Glass or quartz articles having high temperature UV absorbing coatings containing ceria

• US 5,316,854 A
• Filed: 12/06/1991
• Issued: 05/31/1994
• Est. Priority Date: 12/06/1991
• Status: Expired due to Fees

• Current Assignee: PPG Industries Incorporated (Nouryon BV)
• Original Assignee: PPG Industries Incorporated (Nouryon BV)
• Inventors: Bihuniak, Peter P., Lin, Chia-Cheng, Basil, John D., Hunia, Robert M.
• Primary Examiner(s): Robinson, Ellis P.
• Assistant Examiner(s): Speer, Timothy M.
• Application Number:
  US07/802,914
• Time in Patent Office: 907 Days
• Field of Search: 428/336, 428/426, 428/428, 428/429, 428/446, 428/447, 428/688, 428/689, 428/697, 428/702, 428/432, 428/328, 501/12, 501/64, 106/287.13, 106/287.14, 106/287.15
• US Class Current: 428/426
• CPC Class Codes: C03C 17/007 containing a dispersed phase, e.g. particles, fibres or flakes, in a continuous phase
• CPC Class Codes: C03C 17/25 by deposition from the liquid phase
• CPC Class Codes: C03C 2217/23 Mixtures
• CPC Class Codes: C03C 2217/45 Inorganic continuous phases
• CPC Class Codes: C03C 2217/475 Inorganic materials
• CPC Class Codes: C03C 2217/74 UV-absorbing coatings
• CPC Class Codes: C03C 2218/113 by sol-gel processes
• CPC Class Codes: C08L 2666/54 Inorganic substances
• CPC Class Codes: C09D 183/04 Polysiloxanes
• CPC Class Codes: G02B 5/208 for use with infrared or ultraviolet radiation, e.g. for separating visible light from infrared and/or ultraviolet radiation
• CPC Class Codes: Y10T 428/12993 Surface feature [e.g., rough, mirror]
• CPC Class Codes: Y10T 428/256 Heavy metal or aluminum or compound thereof
• CPC Class Codes: Y10T 428/265 1 mil or less
• CPC Class Codes: Y10T 428/31612 As silicone, silane or siloxane
• CPC Class Codes: Y10T 428/31663 As siloxane, silicone or silane

Abstract

An ultraviolet radiation absorbing coating comprising cerium oxide in an inorganic oxide matrix formed by the hydrolysis and condensation of alkoxysilane and/or other metal alkoxide or oxide which has a higher absorbance per unit thickness of coating by virtue of its much higher concentration of colloidal particles in said matrix and a reduced tendency to craze when exposed to temperatures in excess of 1000° C. and/or temperature cycling between ambient temperature and 1000° C. by virtue of heating a coated article at elevated temperature between 500° C. and 1100° C. before cooling the coated article.

Claims

1. A coated article comprising a substrate of glass or quartz and a coating having an absorbance of 1 to 3 per micron of thickness at 320 nanometers and consisting essentially of colloidal particles of cerium oxide in a silica-based matrix and having a minimum concentration on the order of 40 weight percent of cerium oxide based on the total metal oxide content of said matrix containing said cerium oxide particles, said coated article being essentially craze free and essentially optically clear at 1000°

C.

2. A coated article as in claim 1, wherein said silica-based matrix further comprises at least one metal oxide produced from an alkoxide of a metal selected from the group consisting of titanium, zirconium, boron, aluminum and such other metals as form hydrolyzable alkoxides.

3. A coated article as in claim 1, wherein said colloidal particles of cerium oxide have an average particle size on the order of 5 nanometers.

4. A coated article as in claim 3, wherein a considerable portion of said colloidal particles of cerium oxide have a particle size of 3 to 5 nanometers.

5. A coated article as in claim 3, wherein said coating has a maximum thickness on the order of 2 microns.

6. A coated article as in claim 1, wherein said coating has a maximum thickness on the order of 2 microns.

7. A coated article as in claim 1, containing a plurality of said coatings.

8. A coated article as in claim 7, wherein each of said coatings has a maximum thickness on the order of 2 microns.

9. A coated article as in claim 2, wherein said silica-based matrix includes an oxide of titanium.

10. A coated article as in claim 1, wherein said silica-based matrix is formed by heating an organosiloxane of the general formula R_x Si(OR'"'"')_4-x, where R is selected from the group consisting of alkyl, epoxy, glycidoxy and acrylic functional groups, R'"'"' is selected from the group consisting of methyl, ethyl, propyl and butyl, and x is at least one and less than four, at a temperature sufficiently high to render said coating resistant to crazing when exposed to temperature cycling between ambient temperature and 1000°

C.