Surgical dressing and an adhesive composition therefor

• US 5,571,080 A
• Filed: 04/06/1994
• Issued: 11/05/1996
• Est. Priority Date: 04/20/1993
• Status: Expired due to Fees

• Current Assignee: Ole R. Jensen
• Original Assignee: Ole R. Jensen
• Inventors: Jensen, Ole R.
• Primary Examiner(s): Green, Randall L.
• Assistant Examiner(s): STRIGHT, RONALD K
• Application Number:
  US08/223,649
• Time in Patent Office: 944 Days
• Field of Search: 602/41, 602/44, 602/53, 602/43, 602/42, 602/48, 602/47, 602/54, 602/52, 602/56, 602/58, 602/57, 604/304, 604/307, 604/368, 604/370, 604/371, 604/372, 604/373-375, 604/337, 604/308, 128/156, 424/443, 424/448, 424/445
• US Class Current: 602/56
• CPC Class Codes: A61F 5/443 having adhesive seals for securing to the body, e.g. of hydrocolloid type, e.g. gels, starches, karaya gums adhesives or sealing pads therefor A61L24/00
• CPC Class Codes: A61L 15/58 Adhesives
• CPC Class Codes: A61L 15/60 Liquid-swellable gel-forming materials, e.g. super-absorbents

Abstract

An adhesive composition, and the surgical dressing of which it is a part, in which the composition takes the form of a water-absorbing and water-swellable hydrocolloid material distributed throughout the interstices of a three-dimensional, open-mesh, randomly-oriented network of flexible, water-insoluble, polymeric filaments, such filaments being surface coated by a tacky, water-insoluble adhesive material that has an adherence affinity for the filaments and that secures such coated filaments together at their points or zones of contact. When hydrated, the hydrocolloid material swells and become a gelatinous continuous phase, with the network of filaments expanding to retain the hydrated hydrocolloid material within the dressing. Despite the phase change, the water-insoluble adhesive material is also retained within the dressing because of its strong adherence to the filaments of the network.

Claims

1. An adhesive surgical dressing comprising:

a backing layer having first and second side surfaces, and

an adhesive composition applied to one of said surfaces;

said adhesive composition comprising a three-dimensional, open cell mesh network of discrete polymeric filaments coated with a tacky water-insoluble adhesive material having an adherence affinity for said filaments and joining the coated filaments together at their intersections to maintain the integrity of said said network;

and a hydrocolloid material composed of one or more water-absorbing and swellable hydrocolloids, said hydrocolloid material being dispersed throughout the open cells of said network;

said network being expandable for retaining said hydrocolloid material when said hydrocolloid material absorbs water and swells as it becomes hydrated,

said filaments constituting no less than 3% by weight of said adhesive composition.

2. The dressing of claim 1 in which said hydrocolloid material comprises one or more hydrocolloids selected from the group consisting of carboxymethyl cellulose, carboxymethyl starches, and alkali metal derivatives thereof, alginates, polyvinyl alcohol, carrageenan, gelatine, pectin, gum guar, gum arabic, locust bean gum, and karaya.

3. The dressing of claim 2 in which said hydrocolloid material is present in said composition in the form of particles.

4. The dressing of claim 1 in which said filaments are formed of a polymeric material selected from the group consisting of polyethylene, polypropylene, polyesters, and polyurethane.

5. The dressing of claim 1 in which said filaments constitute no less than approximately 5% by weight of said adhesive composition.

6. The dressing of claim 1 in which each of said filaments has a length of within the range of 5 to 100 mm and a diameter within the range of about 5 to 50 μ

m.

7. The dressing of claim 1 in which said adhesive material is selected from the group consisting of polyisobutylene, silicone rubbers, polyurethane, sucrose acetate isobutylate, acrylonitrile rubber, butyl rubber, natural or synthetic rubber materials optionally in combination with plasticizers, tackifiers or solvents enhancing the adhesive characteristic of said adhesive material.

8. The dressing of claim 1 in which said backing layer comprises a thin film of polymeric material selected from the group consisting of polyurethane, polypropylene, styrene-isoprene copolymers, styrene-butadiene block copolymers, butadiene rubbers, isoprene rubbers, neoprene rubbers, acrylonitrile rubbers, silicone rubbers, butyl rubbers, chloroprene rubbers, polyvinylchloride, polyamides, or mixtures thereof.

9. The dressing of claim 1 in which said adhesive material comprises polyisobutylene in an amount within the range of 30-65% by weight of said adhesive composition.

10. The dressing of claim 1 in which said hydrocolloid material comprises a mixture of gelatine, carboxymethyl cellulose and pectin within the range of about 8-65% by weight of said composition.

11. The dressing of claim 1 in which the polymer of said filaments is polyethylene in an amount within the range of 3-25% by weight of said adhesive composition.

12. An adhesive composition for securing a surgical dressing to a patient'"'"'s skin, said composition comprising:

a three-dimensional, open cell mesh network of discrete polymeric filaments coated with a tacky water-insoluble adhesive material having an adherence affinity for said filaments and joining the coated filaments together at their intersections to maintain the integrity of said network; and

a hydrocolloid material composed of one or more water-absorbing and swellable hydrocolloids, said hydrocolloid material being dispersed throughout the open cells of said network;

said network being expandable for retaining said hydrocolloid material when said hydrocolloid material absorbs water and swells as it becomes hydrated,

said filaments constituting no less than 3% by weight of said adhesive composition.

13. The composition of claim 12 in which said hydrocolloid material comprises one or more hydrocolloids selected from the group consisting of carboxymethyl cellulose, carboxymethyl starches, and alkali metal derivatives thereof, alginates, polyvinyl alcohol, carrageenan, gelatine, pectin, gum guar, gum arabic, locust bean gum, and karaya.

14. The composition of claim 13 in which said hydrocolloid material is present in said composition in the form of particles.

15. The composition of claim 14 in which said filaments are formed of a polymeric material selected from the group consisting of polyethylene, polypropylene, polyesters, and polyurethane.

16. The composition of claim 12 in which said filaments constitute no less than approximately 5% by weight of said adhesive composition.

17. The composition of claim 12 in which each of said filaments has a length of within the range of 5 to 100 mm and a diameter within the range of about 5 to 50 μ

m.

18. The composition of claim 12 in which said adhesive material is selected from the group consisting of polyisobutylene, silicone rubbers, polyurethane, sucrose acetate isobutylate, acrylonitrile rubber, butyl rubber, natural or synthetic rubber materials optionally in combination with plasticizers, tackifiers or solvents enhancing the adhesive characteristic of said adhesive material.

19. The composition of claim 12 in which said adhesive material comprises polyisobutylene in an amount within the range of 30-65% by weight of said adhesive composition.

20. The composition of claim 12 in which said hydrocolloid material comprises a mixture of gelatine, carboxymethyl cellulose and pectin within the range of about 8-65% by weight of said composition.

21. The composition of claim 12 in which the polymer of said filaments is polyethylene in an amount within the range of 3-25% by weight of said adhesive composition.