Porpous PTFE film and a manufacturing method therefor
First Claim
1. A thin porous polytetrafluoroethylene membrane consisting essentially of a nonwoven web having a microstructure of substantially only microfibrils fused at crossover points, said membrane having:
- (a) a pore size between 0.05 and 0.4 micrometers;
(b) a bubble point between 10 and 60 psi;
(c) a pore size distribution value between 1.05 and 1.20;
(d) a ball burst strength between 0.9 and 17 lbs./Force;
(e) an air flow of between 20 Frazier number and 10 Gurley seconds;
(f) a thickness between 1-25.4 micrometers.
3 Assignments
0 Petitions
Accused Products
Abstract
A nonwoven web is described that is a thin porous polytetrafluoroethylene membrane consisting essentially of a nonwoven web having a microstructure of substantially only microfibrils fused at crossover points. It is usually strong, is unusually thin, has unusually small pore sizes, but a very high air flow-through. It has a pore size between 0.05 and 0.4 micrometers; a bubble point between 10 and 60 psi; a pore size distribution value between 1.05 and 1.20; a ball burst strength between 0.9 and 17 pounds/force; an air flow of between 20 Frazier and 10 Gurley seconds; a thickness between 1.0-25.4 micrometer; and a fiber diameter ranging between 5 and 200 nm.
312 Citations
3 Claims
-
1. A thin porous polytetrafluoroethylene membrane consisting essentially of a nonwoven web having a microstructure of substantially only microfibrils fused at crossover points, said membrane having:
-
(a) a pore size between 0.05 and 0.4 micrometers; (b) a bubble point between 10 and 60 psi; (c) a pore size distribution value between 1.05 and 1.20; (d) a ball burst strength between 0.9 and 17 lbs./Force; (e) an air flow of between 20 Frazier number and 10 Gurley seconds; (f) a thickness between 1-25.4 micrometers. - View Dependent Claims (2, 3)
-
Specification