Extrusion impregnation compression molding process

• US 5,482,667 A
• Filed: 08/11/1993
• Issued: 01/09/1996
• Est. Priority Date: 08/11/1993
• Status: Expired due to Term

• Current Assignee: Sabic Innovative Plastics IP BV (Government of Saudi Arabia)
• Original Assignee: General Electric Company
• Inventors: Teutsch, Erich O., Dunton, Thomas P.
• Primary Examiner(s): Woo, Jay H.
• Assistant Examiner(s): SMITH, DUANE
• Application Number:
  US08/106,093
• Time in Patent Office: 881 Days
• Field of Search: 264/134, 264/135, 264/136, 264/137, 264/174, 264/257, 264/258, 264/DIG. 65, 156/166, 156/180
• US Class Current: 264/136
• CPC Class Codes: B29C 70/086 and with one or more layers of pure plastics material, e.g. foam layers applying a non-preformed coating, e.g. a gel-coat, B29C37/0025; with foam blocks B29C70/86
• CPC Class Codes: B29C 70/506 and impregnating by melting a solid material, e.g. sheet, powder, fibres B29C70/508 takes precedence

Abstract

This invention is directed to a continuous process for producing a molded thermoplastic fiber reinforced article having a high resin concentration in at least one surface thereof. The finished article may be prepared by compression molding and can have a Class A surface. The continuous process includes coating at least one surface of a heated fiber mat core with a melted first thermoplastic resin, passing the fiber mat core into an extrusion zone wherein a melted second thermoplastic resin is extruded onto at least one surface of the fiber mat core and then molding the fiber mat core and thermoplastic resin into a finished article. The continuous process of this invention provides for fast production of molded finished articles such as roof tile, automobile exterior panels, house siding, etc.

Claims

1. A continuous process for producing a molded thermoplastic resin fiber reinforced article comprising a fiber mat core and thermoplastic resin wherein the surface of the molded article has a high concentration of thermoplastic resin, which process comprises the steps of applying a molten first thermoplastic resin onto at least one surface of a heated fiber mat core, passing the combination to an extrusion zone, applying molten second thermoplastic resin to at least one surface of the heated fiber mat core and molten first thermoplastic resin, passing the combination of the molten first thermoplastic resin, molten second thermoplastic resin and fiber mat core to a molding zone, and molding the heated combination under pressure into a molded thermoplastic resin fiber reinforced article having on at least one surface a high concentration of the second thermoplastic resin wherein prior to said molding, a material selected from the group consisting of powdered pigment and a blend of a powdered pigment and a powdered thermoplastic resin is applied to the surface of the combination of the fiber mat core and molten first and second thermoplastic resin.

2. The process of claim 1 wherein the first molten thermoplastic resin and the second molten thermoplastic resin are the same thermoplastic resin.

3. The process of claim 1 wherein the second thermoplastic resin is extruded onto the top and bottom surfaces of the combination of fiber mat and first molten thermoplastic resin.

4. The process of claim 1 wherein the heated fiber mat core is impregnated with the first molten thermoplastic resin prior to extruding the molten second thermoplastic resin onto said heated fiber mat second thermoplastic resin onto said heated fiber mat core by passing the fiber mat core and first molten thermoplastic resin through the nip of a pair of opposing heated wet-out rolls wherein the pressure of the rolls on the fiber mat core and first molten thermoplastic resin is sufficient to force said first molten thermoplastic resin into the fiber mat core in order to coat the fiber surfaces thereof.

5. The process of claim 1 wherein the temperature of the heated fiber mat is such as to maintain the second thermoplastic resin in the molten state when in the molding zone.

6. The process of claim 1 wherein a material selected from the group consisting of powdered pigment and a blend of a powdered pigment and a powdered thermoplastic resin is applied to the surface of the combination of the fiber mat core and molten first and second thermoplastic resin having the high concentration of the second thermoplastic resin prior to the molding of the said combination.

7. A continuous process for producing a molded thermoplastic resin fiber reinforced article comprising a fiber mat core and thermoplastic resin wherein the surface of the molded article has a high concentration of thermoplastic resin, which process consists essentially of:

passing at least one layer of a fiber mat core into a preheat zone,

heating the fiber mat core to a temperature sufficient to maintain the first thermoplastic resin in the molten state,

passing the preheated fiber mat core through a resin coating zone wherein the melted first thermoplastic resin is applied to at least one surface of the heated fiber mat core,

passing the heated fiber mat core and the first melted thermoplastic resin to an extrusion zone wherein a melted second thermoplastic resin is extruded onto at least one surface of the fiber mat core,

passing the heated combination of fiber mat core, first melted thermoplastic resin and second melted thermoplastic resin to a molding zone, and

molding the combination under pressure into the molding thermoplastic resin fiber reinforced article wherein at least one surface thereof has a high concentration of the second thermoplastic resin wherein prior to said molding, a material selected from the group consisting of powdered pigment and a blend of a powdered pigment and a powdered thermoplastic resin is applied to the surface of the combination of the fiber mat core and molten first and second thermoplastic resin prior.

8. The process of claim 7 wherein the coating zone, the molten first thermoplastic resin is applied to both top and bottom surfaces of the fiber mat core.

9. The process of claim 7 wherein the fiber mat core having the first molten thermoplastic resin coated onto one surface of the fiber mat core is passed between the nip of at least two opposing heated wet-out rolls, the temperature of the surface of which rolls are such as to avoid sticking of the first molten thermoplastic resin to the surface of the rolls and wherein the pressure of the rolls on the fiber mat core and first molten thermoplastic resin is sufficient to force said thermoplastic resin into the fiber mat core in order to coat the fiber surfaces thereof.

10. The process of claim 9 wherein the fiber core consists of chopped glass fibers of about 1/8" to about 2" in length.

11. A continuous process for producing a molded thermoplastic resin fiber reinforced article comprising a fiber mat core and thermoplastic resin wherein the surface of the molded article has a high concentration of thermoplastic resin, which process comprises the steps of applying a molten first thermoplastic resin onto at least one surface of a heated fiber mat core, passing the combination to an extrusion zone, applying a molten second thermoplastic resin to at least one surface of the heated fiber mat core and molten first thermoplastic resin, said first molten thermoplastic resin and said second molten thermoplastic resin are the same thermoplastic resin, said first molten thermoplastic resin is an aromatic polycarbonate resin having an intrinsic viscosity of less than about 0.5 dl/gram and the second molten thermoplastic resin is an aromatic polycarbonate resin having an intrinsic viscosity of greater than about 0.5 dl/gram, passing the combination of the molten first thermoplastic resin, molten second thermoplastic resin and fiber mat core to a molding zone, and molding the heated combination under pressure into a molded thermoplastic resin fiber reinforced article having on at least one surface a high concentration of the second thermoplastic resin.