Water-based paint including glass particulate

• US 5,698,026 A
• Filed: 12/20/1996
• Issued: 12/16/1997
• Est. Priority Date: 12/20/1996
• Status: Expired due to Fees

• Current Assignee: Automotive Components Holdings LLC (Ford Motor Company)
• Original Assignee: Ford Motor Company
• Inventors: Boaz, Premakaran Tucker
• Primary Examiner(s): MARCHESCHI, MICHAEL A
• Application Number:
  US08/771,629
• Time in Patent Office: 361 Days
• Field of Search: 106/38.3, 106/600, 106/635, 106/425, 106/431, 106/38.9, 106/636, 428/357, 428/426, 428/428, 428/432
• US Class Current: 106/600
• CPC Class Codes: C03C 17/008 comprising a mixture of materials covered by two or more of the groups C03C17/02, C03C17/06, C03C17/22 and C03C17/28
• CPC Class Codes: C03C 17/04 by fritting glass powder
• CPC Class Codes: C03C 8/14 Glass frit mixtures having non-frit additions, e.g. opacifiers, colorants, mill-additions
• CPC Class Codes: C09D 1/02 alkali metal silicates
• CPC Class Codes: Y10T 428/29 Coated or structually defined flake, particle, cell, strand, strand portion, rod, filament, macroscopic fiber or mass thereof

Abstract

The invention is directed to a water-based paint composition comprising sodium silicate, water, water-soluble base, metal oxide pigment, soda-lime-silica glass particles and at least one of a low-melting glass frit or zinc oxide. Preferably, it includes only the glass frit and it further preferably comprises surfactants and aluminum hydroxide.

Claims

1. A water-based paint composition, which has excellent adhesion to glass, comprising:

(i) water-soluble sodium silicate forming 20 to 45 weight percent of said composition,

(ii) water forming 5 to 25 weight percent of said composition;

(iii) water-soluble base in an amount sufficient to provide said composition with a pH of at least 10.5;

(iv) finely divided metal oxide powder selected from the group consisting of oxides of copper, iron, nickel, cobalt and mixtures thereof forming 20 to 45 weight percent of said composition and having a particle size, on average, less than 7 microns;

(v) particles of soda-lime-silica glass forming 10 to 55 weight percent of the composition and having a diameter, on average, less than 20 microns and having a melting point of at least about 1700°

F.; and

at least one material selected from the group consisting of;

(vi) low-melting glass frit powder melting below 1300°

F. forming up to 10 weight percent of said composition and having a particle size, on average, less than 10 microns; and

(vii) zinc oxide forming up to 10 weight percent of said composition.

2. The water-based paint composition according to claim 1 wherein said soda-lime-silica particles are composed of, by weight percent, silicon dioxide 68-75;

aluminum oxide 0-5;

calcium oxide 5-15;

magnesium oxide 0-10;

sodium oxide 10-18; and

potassium oxide 0-5, wherein the calcium oxide+magnesium oxide is 6-15% and sodium oxide+potassium oxide is 10-20% by weight.

3. The water-based paint composition according to claim 1 wherein said composition further comprises potassium silicate.

4. The water-based paint composition according to claim 1 wherein said low-melting glass frit powder forms 2 to 10 weight percent of said composition.

5. The water-based paint composition according to claim 1 wherein said composition further comprises 0.1 to 1.0 weight percent of a surfactant.

6. The water-based paint composition according to claim 1 which further comprises up to about 5 weight percent of aluminum hydroxide.

7. The water-based paint composition according to claim 1 wherein said low-melting glass frit is a metal silicate wherein said metal is selected from the group consisting of zinc, boron, bismuth, titanium, zirconium, and aluminum and mixtures thereof.

8. A water-based paint composition, which has excellent adhesion to glass, comprising:

(i) water-soluble sodium silicate forming 25 to 36 weight percent of said composition,

(ii) water forming 10 to 25 weight percent of said composition;

(iii) water-soluble base in an amount sufficient to provide said composition with a pH of at least 10.5;

(iv) finely divided copper oxide powder forming 25 to 45 weight percent of said composition and having a particle size, on average, between 3 and 7 microns;

(v) particles of soda-lime-silica glass forming 10 to 55 weight percent of the composition and having a diameter, on average, in the range of 3 to 10 microns and having a melting point of at least about 1700°

F. and being composed of, by weight percent, silicon dioxide 68-75;

aluminum oxide 0-5;

calcium oxide 5-15;

magnesium oxide 0-10;

sodium oxide 10-18; and

potassium oxide 0-5, wherein the calcium oxide+magnesium oxide is 6-15% and sodium oxide+potassium oxide is 10-20% by weight.;

(vi) glass frit powder, having a melting point below 1300°

F., forming 3 to 8 weight percent of said composition and having a particle diameter, on average, between about 3 and 7 microns and wherein said glass frit is a metal silicate with said metal being selected from the group consisting of zinc, boron, bismuth, titanium zirconium, and aluminum and mixtures thereof; and

(vi) surfactant forming 0.1 to 1.0 weight percent of said composition.

9. The paint composition according to claim 8 wherein said composition further comprises aluminum hydroxide.