Spherical curing agent for epoxy resin, curing agent masterbatch for epoxy resin and their preparation

• US 5,480,957 A
• Filed: 02/18/1993
• Issued: 01/02/1996
• Est. Priority Date: 05/28/1991
• Status: Expired due to Term

• Current Assignee: Henkel Corporation (Henkel AG & Co KGaA)
• Original Assignee: W R Grace & Company - CONN (WR Grace & Company)
• Inventors: Muroi, Souichi, Tsai, Hsi-Chuan
• Primary Examiner(s): Sellers, Robert E.
• Assistant Examiner(s): GULAKOWSKI, RANDY P
• Application Number:
  US08/022,607
• Time in Patent Office: 1,048 Days
• Field of Search: 528/87, 528/93, 528/94, 528/103, 528/117, 528/118, 525/523, 525/524, 525/540, 525/65, 523/400, 523/407, 523/429
• US Class Current: 528/87
• CPC Class Codes: C08G 59/18 Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups ; e.g. general methods of curing
• CPC Class Codes: C08G 59/184 with amines
• CPC Class Codes: H05K 3/303 Surface mounted components, e.g. affixing before soldering, aligning means, spacing means H05K3/32 takes precedence

Abstract

A curing agent for epoxy resins is prepared from an amine and an epoxy, as well as subsequent modification by a polyisocyanate compound, in such a manner that the curing agent is in the form of small spherical particles. The particles can be as small as 0.1 microns. This curing agent can be easily dispersed in curing agent masterbatches and curable compositions with minimal effect on their storage stability. The resulting curable compositions have a wide range of applications, including automobile and electronic adhesives.

Claims

1. A curing agent for epoxy resin which is fine substantially spherical particles of an amine compound having only one active amino-hydrogen/polyfunctional epoxy compound adduct wherein the size of said particles is in the range or 0.1 μ

m to 30 μ

m, said particles being obtained by reacting an amine compound having only one active amino-hydrogen and a polyfunctional epoxy compound at a ratio of the epoxy group in said epoxy compound to the active amino-hydrogen in said amine compound of substantially 1;

1 in the presence of a dispersion stabilizer in an organic solvent capable of dissolving both said amine compound and said epoxy compound but incapable of dissolving the adduct formed therefrom at elevated temperatures with agitation, said dispersion stabilizer being a polymeric compound having high affinity to both said organic solvent and said adduct formed.

2. The curing agent of claim 1 having a melting point of at least 50°

C.

3. The curing agent of claim 1, wherein said amine compound is 2-methylimidazole.

4. The curing agent of claim 1, wherein said amine compound is N-methylpiperazine.

5. The curing agent of claim 1, wherein said epoxy compound has an epoxy equivalent weight of at most 1,000.

6. The curing agent of claim 5, wherein said epoxy compound has an epoxy equivalent weight of at most 500.

7. The curing agent of claim 6, wherein said epoxy compound is bisphenol A diglycidyl ether.

8. The curing agent of claim 1, wherein said dispersion stabilizer has a molecular weight of 1,000 to 300,000.

9. The curing agent of claim 8, wherein said dispersion stabilizer is a methyl methacrylate/methacrylic acid copolymer graft-copolymerized with methyl methacrylate or a styrene/glycidyl methacrylate copolymer graft-copolymerized with methyl methacrylate.

10. The curing agent of claim 1, wherein said organic solvent has a solubility parameter of 8 to 11.

11. The curing agent of claim 10, wherein said organic solvent is methyl isobutyl ketone or xylene.

12. The curing agent of claim 1, wherein said elevated temperatures are 40°

C. to 90°

C.