Method for making a machine readable bar code on glassware and the product thereof
First Claim
Patent Images
1. A method of applying a bar code pattern to glassware comprising the steps ofcreating a bar code pattern;
- providing a ceramic film blank having a ceramic layer and a removable backing strip applied to its rear surface;
applying said bar code pattern with a silk screen process onto said ceramic layer;
applying a gel coating to a front surface of said film blank to create a bar code decal structure;
soaking said bar code decal structure in water at about 90°
F. for about five minutes;
manually removing said backing strip to result in a structure including ceramic film layer and said gel coating;
placing said structure on blank glassware;
drying said glassware and said structure for a period of about 24 hours at an ambient temperature of about 70°
F. to create a dried structure;
placing said dried structure in a kiln for heating to a temperature of about 600°
F. for a period of about ten minutes, and thenincreasing the temperature of said dried structure to about 1140°
F. for a predetermined time period for fusing of the ceramic decal and glassware while said gel coating is vaporized.
0 Assignments
0 Petitions
Accused Products
Abstract
A method for making machine readable bar code markings (20) on glassware (10) is disclosed. A ceramic film (16B) first has bar code markings (20) placed thereon. The ceramic film with the bar code markings (20) is placed on the outer surface (14) of the glassware (10). The ceramic film (16) and glassware (10) are heated or fired for a predetermined time period at a temperature over 1100° F. adequate to effect fusing of the film (16B) onto the glassware (10) while providing a fused layer (18) therebetween.
-
Citations
1 Claim
-
1. A method of applying a bar code pattern to glassware comprising the steps of
creating a bar code pattern; -
providing a ceramic film blank having a ceramic layer and a removable backing strip applied to its rear surface; applying said bar code pattern with a silk screen process onto said ceramic layer; applying a gel coating to a front surface of said film blank to create a bar code decal structure; soaking said bar code decal structure in water at about 90°
F. for about five minutes;manually removing said backing strip to result in a structure including ceramic film layer and said gel coating; placing said structure on blank glassware; drying said glassware and said structure for a period of about 24 hours at an ambient temperature of about 70°
F. to create a dried structure;placing said dried structure in a kiln for heating to a temperature of about 600°
F. for a period of about ten minutes, and thenincreasing the temperature of said dried structure to about 1140°
F. for a predetermined time period for fusing of the ceramic decal and glassware while said gel coating is vaporized.
-