Dental glass ionomer cement composition

• US 5,520,725 A
• Filed: 06/22/1995
• Issued: 05/28/1996
• Est. Priority Date: 07/18/1994
• Status: Expired due to Term

• Current Assignee: GC Corporation (General Cannabis Corp.)
• Original Assignee: GC Corporation (General Cannabis Corp.)
• Inventors: Fusejima, Futoshi, Yoshikawa, Tohru, Kato, Shin-ichi
• Primary Examiner(s): GREEN, ANTHONY J
• Application Number:
  US08/493,467
• Time in Patent Office: 341 Days
• Field of Search: 106/35, 523/115, 523/116, 433/228.1, 522/908
• US Class Current: 106/35
• CPC Class Codes: A61K 6/30 Compositions for temporarily or permanently fixing teeth or palates, e.g. primers for dental adhesives
• CPC Class Codes: A61K 6/889 Polycarboxylate cements; Glass ionomer cements
• CPC Class Codes: A61K 6/891 Compounds obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds
• CPC Class Codes: A61K 6/893 Polyurethanes
• CPC Class Codes: C04B 2111/00836 for medical or dental applications
• CPC Class Codes: C04B 24/20 Sulfonated aromatic compounds
• CPC Class Codes: C04B 24/26 obtained by reactions only involving carbon-to-carbon unsaturated bonds C04B24/243 takes precedence
• CPC Class Codes: C04B 28/28 containing organic polyacids, e.g. polycarboxylate cements , i.e. ionomeric systems
• CPC Class Codes: C08F 8/44 Preparation of metal salts or ammonium salts
• CPC Class Codes: C08L 33/00 Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides or nitriles thereof; Compositions of derivatives of such polymers
• CPC Class Codes: C08L 63/10 Epoxy resins modified by unsaturated compounds
• CPC Class Codes: C08L 75/16 having terminal carbon-to-carbon unsaturated bonds
• CPC Class Codes: Y10S 522/908 Dental utility

Abstract

The invention provides a dental glass ionomer cement composition comprising (a) an α-β unsaturated carboxylic acid polymer having a weight-average molecular weight lying in a specific range, (b) a polymerizable unsaturated organic compound having a CH₂ ═C(R1)--COO group, (c) water, (d) an organic aromatic compound having a --SO₂ group, (e) a fluoroaluminosilicate glass powder having a mean particle size and specific gravity each lying in a specific range and capable of reacting with the component (a), and (f) a compound containing at least one element selected from the group consisting of aluminum, iron and tin. This composition can be cured either without recourse to conventional redox reaction systems or without exposure to visible light. It can be used with good-enough physical properties for dental therapy while it is harmless to the dental pulp, and can be stored over an extended period of time.

Claims

1. A dental glass ionomer cement composition consisting essentially of:

(a) an α

-β

unsaturated carboxylic acid polymer having a weight-average molecular weight lying in the range of 5,000 to 40,000

(b) a polymerizable unsaturated organic compound having at least one group having the following general formula;

space="preserve" listing-type="equation">CH.sub.2 ═

C(R1)--COO where R1 is H or CH.sub.3

(c) water

(d) an organic aromatic compound having at least one --SO₂ group selected from the group consisting or aromatic sulfinic acids and metal salts thereof and aromatic sulfonyl compounds,

(e) a fluoroaluminosilicate glass powder which has a mean particle size lying in the range of 0.02 to 10 μ

m and a specific gravity lying in the range of 2.4 to 4.0 and is capable of reacting with said α

-β

unsaturated carboxylic acid polymer (a) having a weight-average molecular weight lying in the range of 5,000 to 40,000, and

(f) a compound selected from the group consisting of aluminum chloride, aluminum oxide, aluminum acetate, aluminum salicylate, aluminum acrylate, aluminum oxalate, aluminum hydroxide, aluminum nitrate, aluminum carbonate, aluminum lactate, aluminum fluoride, aluminum sulfate, aluminum itaconate, aluminum phosphate, aluminum polychloride, aluminum iodide, aluminum acetylacetonate, aluminum bromide, aluminum butoxide, aluminum butylate, aluminum ethoxide, aluminum cyclohexanelactate, aluminum ethylhexoate, aluminum isopropoxide, aluminum laurate, aluminum oleate, potassium aluminum sulfate, aluminum stearate, aluminum triethoxide, aluminum triethylate, aluminum triisopropoxide, aluminum triisopropylate, barium aluminate, lithium aluminum hydride, sodium aluminate, iron oxide, iron chloride, iron sulfate, iron nitrate, iron hydroxide, iron ammonium sulfate, iron citrate, iron succinate, iron bromide, iron phosphate, iron dichloride, ethylenediamine iron, iron oxalate, iron lactate, iron ethylenediaminetetraacetate, iron 2-ethylhexoate, potassium ferrocyanide, potassium ferricyanide, acetylacetonatosodium ferrocyanide, iron alum, sodium iron citrate, sodium iron oxalate, iron ammonium sulfate, benzoylacetonatoiron, dicyclopentadienyliron, N,N-dimethyl-1-ferrocenylethylamine, iron decanoate, iron naphthenate, iron pentacarbonyl, iron nonacarbonyl, iron perchlorate, phthalocyanine iron, sodium pentacyanonitrosylferrate, sodium pentacyanoammineferrate, dicyano-bis(1,10-phenanthroline) iron, tris(1-phenyl-1,3-butanedionate)iron, tin oxide, tin chloride, tin acetate, tin phosphate, tin diphosphate, tin pyrophosphate, tin fluoride, tin iodide, tin oxalate, tin sulfate, tin bromide, tin tetrachloride, tin borofluoride, 2-ethylhexanoic acid tin salt, triphenyltin hydroxide, bis(tributyltin)oxide, di-n-butyltin diacetate, dibutyltin dichloride, di-n-butyltin dilaurate, dibutyltin oxide, hexabutyltin, bis(2-ethylhexanoic acid)dibutyltin, potassium stannate, sodium stannate, tetrabutyltin, tetraethyltin, tetramethyltin, tetraoctyltin, tetraphenyltin, tributyltin acetate, trimethyltin chloride, triethyltin chloride, tripropyltin chloride, and tributyltin chloride.

2. The dental glass ionomer cement composition as recited in claim 1, wherein said polymerizable unsaturated organic compound (b) is incapable of reacting with said fluoroaluminosilicate glass powder (e).

4. The dental glass ionomer cement composition as recited in any one of claims 1 or 2 further consisting essentially of an additional component (g) that is a photopolymerization initiator.

6. The dental glass ionomer cement composition as recited in any one of claims 1 or 5, wherein said α

-β

unsaturated carboxylic acid polymer (a) is a copolymer or homopolymer of at least one monomer selected from the group consisting of acrylic acid, methacrylic acid, 2-chloroacrylic acid, 3-chloroacrylic acid, aconitic acid, mesaconic acid, maleic acid, itaconic acid, fumaric acid, glutaconic acid and citraconic acid.

7. The dental glass ionomer cement composition as recited in any one of claims 1 or 5, wherein said α

-β

unsaturated carboxylic acid polymer (a) is a homopolymer of acrylic acid or maleic acid, or a copolymer containing acrylic acid or maleic acid.

8. The dental glass ionomer cement composition as recited in any one of claims 1 or 5, wherein said polymerizable unsaturated organic compound (b) is an ester of acrylic acid or methacrylic acid.

9. The dental glass ionomer cement composition as recited in any one of claims 1 or 5, wherein said fluoroaluminosilicate glass powder (e) is a fluoroaluminosilicate glass powder comprising Al³⁺, Si⁴⁺, F^-, O^2- and at least one of Sr²⁺ or Ca²⁺.

10. The dental glass ionomer cement compositions as recited in any one of claims 1 or 5, wherein said fluoraluminosilicate glass powder (e) is a fluoroaluminosilicate glass powder having a surface coated with 0.01 to 20 parts by weight of an organic compound having a polymerizable ethylenic unsaturated double bond, per 100 parts by weight of said glass powder.

11. The dental glass ionomer cement composition as recited in any one of claims 1 or 5, further consisting essentially of (h) 0.01 of 50 parts by weight of an inorganic filler having a mean particle size of 0.02 to 10 μ

m and incapable of reacting with said α

-β

unsaturated carboxylic acid polymer (a).

12. The dental glass ionomer cement composition as recited in claim 11, wherein said inorganic filler (h) is an inorganic filler having a surface coated with 0.01 to 20 parts by weight of an organic compound having a polymerizable ethylenic unsaturated double bond, per 100 parts by weight of said inorganic filler.

13. The dental glass ionomer cement composition as recited in any one of claims 1 or 5, further consisting essentially of 0.01 to 20 parts by weight of a water-soluble polymer (i).

3. A dental glass ionomer cement composition consisting essentially of:

(a) 5 to 100 parts by weight of an α

-β

unsaturated carboxylic acid polymer having weight-average molecular weight lying in the range of 5,000 to 40,000,

(b) 5 to 100 parts by weight of a polymerizable unsaturated organic compound having at least one group having the following formula;

space="preserve" listing-type="equation">CH.sub.2 --C(R1)--COO where R1 is H or CH.sub.3

(c) 5 to 50 part as by weight of water

(d) 0.01 to 5 parts by weight of an organic aromatic compound having at least one --SO₂ group selected from the group consisting of aromatic sulfinic acids and metal salts thereof and aromatic sulfonyl compounds,

(e) 5 to 100 parts by weight of a fluoroaluminosilicate glass powder which has a mean particle size lying in the range of 0.02 to 10 μ

m and a specific gravity lying in the range of 2.4 to 4.0 and is capable of reacting with said α

-β

unsaturated carboxylic acid polymer (a) having a weight-average molecular weight lying in the range of 5,000 to 40,000, and

(f) 0.01 to 100 parts by weight of a compound selected from the group consisting of aluminum chloride, aluminum oxide, aluminum acetate, aluminum salicylate, aluminum acrylate, aluminum oxalate, aluminum hydroxide, aluminum nitrate, aluminum carbonate, aluminum lactate, aluminum fluoride, aluminum sulfate, aluminum itaconate, aluminum phosphate, aluminum polychloride, aluminum iodide, aluminum acetylacetonate, aluminum bromide, aluminum butoxide, aluminum butyrate, aluminum ethoxide, aluminum cyclohexanelactate, aluminum ethylhexoate, aluminum isopropoxide, aluminum laurate, aluminum oleate, potassium aluminum sulfate, aluminum stearate, aluminum triethoxide, aluminum triethylate, aluminum triisopropoxide, aluminum triisopropylate, barium aluminate, lithium aluminum hydride, sodium aluminate, iron oxide, iron chloride, iron sulfate, iron nitrate, iron hydroxide, iron ammonium sulfate, iron citrate, iron succinate, iron bromide, iron phosphate, iron dichloride, ethylenediamine iron, iron oxalate, iron lactate, iron ethylenediaminetetraacetate, iron 2-ethylhexoate, potassium ferrocyanide, potassium ferricyanide, acetylacetonatosodium ferrocyanide, iron alum, sodium iron citrate, sodium iron oxalate, iron ammonium sulfate, benzoylacetonatoiron, dicyclopentadienyliron, N,N-dimethyl-1-ferrocenylethylamine, iron decanoate, iron naphthenate, iron pentacarbonyl, iron nonacarbonyl, iron perchlorate, phthalocyanine iron, sodium pentacyanonitrosylferrate, sodium pentacyanoammineferrate, dicyano-bis(1,10-phenanthroline) iron, tris(1-phenyl-1,3-butanedionate)iron, tin oxide, tin chloride, tin acetate, tin phosphate, tin diphosphate, tin pyrophosphate, tin fluoride, tin iodide, tin oxalate, tin sulfate, tin bromide, tin tetrachloride, tin borofluoride, 2-ethylhexanoic acid tin salt, triphenyltin hydroxide, bis(tributyltin)oxide, di-n-butyltin diacetate, dibutyltin dichloride, di-n-butyltin dilaurate, dibutyltin oxide, hexabutyltin, bis(2-ethylhexanoic acid) dibutyltin, potassium stannate, sodium stannate, tetrabutyltin, tetraethyltin, tetramethyltin, tetraoctyltin, tetraphenyltin, tributyltin acetate, trimethyltin chloride, triethyltin chloride, tripropyltin chloride, and tributyltin chloride.

5. A dental glass ionomer cement composition consisting essentially of:

(a) 5 to 100 parts by weight of an α

-β

unsaturated carboxylic acid polymer having a weight-average molecular weight lying in the range of 5,000 to 40,000,

(b) 5 to 100 parts by weight of a polymerizable unsaturated organic compound having at least one group having the following general formula;

space="preserve" listing-type="equation">CH.sub.2 --C(R1)--COO where R1 is H or CH.sub.3

(c) 5 to 50 parts by weight of water

(d) 0.01 to 5 parts by weight of an organic aromatic compound having at least one --SO₂ group selected from the group consisting of aromatic sulfinic acids and metal salts thereof and aromatic sulfonyl compounds,

(e) 5 to 100 parts by weight of a fluoroaluminosilicate glass powder which has a mean particle size lying in the range of 0.02 to 10 μ

m and a specific gravity lying in the range of 2.4 to 4.0 and is capable of reacting with said α

-β

unsaturated carboxylic acid polymer (a) having a weight-average molecular weight lying in the range of 5,000 to 40,000,

(f) 0.01 to 100 parts by weight of a compound selected from the group consisting of aluminum chloride, aluminum oxide, aluminum acetate, aluminum salicylate, aluminum acrylate, aluminum oxalate, aluminum hydroxide, aluminum nitrate, aluminum carbonate, aluminum lactate, aluminum fluoride, aluminum sulfate, aluminum itaconate, aluminum phosphate, aluminum polychloride, aluminum iodide, aluminum acetylacetonate, aluminum bromide, aluminum butoxide, aluminum butylate, aluminum ethoxide, aluminum cyclohexanelactate, aluminum ethylhexoate, aluminum isopropoxide, aluminum laurate, aluminum oleate, potassium aluminum sulfate, aluminum stearate, aluminum triethoxide, aluminum triethylate, aluminum triisopropoxide, aluminum triisopropylate, barium aluminate, lithium aluminum hydride, sodium aluminate, iron oxide, iron chloride, iron sulfate, iron nitrate, iron hydroxide, iron ammonium sulfate, iron citrate, iron succinate, iron bromide, iron phosphate, iron dichloride, ethylenediamine iron, iron oxalate, iron lactate, iron ethylenediaminetetraacetate, iron 2-ethylhexoate, potassium ferrocyanide, potassium ferricyanide, acetylacetonatosodium ferrocyanide, iron alum, sodium iron citrate, sodium iron oxalate, iron ammonium sulfate, benzoylacetonatoiron, dicyclopentadienyliron, N,N-dimethyl-1-ferrocenylethylamine, iron decanoate, iron naphthenate, iron pentacarbonyl, iron nonacarbonyl, iron perchlorate, phthalocyanine iron, sodium pentacyanonitrosylferrate, sodium pentacyanoammineferrate, dicyano-bis(1,10-phenanthroline) iron, tris(1-phenyl-1,3-butanedionate) iron, tin oxide, tin chloride, tin acetate, tin phosphate, tin diphosphate, tin pyrophosphate, tin fluoride, tin iodide, tin oxalate, tin sulfate, tin bromide, tin tetrachloride, tin borofluoride, 2-ethylhexanoic acid tin salt, triphenyltin hydroxide, bis(tributyltin)oxide, di-n-butyltin diacetate, dibutyltin dichloride, di-n-butyltin dilaurate, dibutyltin oxide, hexabutyltin, bis(2-ethylhexanoic acid)dibutyltin, potassium stannate, sodium stannate, tetrabutyltin, tetraethyltin, tetramethyltin, tetraoctyltin, tetraphenyltin, tributyltin acetate, trimethyltin chloride, triethyltin chloride, tripropyltin chloride, and tributyltin chloride, and

(g) 0.01 to 5 parts by weight of a photopolymerization initiator.