Long life, low air permeable pressurized articles such as play balls

• US 5,593,157 A
• Filed: 05/10/1995
• Issued: 01/14/1997
• Est. Priority Date: 05/10/1995
• Status: Expired due to Term

• Current Assignee: Head Technology GmbH
• Original Assignee: Gencorp Incorporated
• Inventors: Olson, Richard A., Hargis, I. G., Harris, Jason S., Koros, William J.
• Primary Examiner(s): Wong, Steven B.
• Application Number:
  US08/438,674
• Time in Patent Office: 615 Days
• Field of Search: 273/61 R, 273/61 B, 273/61 C, 273/61 D, 273/235 B, 273/218, 273/58 B, 273/58 BA, 273/58 J, 524/908, 156/648
• US Class Current: 473/606
• CPC Class Codes: A63B 2039/022 using special gas-impermeable layers
• CPC Class Codes: A63B 39/02 Arrangements for maintaining the pressure
• CPC Class Codes: Y10S 524/908 Composition having specified shape, e.g. rod, stick, or ball, and other than sheet, film, or fiber

Abstract

Low air permeable, pressurized articles such as play balls, e.g., a tennis ball, have a thin barrier layer formed on the vulcanized rubber core. The barrier layer is chemically bonded to the internal and/or external surface of the core, e.g., by the reaction of a Lewis acid, e.g., sulfur trioxide, with the core rubber. The thin barrier layer permits the tennis ball to be flexible and have good rebound life and yet extends the play life thereof before ball rebound or softness changes to undesired levels.

Claims

1. A tennis ball having improved rebound retention, comprising;

a pressurized hollow vulcanized rubber core having a barrier layer thereon, said barrier layer being the reaction product of a Lewis acid with said rubber core.

2. A tennis ball according to claim 1, wherein said Lewis acid comprises chlorine, fluorine, bromine, chlorosulfuric acid, or sulfur trioxide, combinations thereof, or a mixture of sulfur trioxide and sulfuric acid.

3. A tennis ball according to claim 2, wherein said Lewis acid comprises sulfur trioxide.

4. A tennis ball according to claim 3, wherein said barrier layer is located on the interior surface of said rubber core and wherein said sulfur trioxide is a gas.

5. A tennis ball according to claim 4, wherein said Lewis acid has been neutralized with an alkali metal or an alkaline earth metal, or with an ammonium salt or a quaternary ammonium salt, or combinations thereof, and wherein said core and barrier layer have a air permeability of from about 1.1 to about 5.0 barrers.

6. A tennis ball according to claim 4, wherein the tennis ball has at least a 53 percent rebound after five month'"'"'s exposure to atmospheric pressure.

7. A low air permeable rubber laminate, comprising;

a cured pressurized hollow rubber substrate, and a low air permeable barrier layer, said barrier layer comprising a Lewis acid chemically bonded to said rubber substrate.

8. A low air permeable rubber laminate according to claim 7, wherein said Lewis acid comprises chlorine, fluorine, chlorosulfuric acid, or sulfur trioxide, combinations thereof, or a mixture of sulfur trioxide and sulfuric acid.

9. A low air permeable rubber laminate according to claim 8, wherein said Lewis acid comprises sulfur trioxide gas, and wherein said rubber natural or synthetic cis-1,4-polyisoprene.

10. A low air permeable rubber laminate according to claim 9, wherein said cured rubber substrate is a tennis ball, wherein said barrier layer is located on the inside of said ball, and wherein the air permeability of said ball is from about 1.1 to about 5.0 barrers.

11. In a process for making a low air permeable play ball comprising a hollow cured rubber core containing a gas under pressure;

the improvement comprising applying and reacting a Lewis acid to at least the inside of said core, or to the outside of said core, and forming a low air permeable barrier layer.

12. A process according to claim 11, wherein said Lewis acid is chlorine, fluorine, chlorosulfuric acid, or sulfur trioxide, combinations thereof, or a mixture of sulfur trioxide and sulfuric acid.

13. A process according to claim 12, wherein said Lewis acid comprises sulfur trioxide, and said process further including neutralizing said Applied Lewis acid.

14. A process according to claim 13, wherein said neutralizing agent is an alkali metal or an alkaline earth metal, or an ammonium salt or a quaternary ammonium compound, wherein said core and barrier layer have a air permeability of from about 0.95 to about 7 barrers, and including applying sulfur trioxide to only the inside of said core.

15. A process according to claim 14, including applying sulfur trioxide in the form of a gas.