Flexible rubber article and method of making

• US 5,612,083 A
• Filed: 05/19/1995
• Issued: 03/18/1997
• Est. Priority Date: 06/10/1992
• Status: Expired due to Term

• Current Assignee: Medline Industries Incorporated (Medline Holdings Incorporated)
• Original Assignee: Maxxim Medical, Inc. (UBS Ag)
• Inventors: Muschelewicz, Adana, Chen, Fung-Bor, Haung, Wu-Nan, Manwill, Niles R.
• Primary Examiner(s): Seidleck, James J.
• Assistant Examiner(s): Williamson, Michael A.
• Application Number:
  US08/445,231
• Time in Patent Office: 669 Days
• Field of Search: 427/430.1, 427/2, 427/3, 427/133, 427/299, 427/314, 427/372.2, 427/384, 427/385.5, 427/402, 427/407.1, 427/413, 2/159, 2/167, 2/168, 428/421, 428/423.1, 428/423.9, 428/493
• US Class Current: 264/233
• CPC Class Codes: A61B 42/00 Surgical gloves; Finger-stalls specially adapted for surgery; Devices for handling or treatment thereof
• CPC Class Codes: B29C 41/14 Dipping a core B29C41/10 takes precedence
• CPC Class Codes: B29C 41/22 Making multilayered or multicoloured articles
• CPC Class Codes: B32B 25/04 comprising rubber as the main or only constituent of a layer, which is next to another layer of the same or of a different material next to a layer of a particular substance B32B9/043; next to a bituminous or tarry layer B32B11/044; next to a water setting substance layer B32B13/042; next to a metal layer B32B15/06; next to a glass layer B32B17/063; next to a layer formed of natural mineral fibres or particles B32B19/043; next to a wood layer B32B21/045; next to a cellulosic plastic layer B32B23/046
• CPC Class Codes: Y10T 428/1386 Natural or synthetic rubber or rubber-like compound containing
• CPC Class Codes: Y10T 428/3154 Of fluorinated addition polymer from unsaturated monomers
• CPC Class Codes: Y10T 428/31551 Of polyamidoester [polyurethane, polyisocyanate, polycarbamate, etc.]
• CPC Class Codes: Y10T 428/31569 Next to natural rubber
• CPC Class Codes: Y10T 428/3183 Next to second layer of natural rubber

Abstract

A multi-layer flexible article includes a first layer of natural rubber, a second layer of natural rubber, polyurethane, poly(acrylamide-acrylic acid, sodium salt) and polyethylene oxide and a third layer of acrylic copolymer and fluorocarbon telomer resin. The article is preferably a glove formed by the method of dipping a hand shaped mold into baths containing aqueous emulsions of the components used to form the layers. Gloves manufactured according to the method are substantially wet-hand and dry-hand donnable as compared to powdered latex gloves of similar size. The finished gloved is water washed and wet autoclaved to substantially reduce the protein content from the natural rubber and substantially remove other water extractable allergenic moieties. The washing and autoclaving renders the glove substantially hypoallergenic as compared to gloves not so treated.

Claims

1. A process for making a flexible multilayered article comprising:

forming a first layer from an aqueous emulsion comprising natural rubber latex;

forming a second layer from an aqueous emulsion on said first layer comprising natural rubber latex, polyurethane, poly(acrylamide-acrylic acid, sodium salt) and polyethylene oxide; and

forming a third layer from an aqueous emulsion on said second layer comprising acrylic copolymer and fluorocarbon telomer resin.

2. The process of claim 1 wherein said aqueous emulsion for forming said first layer is a bath having about 25 to 35% total solids content and a pH about 9 to 11 comprising an anionic emulsion of natural rubber latex.

3. The process of claim 1 wherein said aqueous emulsion for forming said second layer is a bath having about 10 to 20% total solids content and a pH about 7 to 10 comprising an anionic emulsion of natural rubber latex, an anionic emulsion of an aliphatic polyester polyurethane, poly(acrylamide/acrylic acid, sodium salt) and polyethylene oxide.

4. The process of claim 1 wherein said aqueous emulsion for forming said third layer is a bath having about 1.5 to 4% total solids content and a pH about 7 to 10 comprising an aqueous emulsion of acrylic copolymer and fluorocarbon telomer resin.

5. The process of claim 1 further including applying a lubricant coating selected from the group consisting of silicone, fluorocarbon telomer, lanolin oil alkoxy ethers and lanolin alkoxy ethers to at least one of a surface of said first layer and a surface of said third layer.

6. The process of claim 1 further including water washing and autoclaving said article.

7. The process of claim 6 wherein said water washing and autoclaving comprises a water wash for about 5 to 10 minutes at about 150°

to 200°

F. and a wet autoclaving cycle for about 10 to 20 minutes with a peak temperature about 180 to 280 degrees Fahrenheit which serves to substantially denature and extract proteins found in natural rubber latex and substantially remove water extractable allergenic moieties, thereby rendering said article substantially hypoallergenic compared to articles not so treated.