Alloy for backing steel of a bimetallic band saw blade

• US 5,417,777 A
• Filed: 02/22/1994
• Issued: 05/23/1995
• Est. Priority Date: 02/22/1994
• Status: Expired due to Fees

• Current Assignee: American Saw & Manufacturing Co. (Newell Brands Inc.)
• Original Assignee: American Saw & Manufacturing Co. (Newell Brands Inc.)
• Inventors: Henderer, Willard E.
• Primary Examiner(s): Yee, Deborah
• Application Number:
  US08/199,539
• Time in Patent Office: 455 Days
• Field of Search: 148/334, 148/335, 30/345, 30/380, 30/350, 428/683
• US Class Current: 148/334
• CPC Class Codes: B23D 61/127 of special material
• CPC Class Codes: B32B 15/011 all layers being formed of iron alloys or steels
• CPC Class Codes: C22C 38/46 with vanadium
• CPC Class Codes: Y10T 428/12965 Both containing 0.01-1.7% carbon [i.e., steel]

Abstract

A bimetallic band saw blade has a high speed cutting edge welded to a backing band of a steel alloy containing the following elements percentages by weight:

Cr - 0.5% to no more than 1.5%

V - 0.10% to 0.75%

Mo - 1.5% to 2.5%

wherein said backing band comprises a substantially lesser amount by weight of Chromium than Molybdenum the alloy also contains C, Si, Mn, Nb and/or Ni and Al in such varying amounts that the total alloy content, except for Fe and inevitable impurities, is in the range of 3.12% to 8.48%.

Claims

1. An improved bimetallic band saw blade having a high speed steel cutting edge and a backing steel band welded thereto, saw teeth formed along the high speed cutting edge including cutting tips and gullets, said cutting tips being formed in the high speed steel edge and-the gullets extending into the backing band, said backing band comprising, by weight from 0.5% to no more than 1.50% Chromium (Cr), 0.10% to 0.75% Vanadium (V), 1.5% to 2.50% Molybdenum (Mo) and wherein said backing band comprises a substantially lesser amount by weight of Chromium than Molybdenum, the backing band alloy also containing Carbon (C), Manganese (Mn) and Nickel (Ni) in such varying amounts that the total alloy content of the backing band, except for iron and inevitable impurities, is in a range of 3.12% to 8.84% by weight.

2. An improved bimetallic saw blade, as set forth in claim 1, in which the backing band in which the said backing band comprises by weight 1.75% to 2.5% Molybdenum also contains Silicon (Si), Niobium (Nb) and Aluminum (Al), whereby said total alloy content is in a range of 3.12% to 8.84% by weight.

3. An improved bimetallic band saw blade, as set forth in claims 1 or 2, in which after welding the cutting edge steel to the backing band in which said backing band comprises 1.75% to 2.5% by weight of Molybdenum and the quantity by weight of Chromium is on the order of one-half that of the Molybdenum to form said blade, said blade is annealed and then hardened by heating to a temperature in the range of 2000°

-2250°

F., the blade is maintained at that temperature for one to ten minutes and quenched, the blade is then tempered by heating to a temperature in the range of 800°

-1100°

F., held at that temperature for approximately for two to three hours and then air-cooled to room temperature.

4. An improved bimetallic band saw blade, as set forth in claim 1, in which the backing band additionally comprises 0.45% to 1.25% by weight nickel (Ni) and in which the alloy content provided by the Carbon (C) and Manganese (Mn) is in the range of 0.57% to 1.68% per weight.

5. An improved bimetallic saw blade as set forth in claim 2, in which the backing band additionally comprises 0.45% to 1.25% by weight nickel (Ni) and in which the remaining alloy content by weight provided by the Carbon (C), Silicon (Si), Manganese (Mn), Niobium (Nb) and Aluminum (Al) is in the range of 0.57% to 2.48%.

6. An improved bimetallic saw blade as set forth in claims 4 or 5, in which the backing band additionally comprises by weight Carbon (C) 0.27% to 0.48%, Silicon (Si) up to 0.50%, Manganese (Mn) 0.30% to 1.20%, Niobium (Nb) up to 0.15% and Aluminum (Al) up to 0.15%.

7. An improved bimetallic saw blade as set forth in claim 6, wherein the tempering of said blade is repeated.

8. An improved bimetallic saw blade as set forth in claims 1, 2, 5 or 6, in which Titanium (Ti) is substituted for at least a portion of said Niobium (Nb).