylic acid, and methacrylic acid halide.

6. The method according to claim 5, wherein the unsaturated monomer is vinylpyridine.

7. The method according to claim 1, wherein the template polymer is selected from the group consisting of poly(acrylic acid), poly(vinylalcohol), and poly(4-vinylpyridine).

8. The method according to claim 1, wherein the functional monomer is vinylpyridine and the template polymer is poly(acrylic acid).

9. The method according to claim 1, wherein the functional monomer is methacrylic acid halide and the template polymer is polyvinyl alcohol.

10. The method according to claim 1, wherein the functional monomer is vinyl-p-toluenesulfonic acid and the template polymer is poly(4-vinylpyridine).

11. The method according to claim 1, wherein in step (a) the template polymer forms an ionic bond with the functional monomer.

12. The method according to claim 10, wherein in step (c) the removal of the template polymer involves extraction with an aqueous alkali or acid solution.

13. The method according to claim 1, wherein in step (a) the template polymer forms a covalent bond with the functional monomer.

14. The method according to claim 13, wherein the covalent bond is an ester or amido.

15. The method according to claim 13, wherein in step (c) the removal of the template polymer involves hydrolysis of the copolymer.

16. The method according to claim 1, wherein the copolymerization is conducted at a temperature of above about 50°

C.

17. The method according to claim 16, wherein the catalyst is AIBN.

18. The method according to claim 1, wherein the cross-linked copolymer has a crosslinking degree of about 10 to about 50%.