Process for preparing an absorbent resin crosslinked with a mixture of trimethylolpropane diacrylate and triacrylate

• US 5,574,121 A
• Filed: 06/17/1994
• Issued: 11/12/1996
• Est. Priority Date: 06/18/1993
• Status: Expired due to Term

• Current Assignee: Nippon Shokubai Company Limited
• Original Assignee: Nippon Shokubai Company Limited
• Inventors: Kubo, Hideyuki, Hirota, Kohichi, Masuda, Yoshihiko, Irie, Yoshio, Nagano, Hideaki, Nagasuna, Kinya, Harada, Nobuyuki
• Primary Examiner(s): Zitomer, Fred
• Application Number:
  US08/262,065
• Time in Patent Office: 879 Days
• Field of Search: 525/330.2, 526/318.4, 526/323.2, 526/930, 526/318.43, 526/318.44
• US Class Current: 526/318.44
• CPC Class Codes: A61L 15/24 Macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds; Derivatives thereof A61L15/225 takes precedence
• CPC Class Codes: C08F 220/04 Acids; Metal salts or ammonium salts thereof
• CPC Class Codes: C08L 33/00 Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides or nitriles thereof; Compositions of derivatives of such polymers
• CPC Class Codes: Y10S 526/93 Water swellable or hydrophilic

Abstract

A process for preparing an absorbent resin includes the steps of: preparing a first crosslinking agent (A) including at least two polymerizable unsaturated bonds; preparing a second crosslinking agent (B) including at least two polymerizable unsaturated bonds and hydroxyl groups; preparing a crosslinking agent including (A) and (B) with a ratio of (A) to (B) ranging from 95/5 to 50/50; and polymerizing a hydrophilic unsaturated monomer having at least one carboxyl group using the crosslinking agent. The crosslinking agent includes a crosslinking agent which includes a main component at least 90 percent by weight, the main component being an ester having at least two polymerizable unsaturated bonds, wherein the ester is composed of a polyhydroxy alcohol (C) having not more than six carbon atoms and at least three hydroxy groups, and an unsaturated carboxylic acid (D); and a molecular weight ratio of the main component to a standard compound (E) is in the range of from 0.7/1 to less than 1.3/1, (E) being an ester composed of (C) that composes the main component, and (D) that composes the main component, in which all the hydroxy groups in (C) are ester-linked with (D).

Claims

1. A process for preparing an absorbent resin comprising the steps of:

providing trimethylolpropane and acrylic acid;

producing a crosslinking agent by mixing and esterifying the trimethylolpropane and acrylic acid so that a ratio in weight percent of trimethylolpropane triacrylate and trimethylolpropane diacrylate is from 95/5 to 50/50; and

polymerizing a hydrophilic unsaturated monomer having at least one carboxyl group in the presence of said crosslinking agent, thereby producing a crosslinked polymer.

2. The process according to claim 1, wherein the crosslinking agent includes a high boiling-point compound at a proportion in the range of from 10 weight percent to 20 weight percent, the high boiling-point compound including at least two trimethylolpropane radicals.

3. The process according to claim 1, wherein the hydrophilic unsaturated monomer is a material selected from the group consisting of acrylic acid, methacrylic acid, acrylic acid in a neutralized form and methacrylic acid in a neutralized form.

4. The process according to claim 1, wherein 30 mole percent to 90 mole percent of the carboxyl groups in the hydrophilic unsaturated monomer are neutralized.

5. The process according to claim 1, wherein 50 mole percent to 80 mole percent of the carboxyl groups in the hydrophilic unsaturated monomer are neutralized.

6. The process according to claim 1, wherein 60 mole percent to 75 mole percent of the carboxyl groups in the hydrophilic unsaturated monomer are neutralized.

7. The process according to claim 1, wherein the process for polymerizing the hydrophilic unsaturated monomer is carried out in an aqueous solution of the hydrophilic unsaturated monomer having a concentration ranging from 20 percent by weight to saturation.

8. The process according to claim 1, wherein the process for polymerizing the hydrophilic unsaturated monomer is carried out in an aqueous solution of the hydrophilic unsaturated monomer having a concentration ranging from 25 percent by weight to 40 percent by weight.

9. The process according to claim 1, further comprising the step of heating said crosslinked polymer at a temperature in the range of from 80°

C. to 250°

C.

10. The process according to claim 1, further comprising the step of heating said crosslinked polymer at a temperature in the range of from 150°

C. to 220°

C.

11. The process according to claim 1, wherein the amount of the crosslinking agent is 0.05 to 1 mole percent with respect to said hydrophilic unsaturated monomer.

12. The process of claim 1, wherein said hydrophilic unsaturated monomer is polymerized in the absence of surface active agents and dispersants.

13. A process for preparing an absorbent resin, comprising the steps of:

providing a hydrophilic unsaturated monomer having at least one carboxyl group;

providing a crosslinking agent which includes at least 90 percent by weight of a main component,

the main component being an ester having at least two polymerizable unsaturated bonds, wherein;

the ester is based on;

a polyhydroxy alcohol having not more than six carbon atoms and at least three hydroxy groups; and

an unsaturated carboxylic acid; and

wherein the molecular weight of the main component is expressed as a molecular weight ratio of the main component to a standard compound, said ratio is in the range of from 0.7/1 to less than 1.3/1, wherein

the standard compound is an ester based on;

the polyhydroxy alcohol that composes the main component, and

the unsaturated carboxylic acid that composes the main component, in which all the hydroxy groups in the polyhydroxy alcohol are ester-linked with the unsaturated carboxylic acid, and

polymerizing said hydrophilic unsaturated monomer in the presence of said crosslinking agent, thereby producing a crosslinked polymer.

14. The process according to claim 13, wherein said crosslinking agent further comprises a high boiling-point compound at a concentration of less than 10 percent by weight, the high boiling-point compound including at least two polyhydroxy alcohol radicals per molecular.

15. The process according to claim 13, wherein said crosslinking agent consists of only a compound including one polyhydroxy alcohol radical per molecule.

16. The process according to claim 13, wherein said crosslinking agent contains at least at 95 percent by weight of said main component.

17. The process according to claim 13, wherein said crosslinking agent has a viscosity of from 10 cps to 60 cps at 25°

C.

18. The process according to claim 13, wherein said polyhydroxy alcohol is trimethylolpropane, and said unsaturated carboxylic acid is acrylic acid.

19. The process according to claim 13, wherein said crosslinking agent is used in an amount ranging from 0.01 mole percent to 5 mole percent with respect to said hydrophilic unsaturated monomer.

20. The process according to claim 13, wherein said crosslinking agent is used in an amount ranging from 0.05 mole percent to 1 mole percent with respect to said hydrophilic unsaturated monomer.

21. The process according to claim 13, wherein said hydrophilic unsaturated monomer is a material selected from the group consisting of acrylic acid, methacrylic acid, acrylic acid in a neutralized form and methacrylic acid in a neutralized form.

22. The process according to claim 13, wherein 30 mole percent to 90 mole percent of the carboxyl groups in the hydrophilic unsaturated monomer are neutralized.

23. The process according to claim 13, wherein 50 mole percent to 80 mole percent of the carboxyl groups in the hydrophilic unsaturated monomer are neutralized.

24. The process according to claim 13, wherein 60 mole percent to 75 mole percent of the carboxyl groups in the hydrophilic unsaturated monomer are neutralized.

25. The process according to claim 13, wherein the step of polymerizing the hydrophilic unsaturated monomer is carried out in an aqueous solution in which the hydrophilic unsaturated monomer has a concentration ranging from 20 percent by weight to saturation.

26. The process according to claim 13, wherein the step of polymerizing the hydrophilic unsaturated monomer is carried out in an aqueous solution in which the hydrophilic unsaturated monomer has a concentration ranging from 25 percent by weight to 40 percent by weight.

27. The process according to claim 13, further comprising heating said crosslinked polymer at a temperature in the range of from 80°

C. to 250°

C.

28. The process according to claim 13, further comprising heating said crosslinked polymer at a temperature in the range of from 150°

C. to 220°

C.

29. The process of claim 13, wherein said hydrophilic unsaturated monomer is polymerized in the absence of surface active agents and dispersants.