Toner for developing electrostatic images and image forming method

• US 5,614,344 A
• Filed: 06/13/1995
• Issued: 03/25/1997
• Est. Priority Date: 06/14/1994
• Status: Expired due to Term

• Current Assignee: Canon Kabushiki Kaisha (Canon Inc.)
• Original Assignee: Canon Kabushiki Kaisha (Canon Inc.)
• Inventors: Kato, Kazunori, Tanikawa, Hirohide, Kawakami, Hiroaki, Doi, Shinji, Fujiwara, Masatsugu
• Primary Examiner(s): MARTIN, ROLAND E
• Application Number:
  US08/489,957
• Time in Patent Office: 651 Days
• Field of Search: 430/102, 430/110
• US Class Current: 430/102
• CPC Class Codes: B82Y 30/00 Nanotechnology for materials or surface science, e.g. nanocomposites
• CPC Class Codes: C01P 2002/74 by peak-intensities or a ratio thereof only
• CPC Class Codes: C01P 2004/03 obtained by SEM
• CPC Class Codes: C01P 2004/61 Micrometer sized, i.e. from 1-100 micrometer
• CPC Class Codes: C01P 2004/62 Submicrometer sized, i.e. from 0.1-1 micrometer
• CPC Class Codes: C01P 2004/64 Nanometer sized, i.e. from 1-100 nanometer
• CPC Class Codes: C01P 2004/82 two phases having the same anion, e.g. both oxidic phases
• CPC Class Codes: C01P 2006/12 Surface area
• CPC Class Codes: C01P 2006/32 Thermal properties
• CPC Class Codes: C01P 2006/40 Electric properties
• CPC Class Codes: C01P 2006/60 Optical properties, e.g. expressed in CIELAB-values
• CPC Class Codes: C01P 2006/80 Compositional purity
• CPC Class Codes: C09C 1/027 Barium sulfates
• CPC Class Codes: G03G 9/09708 Inorganic compounds

Abstract

A toner for developing electrostatic images contains toner particles containing at least a binder resin and a colorant as well as a fine powder comprised of base particles on which crystalline low resistance tin oxide films are formed. The crystalline low resistance tin oxide contains less than 100 ppm of antimony, arsenic and phosphorus, and has an oxygen deficiency structure. The toner is excellent in strength and can consistently give high quality images under any environmental conditions.

Claims

1. A toner for developing an electrostatic image, which comprises:

(a) toner particles containing at least a binder resin and a colorant; and

(b) a fine powder having base particles on the surfaces of which coats of crystalline low electrical resistance tin oxide are formed;

wherein said crystalline low electrical resistance tin oxide contains less than 100 ppm of antimony, arsenic and phosphorus and has an oxygen deficiency structure.

2. The toner according to claim 1, wherein said fine powder comprises base particles formed of fine barium sulfate particles.

3. The toner according to claim 1 or 2, wherein said fine powder has a volume resistivity of 1×

10⁸ Ω

·

cm or lower.

4. The toner according to claim 1, wherein said coats of crystalline low electrical resistance tin oxide are those formed by dispersing fine particles serving as the base particles, in a mineral acid solution of a hydrolyzable tin compound, thereafter raising the pH of the dispersion, and hydrolyzing the tin compound so that the surfaces of the fine particles are coated with tin hydroxide deposited on the fine particle surfaces, followed by calcining the resulting fine particles in an environment having a controlled oxygen concentration.

5. The toner according to claim 1, wherein said base particles have an average particle diameter of 1.5 μ

m or smaller.

6. The toner according to claim 1, wherein said base particles have an average particle diameter of from 0.05 μ

m to 0.9 μ

m.

7. The toner according to claim 1, wherein said fine powder has a volume resistivity of 1×

10⁸ Ω

·

cm or lower.

8. The toner according to claim 1, wherein said fine powder has a volume resistivity of from 1 Ω

·

cm to 1×

Ω

·

cm.

9. The toner according to claim 1, wherein said base particles are coated with the low electrical resistance tin oxide in an amount of from 20/n to 320/n % by weight, where n represents a true specific gravity of the base particles.

10. The toner according to claim 1, wherein said toner particles have a weight average particle diameter of from 2 μ

m to 10 μ

m.

11. The toner according to claim 1, wherein said toner particles have a weight average particle diameter of from 3 μ

m to 9 μ

m.

12. An image forming method comprising;

forming an electrostatic image on an electrostatic image bearing member;

forming a thin layer of a toner on a developer carrying member by means of a coating member pressing the developer carrying member via the toner; and

developing the electrostatic image by transferring the toner on the developer carrying member to the electrostatic image bearing member to form a toner image;

wherein said toner comprises;

(a) toner particles containing at least a binder resin and a colorant; and

(b) a fine powder having base particles on the surfaces of which coats of crystalline low electrical resistance tin oxide are formed;

said crystalline low electrical resistance tin oxide containing less than 100 ppm of antimony, arsenic and phosphorus, and having an oxygen deficiency structure.

13. The method according to claim 12, wherein said fine powder comprises base particles formed of fine barium sulfate particles.

14. The method according to claim 12, wherein said fine powder has a volume resistivity of 1×

10⁸ Ω

·

cm or lower.

15. The method according to claim 12, wherein said coats of crystalline low electrical resistance tin oxide coat are those formed by dispersing fine particles serving as the base particles, in a mineral acid solution of a hydrolyzable tin compound, thereafter raising the pH of the dispersion, and hydrolyzing the tin compound so that the surfaces of the fine particles are coated with tin hydroxide deposited on the fine particle surfaces, followed by calcining the resulting fine particles in an environment having a controlled oxygen concentration.

16. The method according to claim 12, wherein said base particles have an average particle diameter of 1.5 μ

m or smaller.

17. The method according to claim 12, wherein said base particles have an average particle diameter of from 0.05 μ

m to 0.9 μ

m.

18. The method according to claim 12, wherein said fine powder has a volume resistivity of 1×

10⁸ Ω

·

cm or lower.

19. The method according to claim 12, wherein said fine powder has a volume resistivity of from 1 Ω

·

cm to 1×

10⁶ Ω

·

cm.

20. The method according to claim 12, wherein said base particles are coated with the low electrical resistance tin oxide in an amount of from 20/n to 320/n % by weight, where n represents a true specific gravity of the base particles.

21. The method according to claim 12, wherein said toner particles have a weight average particle diameter of from 2 μ

m to 10 μ

m.

22. The method according to claim 12, wherein said toner particles have a weight average particle diameter of from 3 μ

m to 9 μ

m.

23. The method according to claim 12, wherein said coating member is an elastic blade.

24. The method according to claim 12, wherein said coating member is an elastic roller.