Method for preparing silicone mold tooling

• US 5,326,521 A
• Filed: 05/26/1993
• Issued: 07/05/1994
• Est. Priority Date: 05/26/1993
• Status: Expired due to Fees

• Current Assignee: Douglas A. East
• Original Assignee: Douglas A. East
• Inventors: East, Douglas A.
• Primary Examiner(s): Woo, Jay H.
• Assistant Examiner(s): Davis, Robert B.
• Application Number:
  US08/067,846
• Time in Patent Office: 405 Days
• Field of Search: 264/220, 264/225, 264/227, 264/337, 264/DIG.72, 425/DIG. 44, 249/134, 427/426
• US Class Current: 264/225
• CPC Class Codes: B29C 33/40 Plastics, e.g. foam or rubber
• CPC Class Codes: B29C 41/08 Coating a former, core or other substrate by spraying or fluidisation, e.g. spraying powder spray-up of reinforcing fibres B29C70/305
• CPC Class Codes: B29K 2105/0094 having particular viscosity
• CPC Class Codes: B29K 2105/246 Uncured, e.g. green
• CPC Class Codes: Y10S 264/72 Processes of molding by spraying

Abstract

The present invention relates to spraying of high viscosity silicone molding compositions and to cured silicone molds or tools formed by that process that allow for near perfect transfer of detail from a surface to a molded object.

Claims

1. A method for preparing silicone molding tooling of a shaped article, comprising the steps of:

providing a curable silicone resin composition having at least two parts that, upon mixing, cure to form a silicone rubber;

mixing the parts of the silicone resin composition to form an uncured silicone rubber having a viscosity between about one million centipoise and about four million centipoise and having the ability to hang on a vertical surface in a layer of about 0.2 cm thickness without significant slumping, said mixing being accomplished in such a manner that entrainment of air in said uncured silicone rubber is avoided;

spraying the uncured silicone rubber onto a surface to be molded in a single operation with said mixing step, said spraying being done in such a manner that entrainment of air in said uncured silicone rubber is avoided, wherein said layer is at least about 0.1 cm thick; and

allowing said silicone rubber to cure on said surface to form a mold of said surface.

2. The method of claim 1, wherein said cured silicone rubber has a Shore A durometer hardness of between about 10 and 50 measured according to ASTM D2240.

3. The method of claim 2, wherein the tensile strength of said cured silicone rubber is at least about 400 psi.

4. The method of claim 3, wherein said cured silicone rubber is capable of at least about 350% elongation, measured according to ASTM D412, Die C.

5. The method of claim 4, wherein said cured silicone rubber has a tear strength of at least 80 pounds per inch, measured according to ASTM 621, Die B.

6. The method of claim 5, wherein said cured silicone rubber has a shrinkage of less than about 0.5%, measured according to Mil. Spec. 23586E, paragraph 4.8.7.

7. The method of claim 1, wherein said mixing and spraying steps is accomplished by pumping and metering said parts of said curable silicone resin composition into contact with each other in a manner that said parts are mixed, and in the same continuous operation spraying the resulting uncured silicone rubber through a spray gun onto said surface.

8. The method of claim 7, wherein said spraying is accomplished by pushing said uncured silicone rubber through a spray nozzle by virtue of air pressure introduced into said nozzle combined with pumping pressure applied to said uncured silicone rubber.

9. The method of claim 1, wherein said uncured silicone rubber is applied to said surface in a thickness between about 0.2 and about 1.0 cm.

10. The method of claim 1, further comprising the step of applying backup tooling to said cured silicone rubber while on said surface.

11. The method of claim 1, wherein said surface is a generally vertical surface.

12. The method of claim 1, wherein said surface to which said silicone rubber is applied has a surface area of at least about 1 m².

13. The method of claim 1, wherein said surface to which said silicone rubber is applied has a surface area of about 10 m².