Bullet resistant glass/glass, glass/plastic, and plastic/plastic laminate composites
First Claim
1. A glass laminate composite, comprising:
- at least two parallel sheets of glass joined by a layer of adhesive polyester prepared by cross-linking a pre-polymer, said pre-polymer prepared by preparing a linear polyester oligomer by reacting a mixture comprising at least one dibasic acid selected from the group consisting of adipic acid, phthalic anhydride, anhydride and maleic anhydride with at least one diol selected from the group consisting of dipropylene glycol and 2-methyl-1,3-propanediol to obtain a linear polyester oligomer having a molecular weight between about 900 and 1,200 measured by gel permeation chromatography;
adjusting the refractive index of said linear polyester oligomer to the refractive index of float glass by adding propylene glycol to said mixture of said dibasic acid and said diol;
and thinning said linear polyester oligomer with at least one monomer capable of cross-linking said linear polyester, said at least one monomer containing at least 60% by weight of t-butyl styrene, to obtain an adhesive polyester pre-polymer.
1 Assignment
0 Petitions
Accused Products
Abstract
This invention relates to multiple glass/plastic laminates for ballistic resistant and security applications. The laminates typically comprise a glass lite and a plastic sheet, such as polycarbonate, bonded with an adhesive based on a novel solvent free thermosetting alkyd resin. Subsequent layers can be polycarbonate sheets and/or acrylic sheets and glass lites with the adhesive layer separating the lites and sheets.
Further, this invention relates to a vertical liquid pour process which enables the rapid manufacture of bullet resistant glass/plastic laminates without the need for expensive ultra-violet or heat curing ovens. The adhesive cures at temperatures ranging from 60° F. to 90° F. High temperature and high pressure treatments are unnecessary. Laminates produced in this manner with adhesive interlayer will pass all intended ballistic or security tests within a 12 hour period.
-
Citations
12 Claims
-
1. A glass laminate composite, comprising:
-
at least two parallel sheets of glass joined by a layer of adhesive polyester prepared by cross-linking a pre-polymer, said pre-polymer prepared by preparing a linear polyester oligomer by reacting a mixture comprising at least one dibasic acid selected from the group consisting of adipic acid, phthalic anhydride, anhydride and maleic anhydride with at least one diol selected from the group consisting of dipropylene glycol and 2-methyl-1,3-propanediol to obtain a linear polyester oligomer having a molecular weight between about 900 and 1,200 measured by gel permeation chromatography; adjusting the refractive index of said linear polyester oligomer to the refractive index of float glass by adding propylene glycol to said mixture of said dibasic acid and said diol; and thinning said linear polyester oligomer with at least one monomer capable of cross-linking said linear polyester, said at least one monomer containing at least 60% by weight of t-butyl styrene, to obtain an adhesive polyester pre-polymer. - View Dependent Claims (2, 3, 4)
-
-
5. A glass/plastic laminate, comprising:
-
at least one plastic sheet in parallel relation and spaced from at least one glass sheet, said plastic sheet joined to said glass sheet by a layer of adhesive polyester prepared by cross-linking a pre-polymer, said pre-polymer prepared by preparing a linear polyester oligomer by reacting a mixture comprising at least one dibasic acid selected from the group consisting of adipic acid, phthalic anhydride, nadic anhydride and maleic anhydride with at least one diol selected from the group consisting of dipropylene glycol and 2-methyl-1,3-propanediol to obtain a linear polyester oligomer having a molecular weight between about 900 and 1,200 measured by gel permeation chromatography; adjusting the refractive index of said linear polyester oligomer to the refractive index of float glass by adding propylene glycol to said mixture of said dibasic acid and said diol; and thinning said linear polyester oligomer with at least one monomer capable of cross-linking said linear polyester, said at least one monomer containing at least 60% by weight of t-butyl styrene, to obtain an adhesive polyester pre-polymer. - View Dependent Claims (6, 7, 8)
-
-
9. A plastic/plastic laminate, comprising:
-
at least two parallel plastic sheets joined to each other by a layer of adhesive polyester resin prepared by cross-linking a pre-polymer, said pre-polymer prepared by preparing a linear polyester oligomer by reacting a mixture comprising at least one dibasic acid selected from the group consisting of adipic acid, phthalic anhydride, nadic anhydride and maleic anhydride with at least one diol selected from the group consisting of dipropylene glycol and 2-methyl-1,3-propanediol to obtain a linear polyester oligomer having a molecular weight between about 900 and 1,200 measured by gel permeation chromatography; adjusting the refractive index of said linear polyester oligomer to the refractive index of float glass by adding propylene glycol to said mixture of said dibasic acid and said diol; and thinning said linear polyester oligomer with at least one monomer capable of cross-linking said linear polyester, said at least one monomer containing at least 60% by weight of t-bytyl styrene, to obtain an adhesive polyester pre-polymer. - View Dependent Claims (10, 11, 12)
-
Specification