Ferromagnetic fine powder for magnetic recording

• US 5,585,032 A
• Filed: 05/09/1995
• Issued: 12/17/1996
• Est. Priority Date: 04/21/1987
• Status: Expired due to Fees

• Current Assignee: Ishihara Sangyo Kaisha Limited
• Original Assignee: Ishihara Sangyo Kaisha Limited
• Inventors: Kato, Saburo, Nakata, Kazuo, Takumi, Nobusuke, Hirai, Masaharu
• Primary Examiner(s): KOSLOW, CAROL M
• Application Number:
  US08/437,544
• Time in Patent Office: 588 Days
• Field of Search: 423/593, 252/62.62, 252/62.63, 252/62.59
• US Class Current: 252/62.62
• CPC Class Codes: G11B 5/70678 Ferrites

Abstract

Ferromagnetic fine powder for magnetic recording, characterized by comprising platelet like ferrite crystal particles which have such a metallic element composition that the Ba/Fe molar ratio is 1/50 to 1/8 and that the total amount of Ni and Zn is less than 0.5 mole and not less than 0.07 mole per mole of Fe, a crystal phase of magnetoplumbite phase, spinel phase or composite phase thereof and a saturation magnetization of 60 emu/g or more; and a process for producing said ferromagnetic fine powder for magnetic record.

Claims

1. A ferromagnetic fine powder for magnetic recording of platelet ferrite crystal particles comprising constituents of Fe, Ba, Ni and Zn, having a Ba/Fe molar ratio of 1/50 to 1/12,

wherein a total amount of Ni and Zn is less than 0.5 mole and not less than 0.07 mole per mole of Fe,

said ferrite comprising a crystal phase being magnetoplumbite phase, spinel phase or composite phase thereof and said particles thereof have a saturation magnetization of at least 60 emu/g.

2. A ferromagnetic fine powder for magnetic recording according to claim 1, wherein the Ba/Fe molar ratio is 1/45 to 1/12.

3. A ferromagnetic fine powder for magnetic recording according to claim 1, wherein the molar ratio of the total amount of Ni and Zn to Fe is 0.14 to 0.4.

4. A ferromagnetic fine powder for magnetic recording according to claim 1, wherein the Zn/Fe molar ratio is 0.03 or more.

5. A ferromagnetic fine powder for magnetic recording of platelet ferrite crystal particles comprising constituents of Fe, Ba, Ni and Zn, having a Ba/Fe molar ratio is 1/50 to 1/8,

wherein a total amount of Ni and Zn is less than 0.5 mole and not less than 0.07 mole per mole of Fe, wherein a Zn/Fe molar ratio is 0.03 or more,

said ferrite comprising a crystal phase which is a composite of magnetoplumbite phase and spinel phase and wherein said particles have a saturation magnetization of at least 60 emu/g.

6. A ferromagnetic fine powder for magnetic recording according to claim 5, wherein the Ba/Fe molar ratio is 1/45 to 1/10,

wherein the molar ratio of the total amount of Ni and Zn to Fe is 0.14 to 0.4, and

wherein the Zn/Fe molar ratio is 0.03 or more.

7. A ferromagnetic ferrite fine powder for magnetic recording of platelet ferrite crystal particles comprising constituents of Fe, Ba, Ni and Zn, having a Ba/Fe molar ratio 1/44 to 1/12,

wherein a total amount of Ni and Zn is 0.125 to 0.380 mole per mole of Fe,

wherein a Zn/Fe molar ratio is 0.063 or more to 0.19 and a Ni/Fe molar ratio is 0.062 or more to 0.19,

said ferrite comprising a crystal phase which is a composite of a magnetoplumbite phase and spinel phase and wherein said particles have a saturation magnetization of at least 60 emu/g.

8. A ferromagnetic ferrite fine powder for magnetic recording of platelet ferrite crystal particles comprising constituents of Fe, Ba, Ni and Zn and at least one element selected from Ti and Co, having a Ba/Fe molar ratio of 1/45 to 1/10,

wherein the total amount of Ni and Zn is 0.07 to 0.5 mole per mole of Fe, and the Zn/Fe molar ratio is 0.03 or more;

said ferrite comprising a crystal phase which is a composite of a magnetoplumbite phase and spinel phase and wherein said particles have a saturation magnetization of at least 60 emu/g.

9. A ferromagnetic fine powder for magnetic recording of platelet ferrite crystal particles consisting essentially of constituents of Fe, Ba, Ni and Zn, having a Ba/Fe molar ratio of 1/50 to 1/8, wherein a total amount of Ni and Zn is less than 0.5 mole and not less than 0.07 mol per mole of Fe, said ferrite comprising a crystal phase being magnetoplumbite phase, spinel phase of composite phase thereof and said particles thereof have a saturation magnetization of at least 60 emu/g.