Magnetic recording medium

• US 5,496,607 A
• Filed: 11/25/1994
• Issued: 03/05/1996
• Est. Priority Date: 04/14/1992
• Status: Expired due to Term

• Current Assignee: Fujifilm Corporation (Fujifilm Holdings Corporation)
• Original Assignee: Fuji Photo Film Co Limited (Fujifilm Holdings Corporation)
• Inventors: Nakamikawa, Jun-ichi, Miura, Toshihiko, Ejiri, Kiyomi, Inaba, Hiroo
• Primary Examiner(s): KILIMAN, LESZEK B
• Application Number:
  US08/348,949
• Time in Patent Office: 466 Days
• Field of Search: 428/694 B, 428/694 BS, 428/694 BN, 428/694 BA, 428/694 BH, 428/900, 428/694 BM, 428/65.3
• US Class Current: 428/840.6
• CPC Class Codes: G11B 5/733 characterised by the addition of non-magnetic particles base layers having a non-magnetic layer under a soft magnetic layer G11B5/736; magnetic recording media substrates G11B5/739
• CPC Class Codes: Y10S 428/90 Magnetic feature
• CPC Class Codes: Y10T 428/265 1 mil or less

Abstract

Disclosed is a magnetic recording medium comprising at least two layers comprising at least one lower non-magnetic layer containing at least a non-magnetic particle and a binder on a non-magnetic support, and at least one upper magnetic layer containing at least a ferromagnetic particle and a binder on the lower non-magnetic layer, wherein a mean total thickness d of the upper magnetic layer is more than 0.01 μm to less than 0.3 μm, and a standard deviation σ of the total thickness of the upper magnetic layer and the mean total thickness d of the upper magnetic layer satisfy the relationship of 0.05≦σ/d≦0.5.

Claims

1. A magnetic recording medium, comprising a non-magnetic support and at least two layers, the at least two layers comprising at least one lower non-magnetic layer comprising non-magnetic particles and a binder, one of the at least one non-magnetic layers being located on the non-magnetic support, and at least one upper magnetic layer comprising ferromagnetic particles and a binder, one of the at least one upper magnetic layers being located on the lower non-magnetic layer located on the non-magnetic support, wherein the upper magnetic layer located on the lower non-magnetic layer located on the non-magnetic support has a mean total thickness d more than 0.01 μ

m to less than 0.3 μ

m, and a standard deviation σ

of the total thickness of the upper magnetic layer located on the lower non-magnetic layer located on the non-magnetic support and the mean total thickness d satisfy the following relationship;

space="preserve" listing-type="equation">0.05<

σ

/d<

0.5.

2. The magnetic recording medium as in claim 1, wherein the magnetic recording medium is selected from the group consisting of an audio tape, a video tape, a computer tape and a floppy disk for digital signal recording.

3. The magnetic recording medium as in claim 1, further comprising non-magnetic particles located in the upper magnetic layer, the upper layer non-magnetic particles having a mean particle size of 0.005 to 2 μ

m.

4. The magnetic recording medium as in claim 1, further comprising non-magnetic particles located in the upper magnetic layer, the upper layer non-magnetic particles having an average longest diameter a satisfying the following relationship:

space="preserve" listing-type="equation">0.1≦

a/d≦

5.

5. The magnetic recording medium as in claim 1, wherein the magnetic recording medium has a coercive force in a plane of the upper magnetic layer parallel to a plane of the non-magnetic support of from 1,000 to 3,000 Oe, the coercive force being measured in a direction along a plane wherein the coercive force is highest, and the upper magnetic layer has a saturation magnetization in the plane of the upper magnetic layer parallel to a plane of the non-magnetic support of from 0.002 to 0.15 emu.

6. The magnetic recording medium as in claim 1, wherein the upper magnetic layer located on the lower non-magnetic layer located on the non-magnetic support has a coercive force in a direction perpendicular to a plane of the non-magnetic support of from 900 to 5,000 Oe, and a saturation magnetization per cm² in the perpendicular direction of from 0.001 to 0.014 emu.

7. The magnetic recording medium as in claim 1, wherein the lower non-magnetic layer is forced from a coating solution coated on the non-magnetic support and then, while the coating solution is still in a wet state, a coating solution for forming the upper magnetic layer is coated on the lower non-magnetic layer.

8. The magnetic recording medium as in claim 1, wherein the magnetic recording medium has a half-value width W₅₀ of an isolated pulse waveform of 0.6 μ

m or less and a symmetry γ

thereof at a recording current of at least 20 mA is up to 10%, as measured using an external contact type drum tester equipped with a laminated Sendust head having a gap length of 0.2 μ

m and a track width of 20 μ

m at a relative tape speed at the magnetic head of 3.8 m/sec.

9. The magnetic recording medium as in claim 1, wherein the mean total thickness d of the upper magnetic layer is from 0.02 to 0.25 μ

m and σ

/d is from 0.1/l to 0.4/l.

10. The magnetic recording medium as in claim 1, wherein a difference Δ

T between a maximum value and a minimum value of the total thickness of the upper magnetic layer located on the lower non-magnetic layer located on the non-magnetic support satisfies the following relationship;

space="preserve" listing-type="equation">0.001<

Δ

T/d<

0.55.

11. The magnetic recording medium as in claim 1, further comprising non-magnetic abrasive particles located in the upper magnetic layer located on the lower non-magnetic layer located on the non-magnetic support.

12. The magnetic recording medium as in claim 1, further comprising non-magnetic particles located in the upper magnetic layer located on the lower non-magnetic layer located on the non-magnetic support in an amount of 0.01 to 30 parts by weight per 100 parts by weight of the ferromagnetic particles.

13. The magnetic recording medium as in claim 1, further comprising non-magnetic particles present in the upper magnetic layer located on the lower non-magnetic layer located on the non-magnetic support in a proportion from 20 to 0.1 by weight and from 10 to 0.1 by volume, based on the binder in the upper magnetic layer located on the lower non-magnetic layer located on the non-magnetic support.

14. The magnetic recording medium as in claim 1, wherein the lower non-magnetic layer or the upper magnetic layer has a multilayer structure.

15. The magnetic recording medium as in claim 1, further comprising carbon black located in the upper magnetic layer located on the lower non-magnetic layer located on the non-magnetic support the carbon black being present in an amount of 0.1 to 30% by weight based on the amount of the ferromagnetic particle in the upper magnetic layer located on the lower non-magnetic layer located on the non-magnetic support.

16. The magnetic recording medium as in claim 1, wherein the mean total thickness d of the upper magnetic layer located on the lower non-magnetic layer located on the non-magnetic support is from 0.02 to 0.23 μ

m.

17. The magnetic recording medium as in claim 1, wherein σ

/d is from 0.1/l to 0.4/l.

18. The magnetic recording medium as in claim 5, wherein the ferromagnetic particles are acicular ferromagnetic particles having an acicular ratio of 3/l to 20/l and a long axis length of 0.3 μ

m or less.

19. The magnetic recording medium as in claim 6, wherein the ferromagnetic particles are hexagonal tabular shaped ferromagnetic particles having an axis of easy magnetization perpendicular to a plate face.

20. The magnetic recording medium as in claim 16, wherein the mean total thickness d of the upper magnetic layer located on the lower non-magnetic layer located on the non-magnetic support is from 0.03 to 0.23 μ

m.