Antifogging plastic lens material

• US 5,324,573 A
• Filed: 12/18/1992
• Issued: 06/28/1994
• Est. Priority Date: 12/18/1992
• Status: Expired due to Fees

• Current Assignee: Rexam Industries Corp.
• Original Assignee: Rexham Industries Corp.
• Inventors: Evans, Joseph H.
• Primary Examiner(s): Sluby, P. C.
• Application Number:
  US07/993,310
• Time in Patent Office: 557 Days
• Field of Search: 428/215, 428/478.2, 428/483, 428/518, 428/918
• US Class Current: 428/215
• CPC Class Codes: B05D 7/02 to macromolecular substances, e.g. rubber treatment or coating of shaped articles made of macromolecular substances C08J7/00
• CPC Class Codes: B05D 7/57 the last layer being a clear coat
• CPC Class Codes: G02B 1/041 Lenses
• CPC Class Codes: Y10S 428/918 Material abnormally transparent
• CPC Class Codes: Y10T 428/24967 Absolute thicknesses specified
• CPC Class Codes: Y10T 428/31768 Natural source-type polyamide [e.g., casein, gelatin, etc.]
• CPC Class Codes: Y10T 428/31797 Next to addition polymer from unsaturated monomers
• CPC Class Codes: Y10T 428/3192 Next to vinyl or vinylidene chloride polymer

Abstract

An antifogging plastic material is disclosed that is particularly suitable for use as a disposable fog-resistant lens. The lens material comprises a substantially transparent polyester substrate; a layer of polyvinylidene chloride-containing polymer on the polyester substrate; a water permeable colloid layer on the polyvinylidene chloride-containing layer; and a polyvinyl alcohol-containing layer on the water permeable colloid layer.

Claims

1. An antifogging plastic lens material comprising:

a substantially transparent polyester substrate;

a substantially transparent layer containing polyvinylidene chloride on said polyester substrate;

a substantially transparent water permeable colloid layer on said polyvinylidene chloride-containing layer; and

a substantially transparent layer containing polyvinyl alcohol on said water permeable colloid layer.

2. An antifogging lens material according to claim 1 wherein said polyvinyl alcohol-containing layer further comprises polyvinyl acetate.

3. An antifogging lens material according to claim 1 wherein said water permeable colloid layer comprises gelatin.

4. An antifogging lens material according to claim 1 wherein said polyvinylidene chloride-containing layer contains at least about 35 percent by weight polyvinylidene chloride.

5. An antifogging lens material according to claim 1 wherein said polyvinylidene chloride-containing layer includes a copolymer selected from the group consisting of:

acrylic polymers, methacrylic polymers, nitrile polymers, itaconic acid polymers, polyisocyanates, and polyisothiocyanates.

6. An antifogging lens material according to claim 1 wherein said polyvinyl alcohol-containing layer has an average molecular weight of between about 11,000 and 110,000 grams per mole and is between about 80 and 99 percent hydrolyzed.

7. An antifogging lens material according to claim 1 wherein said polyvinyl alcohol-containing layer is at least 87 percent hydrolyzed.

8. An antifogging lens material according to claim 1 wherein said polyvinyl alcohol-containing layer has a thickness of between about 2.5 and 12.7 microns.

9. An antifogging lens material according to claim 1 wherein said polyvinylidene chloride-containing layer has a thickness of about 1 micron.

10. An antifogging lens material according to claim 1 wherein said water permeable colloid layer has a thickness of about 1 micron.

11. An antifogging lens material according to claim 1 wherein said polyester substrate is between about 101.6 and 177.8 microns thick.

12. An antifogging lens material according to claim 1 in which said polyvinyl alcohol-containing layer cannot be removed from said substrate using a Scotch Brand #600 adhesive tape in a Cross hatch tape test described in ASTM B 449.

13. A method of preparing an antifogging plastic material that is particularly suitable for use as a disposable fog-resistant lens, said method comprising applying a layer of a polyvinyl alcohol-containing polymer to the surface of a polyester substrate that has a polyvinylidene chloride-containing layer on the polyester substrate, and a water permeable colloid layer on the polyvinylidene chloride-containing layer.

14. A method according to claim 13 wherein the step of applying the polyvinyl alcohol-containing polymer comprises applying an aqueous solution of polyvinyl alcohol.

15. A method according to claim 14 wherein the step of applying the polyvinyl alcohol from an aqueous solution comprises applying the polyvinyl alcohol from an aqueous solution that contains about ten percent of a low aliphatic alcohol.

16. A method according to claim 13 in which the step of applying the polyvinyl alcohol-containing polymer comprises applying the polymer from an aqueous solution at a rate of about 2 pounds per ream of substrate.

17. A method according to claim 13 in which the step of applying the polyvinyl alcohol-containing polymer comprises applying the polymer in a thickness of about 0.1 mil.

18. A method according to claim 13 in which the step of applying the polyvinyl alcohol-containing polymer comprises applying the polymer from an aqueous solution containing a solids content of between about 1 and 20 percent.

19. A method according to claim 13 in which the step of applying the polyvinyl alcohol-containing polymer comprises applying the polymer from an aqueous solution containing a solids content of between about 5 and 10 percent.

20. A method of preparing an antifogging plastic material that is particularly suitable for use as a disposable fog-resistant lens, said method comprising:

applying a layer of a polyvinylidene chloride-containing polymer to a polyester substrate;

applying a layer of a water permeable colloid to the polyvinylidene chloride-containing layer; and

applying a layer of polyvinyl alcohol-containing polymer to the water permeable colloid layer on the polyviylidene chloride-containing layer.

21. A method according to claim 20 wherein the step of applying the polyvinyl alcohol-containing polymer comprises applying an aqueous solution of polyvinyl alcohol.