High strength member for intracorporeal use

• US 5,636,641 A
• Filed: 07/25/1994
• Issued: 06/10/1997
• Est. Priority Date: 07/25/1994
• Status: Expired due to Term

• Current Assignee: Advanced Cardiovascular Systems Incorporated
• Original Assignee: Advanced Cardiovascular Systems Incorporated
• Inventors: Fariabi, Sepehr
• Primary Examiner(s): RIMELL, SAMUEL G
• Application Number:
  US08/280,209
• Time in Patent Office: 1,051 Days
• Field of Search: 128/657, 128/772, 604/95, 604/280, 604/281, 604/282, 604/283, 600/37, 623/1
• US Class Current: 600/585
• CPC Class Codes: A61F 2/958 Inflatable balloons for placing stents or stent-grafts
• CPC Class Codes: A61F 2210/0019 operated at only one temperature whilst inside or touching the human body, e.g. constrained in a non-operative shape during surgery, another temperature only occurring before the operation
• CPC Class Codes: A61M 2025/09083 having a coil around a core
• CPC Class Codes: A61M 25/0009 Making of catheters or other medical or surgical tubes
• CPC Class Codes: A61M 25/0012 with embedded structures, e.g. coils, braids, meshes, strands or radiopaque coils
• CPC Class Codes: A61M 25/09 Guide wires

Abstract

This invention is directed to an intracorporeal device formed of a high strength Co--Ni--Cr alloy and is particularly suitable for forming a composite product with a pseudoelastic member formed of NiTi alloy. Suitable intracorporeal products include guidewires and stents. The high strength alloy consists essentially of about 28 to about 65% cobalt, about 2 to about 40% nickel, about 5 to about 35% chromium, up to about 12% molybdenum, up to about 20% tungsten, up to about 20% iron and the balance inconsequential amounts of impurities and other alloying constituents, with a preferred alloy composition including about 30 to about 45% cobalt, about 25 to about 37% nickel, about 15 to about 25% chromium and about 5 to about 15% molybdenum. Intravascular devices such as guidewires, stents and the like can be formed of this high strength Co--Ni--Cr alloy.

Claims

1. An elongated member configured for advancement within a body lumen which is formed at least in part of a cold worked biocompatible alloy consisting essentially of 28 to 65% by wt. cobalt, 2 to 40% by wt. nickel, 5 to 35% by wt. chromium, up to 12% by wt. molybdenum, up to 20% by wt. tungsten and up to 20% by wt. iron.

2. The elongated member of claim 1 wherein the cold worked biocompatible alloy includes 30 to 45% by wt. cobalt, 25 to 37% by wt. nickel, and 25% by wt. chromium and 5 to 15% by wt. molybdenum.

3. The elongated member of claim 2 wherein the cold worked biocompatible alloy has been age hardened.

4. The elongated member of claim 1 in the form of a guidewire.

5. The elongated member of claim 1 wherein a distal portion thereof is formed of a pseudoelastic NiTi alloy.

6. A composite product comprising:

a) a first portion formed of a high strength alloy containing 28 to 65% by wt. cobalt, 2 to 40% by wt. nickel and 5 to 35% by wt. chromium; and

b) a second portion formed of an alloy of nickel and titanium.

7. The composite product of claim 6 wherein the second portion exhibits a stress induced transformation from an austenite phase which is stable at body temperature to a martensite phase.

8. The composite product of claim 6 having an elongated shape with the second portion being an elongated inner member and the first portion being an outer sheath disposed about the inner member.

9. The composite product of claim 8 wherein the composite product has proximal and distal sections and has at least a portion of the outer sheath removed from the inner member in at least part of the distal section.

10. The composite product of claim 9 wherein the inner member in the distal section tapers in the distal direction to a smaller transverse dimension.

11. A co-worked high strength elongated composite intracorporeal device comprising:

a) a first member formed of a pseudoelastic NiTi alloy which has;

desirable mechanical properties due to having been subjected to certain thermomechanical processing; and

b) a second member secured to the first member formed of a high strength alloy which contains 28 to 65% by wt. cobalt, 2 to 40% by wt. nickel and 5 to 35% by wt. chromium and which has been subjected to the same thermomechanical processing to which the first member has been subjected.

12. The intracorporeal device of claim 11 wherein the thermomechanical processing includes a plurality of cold working stages with intermediate anneals and a final cold working stage followed by an age hardening heat treatment.

13. An elongated guidewire for intracorporeal use comprising:

a) a core member having

an inner portion formed of a pseudoelastic NiTi alloy; and

an outer portion formed of a high strength alloy which contains 28 to 65% by wt. cobalt, 2 to 40% by wt. nickel and 5 to 35% by wt. chromium; and

b) a helical coil disposed about a distal portion of the core member.

14. The elongated guidewire of claim 13 having proximal and distal sections with a length of the outer portion removed to expose the underlying inner portion in the distal section of the guidewire.

15. The elongated guidewire of claim 14 wherein the helical coil is disposed about the exposed portion of the core member.

16. The elongated guidewire of claim 15 wherein the helical coil is secured by its proximal portion to the outer portion of the core member.

17. The elongated guidewire of claim 16 wherein a shapeable ribbon having proximal and distal ends is secured by its distal end to the distal end of the coil and by its proximal end to the core member.

18. The elongated guidewire of claim 16 wherein the helical coil is secured by its distal end to the core member.

19. The elongated guidewire of claim 13 wherein the Co--Ni--Cr alloy consists essentially of 28 to 65% by wt. cobalt, 2 to 40% by wt. nickel, and 5% to 35% by wt. chromium and up to 12% by wt. molybdenum, up to 20% by wt. tungsten, up to 20% by wt. iron and the balance inconsequential amounts of other alloying constituents and impurities.

20. The elongated guidewire of claim 19 wherein the Co--Ni--Cr alloy includes 30 to 45% by wt. cobalt, 25 to 37% by wt. nickel, 15 to 25% by wt. chromium and about 5 to about 15% by wt. molybdenum.

21. The elongated guidewire of claim 13 wherein the Ni--Ti alloy consists essentially of 25 to 47% by wt. titanium and the balance nickel and up to about 10% by wt. of one or more additional alloying elements.

22. The elongated guidewire of claim 21 wherein the additional alloying elements are selected from the group consisting of up to 3% by wt. of iron, cobalt, chromium, platinum and palladium and up to about 10% by wt. copper and vanadium.

23. A method of making an elongated composite product comprising:

a) providing an elongated outer sheath formed of a Co--Ni--Cr alloy with an inner lumen extending therein;

b) advancing an elongated core member formed of NiTi alloy into the inner lumen of the outer sheath to form an assembly therewith; and

c) cold working the assembly in a plurality of cold working stages and intermediate annealing the cold worked assembly between cold working stages.

24. The method of claim 23 wherein the outer sheath is formed of an alloy containing up to 10% molybdenum.

25. The method of claim 23 wherein the assembly is cold worked by drawing with a reduction of at least about 20% in each cold working stage.

26. The method of claim 23 wherein the cold worked assembly is intermediate annealed at a temperature of about 600°

and 900°

C.

27. The method of claim 25 wherein the final cold working stage includes a reduction of at least 50%.

28. The method of claim 24 wherein the cold worked assembly is heat treated after the final cold working stage at a temperature between about 400°

and about 700°

C. to age harden the outer sheath formed of Co--Ni--Cr--Mo alloy and provide pseudoelastic characteristics to the inner member.

29. The method of claim 24 wherein the cold worked assembly is heat treated at a temperature between about 550°

and about 675°

C. to age harden the outer sheath formed of Co--Ni--Cr--Mo alloy and provide pseudoelastic characteristics to the inner member.