Plated aluminum sheet having improved spot weldability

• US 5,436,081 A
• Filed: 02/02/1994
• Issued: 07/25/1995
• Est. Priority Date: 02/18/1991
• Status: Expired due to Fees

• Current Assignee: Sumitomo Metal Industries Limited (Nippon Steel Corporation), Sumitomo Light Metal Industries Limited (UACJ Corporation)
• Original Assignee: Sumitomo Metal Industries Limited (Nippon Steel Corporation), Sumitomo Light Metal Industries Limited (UACJ Corporation)
• Inventors: Hoboh, Yoshihiko, Ueda, Naotaka, Tsuji, Masanori, Fujita, Kazuyuki
• Primary Examiner(s): ZIMMERMAN, JOHN J
• Application Number:
  US08/191,356
• Time in Patent Office: 538 Days
• Field of Search: 428/650, 428/651, 428/652, 428/653, 428/658, 428/654, 428/686, 428/636, 205/139, 205/153, 205/213
• US Class Current: 428/650
• CPC Class Codes: C25D 5/34 Pretreatment of metallic surfaces to be electroplated
• CPC Class Codes: C25D 5/44 Aluminium
• CPC Class Codes: Y10T 428/12736 Al-base component
• CPC Class Codes: Y10T 428/12764 Next to Al-base component

Abstract

A plated aluminum sheet has improved spot weldability and press-formability and is suitable for use in the manufacture of automobile bodies. The aluminum sheet has a plated coating of a metal having a melting point of about 700° C. or above, e.g., Cr, Mn, Fe, Co, or Ni, an alloy of two or more of these metals, or a Zn alloy with at least one of these metals, on one or both surfaces thereof.

Claims

1. A spot welded plated aluminum sheet having improved spot weldability which comprises an aluminum sheet having on one or both surfaces a plated coating of a metal which has a melting point of about 700°

C. or above, the plated coating being present in a thickness sufficient to improve efficiency of spot welding of the aluminum sheet, the plated coating having a higher electric resistivity and lower thermal conductivity than the aluminum sheet, the plated coating having a hardness higher than the aluminum sheet, and the hardness being high enough to improve sliding properties and improve press-formability of the aluminum sheet, the plated coating being a zinc base alloy containing at least one of Cr, Mn, Fe, Co and Ni, the plated coating forming an exposed layer of the plated aluminum sheet.

2. The plated aluminum sheet of claim 1, wherein the plated coating is formed on one surface of the aluminum sheet with a coating weight in the range of from about 0.1 to about 40 g/m².

3. The plated aluminum sheet of claim 2, wherein the plated coating has a coating weight in the range of from about 3 to about 20 g/m².

4. The plated aluminum sheet of claim 1, wherein the plated coating is formed on both surfaces of the aluminum sheet with a coating weight in the range of from about 0.1 to about 20 g/m² on each surface.

5. The plated aluminum sheet of claim 1, wherein the plated coating is formed on both surfaces of the aluminum sheet with a coating weight in the range of from about 0.1 to about 40 g/m² on each surface.

6. The plated aluminum sheet of claim 1, wherein the plated coating consists essentially of a zinc base alloy containing at least 5% Ni.

7. The plated aluminum sheet of claim 1, wherein the plated coating consists essentially of a zinc base alloy containing at least 3% Fe.

8. The plated aluminum sheet of claim 1, wherein the sheet comprises a body panel of an automobile.

9. The plated aluminum sheet of claim 1, wherein the sheet comprises an engine hood, door or fender of an automobile.

10. The plated aluminum sheet of claim 1, wherein the sheet comprises a press-formed vehicle body panel.

11. A plated aluminum sheet having improved spot weldability which comprises an aluminum sheet having on one or both surfaces a plated coating of a metal which has a melting point of about 700°

C. or above, the plated coating being present in a thickness sufficient to improve efficiency of spot welding of the aluminum sheet, the plated coating having a higher electric resistivity and lower thermal conductivity than the aluminum sheet, the plated coating having a hardness higher than the aluminum sheet, and the hardness being high enough to improve sliding properties and improve press-formability of the aluminum sheet, the plated coating being a zinc base alloy containing at least one of Cr, Mn, Fe, CO and Ni, the plated coating forming an exposed layer of the plated aluminum sheet, the plated coating being only on one side of the aluminum sheet and the other side of the aluminum sheet being uncoated, the aluminum sheet being bent 180° and

spot welded such that portions of the uncoated side of the aluminum sheet face each other than are spot welded together.

12. A plated aluminum sheet having improved spot weldability which comprises an aluminum sheet having on one or both surfaces a plated coating of a metal which has a melting point of about 700°

C. or above, the plated coating being present in a thickness sufficient to improve efficiency of spot welding of the aluminum sheet, the plated coating having a higher electric resistivity and lower thermal conductivity than the aluminum sheet, the plated coating having a hardness higher than the aluminum sheet, and the hardness being high enough to improve sliding properties and improve press-formability of the aluminum sheet, the plated coating being a zinc base alloy containing at least one of Cr, Mn, Fe, Co and Ni, the plated coating forming an exposed layer of the plated aluminum sheet, the plated coating being on one side of the aluminum sheet and the other side of the aluminum sheet being uncoated, the uncoated side of the aluminum sheet being spot welded to an aluminum article.

13. A plated aluminum sheet having improved spot weldability which comprises an aluminum sheet having on one or both surfaces a plated coating of a metal which has a melting point of about 700°

C. or above, the plated coating being present in a thickness sufficient to improve efficiency of spot welding of the aluminum sheet, the plated coating having a higher electric resistivity and lower thermal conductivity than the aluminum sheet, the plated coating having a hardness higher than the aluminum sheet, and the hardness being high enough to improve sliding properties and improve press-formability of the aluminum sheet, the plated coating being a zinc base alloy containing at least one of Cr, Mn, Fe, Co and Ni, the plated coating forming an exposed layer of the plated aluminum sheet, the sheet comprising a press-formed and spot welded vehicle body panel.