Distortion control additives for ultraviolet-curable compositions

• US 5,498,782 A
• Filed: 09/08/1993
• Issued: 03/12/1996
• Est. Priority Date: 09/08/1993
• Status: Expired due to Fees

• Current Assignee: Union Carbide Chemicals & Plastics Technology Corporation (Dow, Inc.)
• Original Assignee: Union Carbide Chemicals & Plastics Technology Corporation (Dow, Inc.)
• Inventors: Rex, Gary C.
• Primary Examiner(s): Seidleck, James J.
• Assistant Examiner(s): SERGENT, RABON A
• Application Number:
  US08/118,014
• Time in Patent Office: 916 Days
• Field of Search: 522/96, 522/90, 522/107, 522/103, 525/126, 525/440, 525/455, 525/457, 525/458, 525/528, 525/123, 528/75
• US Class Current: 525/126
• CPC Class Codes: B33Y 70/00 Materials specially adapted for additive manufacturing
• CPC Class Codes: C08F 222/103 of trialcohols, e.g. trimethylolpropane tri(meth)acrylate
• CPC Class Codes: C08F 283/006 on to polymers provided for in C08G18/00 C08F283/004 takes precedence
• CPC Class Codes: C08F 290/067 Polyurethanes; Polyureas
• CPC Class Codes: C08G 18/637 characterised by the in situ polymerisation of the compounds having carbon-to-carbon double bonds in a reaction mixture of saturated polymers and isocyanates
• CPC Class Codes: C09D 4/00 Coating compositions, e.g. paints, varnishes or lacquers, based on organic non-macromolecular compounds having at least one polymerisable carbon-to-carbon unsaturated bond ; Coating compositions, based on monomers of macromolecular compounds of groups C09D183/00 - C09D183/16

Abstract

Distortion control additives are disclosed which comprise a polyisocyanate, a polyol or polyol blend having a hydroxyl functionality of 2 to 3 hydroxyl groups per molecule and an average molecular weight of at least about 500 grams per gram mole, a diol chain extender having from about 2 to 35 carbon atoms per molecule and an acrylate or methacrylate having an acrylate functionality of from 1 to 5 acrylate groups per molecule. Ultraviolet-curable liquid compositions comprising an unsaturated polymeric resin, a monomer and the distortion control additives of the present invention are also disclosed. The distortion control additives can provide substantial reductions in distortion, e.g., shrinkage, of objects produced by ultraviolet curing, e.g., stereolithography.

Claims

1. In an ultraviolet-curable liquid composition comprising;

(i) an unsaturated polymeric resin having an average molecular weight of at least 500 grams per gram mole;

(ii) a monomer suitable for crosslinking with the unsaturated polymeric resin; and

(iii) a distortion control additive;

the improvement wherein the distortion control additive comprises the reaction product of;

(a) from about 1 to 10 weight percent of a polyisocyanate;

(b) from about 30 to 60 weight percent of a polyol or polyol blend having a hydroxyl functionality of 2 to 3 hydroxyl groups per molecule and an average molecular weight of about 500 to 10,000 grams per gram mole;

(c) from about 0.2 to 6 weight percent of a diol chain extender having between 2 and 32 carbon atoms per molecule; and

(d) from about 20 to 90 weight percent of an acrylate or methacrylate having a acrylate functionality of from 2 to 5 acrylate groups per molecule.

2. The composition of claim 1 wherein the acrylate or methacrylate comprises from about 4 to 35 carbon atoms per molecule.

3. The composition of claim 1 comprising from about 5 to 60 weight percent of the distortion control additive.

4. The composition of claim 1 wherein the acrylate or methacrylate is selected from the group consisting of, trimethylol propane trimethacrylate, trimethylol propane triacrylate, pentaerythritol trimethacrylate, 1,6-hexanediol diacrylate, 1,6-hexane diol dimethacrylate, pentaerythritol tetraacrylate, pentaerythritol tetramethacrylate, ethoxylated and propoxylated derivatives thereof, and mixtures thereof.

5. The composition of claim 1 wherein the monomer is the same as said acrylate or methacrylate.

6. In an ultraviolet-curable liquid composition comprising;

(i) from about 40 to 60 weight percent of an unsaturated polymeric resin having an average molecular weight of at least 500 grams per gram mole;

(ii) from about 30 to 60 weight percent of a monomer suitable for crosslinking with the unsaturated polymeric resin; and

(iii) from about 5 to 60 weight percent of a distortion control additive;

the improvement wherein the distortion control additive comprises the reaction product of;

(a) from about 1 to 10 weight percent of a polyisocyanate;

(b) from about 30 to 60 weight percent of a polyol or polyol blend having a hydroxyl functionality of 2 to 3 hydroxyl groups per molecule and an average molecular weight of about 500 to 10,000 grams per gram mole;

(c) from about 0.2 to 6 weight percent of a diol chain extender having from about 2 to 8 carbon atoms per molecule; and

(d) from about 20 to 90 weight percent of an acrylate or methacrylate having a acrylate functionality of from 2 to 5 acrylate groups per molecule.

7. The composition of claim 6 wherein the acrylate or methacrylate is selected from the group consisting of trimethylol propane trimethacrylate, trimethylol propane triacrylate, and mixtures thereof.

8. The composition of claim 6 wherein the polyisocyanate is selected from the group consisting of 2,4-toluene diisocyanate, 2,6-toluene diisocyanate, 4,4'"'"'-diphenylmethane diisocyanate and isomers thereof, isophorone diisocyanate, and mixtures thereof.

9. The composition of claim 6 wherein the polyol has an average molecular weight of from about 1000 to 3000 grams per gram mole.

10. The composition of claim 6 wherein the diol chain extender is selected from the group consisting of neopentyl glycol, butanediol isomers, hexanediol isomers, ethylene glycol, propylene glycol isomers, isomers of cyclohexane dimethanol, octanediol isomers, diethylene glycol, and dipropylene glycol.

11. The composition of claim 6 wherein the diol chain extender is selected from the group consisting of neopentyl glycol, 1,4-butanediol, 1,6-hexanediol, ethylene glycol, 1,3-propylene glycol, 1,2-propylene glycol, 1,6-octanediol, diethylene glycol and dipropylene glycol.

12. The composition of claim 6 wherein the distortion control additive comprises less than about 5 weight percent of olefinically unsaturated non-acrylic reactants.

13. The composition of claims 6 wherein the distortion control additive comprises the reaction product of:

(a) from about 4 to 6 weight percent of 2,4-toluene diisocyanate;

(b) from about 35 to 50 weight percent of a polyester polyol based on the reaction product of polycarboxylic acids or anhydrides and diols;

(c) from about 0.5 to 4.0 weight percent of 1,4-butanediol, ethylene glycol or mixtures thereof; and

(d) from about 40 to 60 weight percent of trimethylol propane triacrylate, trimethylol propane trimethacrylate, and mixtures thereof.

14. The composition of claim 13 wherein the distortion control additive has less than about 1 weight percent of olefinically unsaturated non-acrylic reactants.

15. In an ultraviolet-curable liquid composition comprising;

(i) from about 40 to 60 weight percent of an unsaturated polymeric resin having an average molecular weight of at least 500 grams per gram mole;

(ii) a monomer suitable for crosslinking with the unsaturated polymeric resin; and

(iii) from about 5 to 60 weight percent of a distortion control additive;

the improvement wherein;

(1) the distortion control additive comprises the reaction product of;

(a) from about 4 to 6 weight percent of 2,4-toluene diisocyanate;

(b) from about 35 to 50 weight percent of a polyester polyol based on the reaction product of polycarboxylic acids or anhydrides and diols, said polyol having an average molecular weight of about 500 to 10,000 grams per gram mole;

(c) from about 0.5 to 4.0 weight percent of 1,4-butanediol, ethylene glycol or mixtures thereof; and

(d) from about 40 to 60 weight percent of trimethylol propane triacrylate, trimethylol propane trimethacrylate, or mixtures thereof; and

(2) the distortion control additive has less than about 1 weight percent of olefinically unsaturated non-acrylic reactants.