Process for the production of stainless steel sheets having an excellent corrosion resistance

• US 5,626,694 A
• Filed: 09/22/1995
• Issued: 05/06/1997
• Est. Priority Date: 01/26/1994
• Status: Expired due to Term

• Current Assignee: Kawasaki Steel Corporation (JFE Holdings Incorporated)
• Original Assignee: Kawasaki Steel Corporation (JFE Holdings Incorporated)
• Inventors: Fukuda, Kunio, Kawabata, Yoshikazu, Satoh, Susumu, Fujisawa, Mitsuyuki
• Primary Examiner(s): Yee, Deborah
• Application Number:
  US08/522,383
• Time in Patent Office: 592 Days
• Field of Search: 148/609, 148/610, 148/654, 148/661
• US Class Current: 148/609
• CPC Class Codes: C21D 6/002 containing Cr C21D6/004 takes precedence
• CPC Class Codes: C21D 8/0205 of ferrous alloys

Abstract

This invention relates to a process for the production of stainless steel sheets and proposes a process for the production of stainless steel sheets having a more excellent corrosion resistance as compared with the conventional one without trimming the steel sheet surface after annealing-pickling by preventing the chapping of steel sheet surface created in the production of present stainless steel sheet, particularly stainless steel sheets having extreme-low amounts of C, S, O.

For this purpose, according to the invention, a starting material of stainless steel containing C: not more than 0.01 wt %, S: not more than 0.005 wt % and O: not more than 0.005 wt % is subjected to a hot rolling at a draft below 830° C. of not less than 30%, cooled at a cooling rate of not less than 25° C. sec, coiled below 650° C. and then annealed and pickled.

Claims

1. A process for the production of stainless steel sheets having an excellent corrosion resistance, wherein said stainless steel sheet contains C:

not more than 0.01 wt %, S;

not more than 0.005 wt % and O;

not more than 0.005 wt % said stainless steel being produced by the steps of;

hot rolling said stainless steel sheet at a draft below 830°

C. of greater than about 30%,

cooling the resulting hot rolled sheet at a cooling rate of greater than about 25°

C./sec,

coiling said stainless steel sheet at a temperature of less than about 650°

C., and thereafter subjecting said stainless steel sheet to annealing and pickling.

2. The process for the production of stainless steel sheets of claim 1, further comprising the step of skin pass rolling said stainless steel sheet at a draft of less than about 20%.

3. The process for the production of stainless steel sheets of claim 1, wherein said stainless steel sheet is further subjected to a cold rolling at a total draft of more than about 20% with work rolls having a roll diameter of greater than about 250 mm.

4. A process according to anyone of claims 1 to 3, wherein said stainless steel sheet is a ferritic stainless steel comprising C:

not more than 0.01 wt %, S;

not more than 0.005 wt %, O;

not more than 0.005 wt %, Si;

not more than 3 wt %, Mn;

not more than 5 wt %, Cr;

9-50 wt %, Ni;

less than 5 wt %, and the remainder being Fe and inevitable impurities.

5. A process according to anyone of claims 1 to 3, wherein said stainless steel sheet is a ferritic stainless steel comprising C:

not more than 0.01 wt %, S;

not more than 0.005 wt %, O;

not more than 0.005 wt %, Si;

not more than 3 wt %, Mn;

not more than 5 wt %, Cr;

9-50 wt %, Ni;

less than 5 wt %, and further containing one or more elements selected from the group consisting of Ti;

0.01-1.0 wt %, Nb;

0.01-1.0 wt %, V;

0.01-1.0 wt %, Zr;

0.01-1.0 wt %, Ta;

0.01-1.0 wt %, Co;

0.1-5 wt %, Cu;

0.1-5 wt %, Mo;

0.1-5 wt %, W;

0.1-5 wt %, Al;

0.005-5.0 wt %, Ca;

0.0003-0.01 wt % and B;

0.0003-not more than 0.01 wt %, and the remainder being Fe and inevitable impurities.

6. A process according to anyone of claims 1 to 3, wherein said stainless steel sheet is selected from the group consisting of an austenitic stainless steel and a dual-phase stainless steel comprising C:

not more than 0.01 wt %, S;

not more than 0.005 wt %, O;

not more than 0.005 wt %, Si;

not more than 3 wt %, Mn;

not more than 20 wt %, Cr;

9-50 wt %, Ni;

5-20 wt %, N;

not more than 0.2 wt %, and the remainder being Fe and inevitable impurities.

7. A process according to anyone of claims 1 to 3, wherein said stainless steel sheet is selected from the group consisting of an austenitic stainless steel and a dual-phase stainless steel comprising C:

not more than 0.01 wt %, S;

not more than 0.005 wt %, O;

not more than 0.005 wt %, Si;

not more than 3 wt %, Mn;

not more than 20 wt %, Cr;

9-50 wt %, Ni;

5-20 wt %, N;

not more than 0.2 wt %, and further containing one or more elements selected from the group consisting of Ti;

0.01-1.0 wt %, Nb;

0.01-1.0 wt %, V;

0.01-1.0 wt %, Zr;

0.01-1.0 wt %, Ta;

0.01-1.0 wt %, Co;

0.1-5 wt %, Cu;

0.1-5 wt %, Mo;

0.1-5 wt %, W;

0.1-5 wt %, Al;

0.005-5.0 wt %, Ca;

0.0003-0.01 wt % and B;

0.0003-not more than 0.01 wt %, and the remainder being Fe and inevitable impurities.