Method of modifying the charging propensity of carrier particles for electrostatographic developers and modified carrier particles

• US 5,411,832 A
• Filed: 09/24/1993
• Issued: 05/02/1995
• Est. Priority Date: 09/24/1993
• Status: Expired due to Term

• Current Assignee: Eastman Kodak Company
• Original Assignee: Eastman Kodak Company
• Inventors: Yoerger, William E.
• Primary Examiner(s): GOODROW, JOHN L
• Application Number:
  US08/127,382
• Time in Patent Office: 585 Days
• Field of Search: 430/106, 430/110, 430/108
• US Class Current: 430/111.32
• CPC Class Codes: C08F 114/22 Vinylidene fluoride
• CPC Class Codes: C08F 2800/20 as weight or mass percentages
• CPC Class Codes: C08F 8/04 Reduction, e.g. hydrogenation
• CPC Class Codes: G03G 9/1134 containing fluorine atoms

Abstract

A method for modifying the triboelectric charging propensity of particles coated with fluorohydrocarbon polymer for use as carriers in electrostatographic development comprising contacting the particles with a basic solution including a reducing agent for said particles and optionally including an oxidizing agent for said particles and carriers and developers produced by that method.

Claims

1. A method for modifying the triboelectric charging propensity of particles coated with fluorohydrocarbon polymer for use as carriers in electrostatographic development, said method comprising contacting said particles with a basic solution including a reducing agent for said particles.

2. The method of claim 1 wherein said solution is aqueous.

3. The method of claim 1 wherein said contacting step further comprises maintaining said particles in said basic solution at a temperature from room temperature to about 100°

C.

4. The method of claim 1 wherein said contacting step further comprises maintaining said particles in said basic solution at a temperature from 50°

C. to 70°

C.

5. The method of claim 1 wherein said particles have ferrite cores.

6. The method of claim 1 wherein said fluorohydrocarbon is poly(vinylidene fluoride).

7. The method of claim 1 wherein said reducing agent is one or more sulfur reducing ions said base is one or more hydroxides.

8. The method of claim 7 wherein said reducing agent is HSO₃ --, SO₃^2--, S₂ O₃^2--, S₂ O₄^2--, S₂ O₅^2--, or S₂ O₇^2--.

9. The method of claim 1 wherein said particles have strontium ferrite cores and said contacting step further comprises maintaining said particles in an aqueous solution of hydroxide and sulfur reducing ion at a temperature of from 50°

C. to 70°

C. for from 1 to 3 hours.

10. A carrier produced by the method of claim 1.

23. An electrostatic developer comprising toner particles and the carrier particles of claim 10, said toner particles including binder selected from the group consisting of styrene-butyl-acrylate copolymers.

24. A method for developing latent images comprising forming an electrostatic latent image with the developer defined in claim 23, followed by transferring the image to a suitable substrate and permanently affixing the image thereto.

11. A method for modifying the triboelectric charging propensity of particles coated with fluorohydrocarbon polymer for use as carriers in electrostatographic development, said method comprising contacting said particles with a basic solution including an oxidizing agent for said particles and a reducing agent for said particles.

12. The method of claim 11 wherein said oxidizing agent and said reducing agent are interconvertable, within said basic solution, by one or more oxidation-reduction reactions.

13. The method of claim 11 wherein said solution is aqueous and said contacting step further comprises maintaining said particles in said basic solution at a temperature from room temperature to about 100°

C.

14. The method of claim 11 wherein said contacting step further comprises maintaining said particles in said basic solution at a temperature from 50°

C. to 70°

C.

15. The method of claim 11 wherein said particles have ferrite cores.

16. The method of claim 11 wherein said fluorohydrocarbon is poly(vinylidene fluoride).

17. The method of claim 11 wherein said reducing agent is one or more sulfur reducing ions, said oxidizing agent is one or more peroxysulfates and said base is one or more hydroxides.

18. The method of claim 17 wherein said reducing agent is HSO₃ --, SO₃^2--, S₂ O₄^2--, S₂ O₅^2--, or S₂ O₇^2-- and said oxidizing agent is peroxydisulfate.

19. The method of claim 11 wherein said particles have strontium ferrite cores and said contacting step further comprises maintaining said particles in an aqueous solution of potassium hydroxide, peroxydisulfate, and sulfur reducing ions at a temperature of from 50°

C. to 70°

C. for from 1 to 3 hours.

20. A carrier produced by the method of claim 11.

21. An electrostatographic developer comprising toner and carrier particles produced by contacting fluorhydrocarbon coated particles with a basic solution including a reducing agent for said particles, said toner including binder selected from the group consisting of styrene-butyl-acrylate copolymers.

22. A method for developing latent images comprising forming an electrostatic latent image with the developer defined by claim 21, followed by transferring the image to a suitable substrate and permanently affixing the image thereto.