N-alkoxymethyl (meth)acrylamide functional polymers and their use in self-crosslinkable coating compositions

• US 5,618,586 A
• Filed: 03/16/1995
• Issued: 04/08/1997
• Est. Priority Date: 03/29/1994
• Status: Expired due to Fees

• Current Assignee: PPG Industries Incorporated (Nouryon BV)
• Original Assignee: PPG Industries Incorporated (Nouryon BV)
• Inventors: Swarup, Shanti, Mayo, Michael A.
• Primary Examiner(s): DUDASH, DIANA L
• Application Number:
  US08/405,470
• Time in Patent Office: 754 Days
• Field of Search: 427/409, 427/407.1, 427/388.4
• US Class Current: 427/407.1
• CPC Class Codes: B05D 7/534 the first layer being let to dry at least partially before applying the second layer B05D7/538 takes precedence
• CPC Class Codes: C08L 2666/04 Macromolecular compounds according to groups C08L7/00 - C08L49/00, or C08L55/00 - C08L57/00; Derivatives thereof
• CPC Class Codes: C09D 133/18 Homopolymers or copolymers of nitriles
• CPC Class Codes: C09D 163/00 Coating compositions based on epoxy resins; Coating compositions based on derivatives of epoxy resins

Abstract

Self-crosslinkable film-forming compositions and a process for preparing multi-layered coated articles coated with a pigmented or colored base coat and a transparent or clear topcoat containing a self-crosslinkable film-forming composition are disclosed. The self-crosslinkable film-forming composition comprises a non-gelled addition polymer which is the free radical initiated reaction product of an N-alkoxymethyl(meth)acrylamide and at least one other ethylenically unsaturated monomer. The topcoat composition may be aqueous based. The transparent topcoat provides a composite coating with improved acid etch resistance and mar resistance, making the composite coating particularly useful as a topcoat for automotive parts.

Claims

1. A method for applying a composite coating to a substrate which comprises applying to the substrate a colored film-forming composition to form a base coat and applying to said base coat a clear film-forming composition to form a transparent top coat over the base coat characterized in that the clear film-forming composition is self-crosslinkable and comprises as the main resinous component a non-gelled addition polymer which is the free radical initiated reaction product of the following polymerizable ethylenically unsaturated monomers:

a) about 40 to 80% by weight of an N-alkoxymethyl(meth)acrylamide;

b) about 20 to 60% total by weight of at least one polymerizable ethylenically unsaturated monomer selected from the group consisting of styrene, methyl (meth)acrylate, butyl (meth)acrylate, cyclohexyl (meth)acrylate, and mixtures thereof;

c) up to 10% by weight, based on total weight of the polymerizable ethylenically unsaturated monomers used in preparing the polymer, of a hydroxyl functional ethylenically unsaturated monomer selected from the group consisting of hydroxypropyl (meth)acrylate, hydroxyethyl (meth)acrylate, and hydroxybutyl (meth)acrylate, and

d) up to 5% by weight, of an acid functional ethylenically unsaturated monomer, and

where the percentage by weight is based on total weight of the polymerizable ethylenically unsaturated monomers used in preparing the polymer.

2. The method of claim 1, wherein the N-alkoxymethyl(meth)acrylamide is N-butoxymethyl(meth)acrylamide.

3. The method of claim 1, wherein the N-alkoxymethyl(meth)acrylamide is present at about 40 to 50% by weight.

4. The method of claim 1, wherein the weight average molecular weight of the polymer is about 1800 to 80,000.

5. The method of claim 4, wherein the weight average molecular weight of the polymer is about 2000 to 8500.

6. The method of claim 5, wherein the weight average molecular weight of the polymer is less than about 3000 and the polymer is synthesized in high boiling solvents that reflux of around 110°

to 160°

C. at a solids content of about 30 to 40 weight percent by weight.

7. The method of claim 1, wherein the clear film-forming composition further comprises about 0.5 to 1.5% by weight, based on total weight of resin solids, of an acid functional catalyst selected from the group consisting of phenyl acid phosphate, sulfonic acid, or a substituted sulfonic acid such as paratoluene sulfonic acid and dodecyl benzene sulfonic acid.

8. The method of claim 3, wherein the clear film-forming composition is aqueous based.

9. The method of claim 8, wherein the N-alkoxymethyl(meth)acrylamide is N-butoxymethyl(meth)acrylamide.

10. The method of claim 8, wherein the weight average molecular weight of the polymer is about 25,000 to 70,000.

11. The method of claim 8, wherein the clear film-forming composition further comprises about 0.5 to 1.5% by weight, based on total weight of resin solids, of an acid functional catalyst.

12. The method of claim 1, wherein the polymer further includes up to 15% by weight, based on total weight of the polymerizable ethylenically unsaturated monomers used in preparing the polymer, of an epoxy functional ethylenically unsaturated monomer.