Process for vitrifying asbestos containing waste, infectious waste, toxic materials and radioactive waste
First Claim
1. A process for converting waste materials into a silicate, said process comprising:
- heating a silicate melt within an electrical glass melting furnace by passing an electric current through the melt between at least two electrodes so as to maintain the melt at a temperature above a decomposition temperature of waste materials;
generating a curtain of gas bubbles across a substantial portion of the current path between the at least two electrodes to increase the power density of the melt in the region of the curtain of gas bubbles;
supplying waste materials to the furnace above the melt so that the waste materials fall onto the melt and the waste materials are melted into silicates;
withdrawing molten silicate from the furnace in a molten glass stream at a temperature of at least 900°
C.;
cutting the molten glass stream into a set of gobs by interrupting the molten glass stream; and
contacting said gobs with a cold surface to form gems having at least one flattened surface.
4 Assignments
0 Petitions
Accused Products
Abstract
Material, such as, for example, sealed double bags of asbestos containing waste or ash from infectious waste or toxic material or radioactive waste, is transferred into a glass melt of a furnace. Gas bubbles released into the melt form a gas curtain which causes enhanced mixing of the material to accelerate the dissolution of the components of the added material. The presence of the gas bubbles reduces the cross-section of the molten glass through which current passes, which in turn increases the electrical resistance of the glass melt and therefore increases power generation of the melt or power density at constant current. A highly oxidizing hot region is produced under the location where the material is introduced into the furnace. Drawn off glass is shaped and quenched into at least two sizes of approximate spheres. The spheres are cooled sufficiently fast to be thermally tempered and have a surface compressive strength level above 5000 psi.
-
Citations
22 Claims
-
1. A process for converting waste materials into a silicate, said process comprising:
-
heating a silicate melt within an electrical glass melting furnace by passing an electric current through the melt between at least two electrodes so as to maintain the melt at a temperature above a decomposition temperature of waste materials; generating a curtain of gas bubbles across a substantial portion of the current path between the at least two electrodes to increase the power density of the melt in the region of the curtain of gas bubbles; supplying waste materials to the furnace above the melt so that the waste materials fall onto the melt and the waste materials are melted into silicates; withdrawing molten silicate from the furnace in a molten glass stream at a temperature of at least 900°
C.;cutting the molten glass stream into a set of gobs by interrupting the molten glass stream; and contacting said gobs with a cold surface to form gems having at least one flattened surface. - View Dependent Claims (2, 3, 4, 5, 6, 7, 8, 9, 10, 11)
-
-
12. A process for converting waste materials into a silicate, said process comprising:
-
heating a silicate melt within a glass melting furnace so as to maintain the melt at a temperature above a decomposition temperature of waste materials; supplying waste materials to the furnace above the melt so that the waste materials fall onto the melt and the waste materials are melted into silicates; withdrawing molten silicate from the furnace in a molten glass stream at a temperature of at least 900°
C., the molten silicate being withdrawn from the furnace through a melt outlet adjacent the bottom of the furnace, the melt outlet being connected to an airlift conduit in which gas bubbles are introduced to create an effective head pressure to force the melt up the airlift and out of the furnace,cutting the molten glass stream into a set of gobs by interrupting the molten glass stream; and contacting said gobs with a cold surface to form gems having at least one flattened surface. - View Dependent Claims (13, 14, 15, 16, 17, 18, 19, 20, 21, 22)
-
Specification