Aqueous two-component polyurethane coating compositions and a method for their preparation

• US 5,723,518 A
• Filed: 01/06/1997
• Issued: 03/03/1998
• Est. Priority Date: 06/03/1994
• Status: Expired due to Term

• Current Assignee: Covestro LLC (Covestro AG)
• Original Assignee: Bayer AG
• Inventors: Bock, Manfred, Klinksiek, Bernd, Yuva, Nusret, Schleenstein, Dieter, Kahl, Lothar
• Primary Examiner(s): SERGENT, RABON A
• Application Number:
  US08/779,103
• Time in Patent Office: 421 Days
• Field of Search: 523/324, 524/591, 524/839, 524/840, 427/421, 528/71, 528/502 C, 528/502 E, 528/502 F
• US Class Current: 523/324
• CPC Class Codes: B01F 2101/30 Mixing paints or paint ingredients, e.g. pigments, dyes, colours, lacquers or enamel
• CPC Class Codes: B01F 2215/0431 Numerical size values, e.g. diameter of a hole or conduit, area, volume, length, width, or ratios thereof
• CPC Class Codes: B01F 2215/0468 Numerical pressure values
• CPC Class Codes: B01F 23/4105 Methods of emulsifying
• CPC Class Codes: B01F 25/3131 with additional mixing means other than injector mixers, e.g. screens, baffles or rotating elements
• CPC Class Codes: B01F 25/45 Mixers in which the materials to be mixed are pressed together through orifices or interstitial spaces, e.g. between beads B01F25/44 takes precedence
• CPC Class Codes: B01F 25/45211 the elements being cylinders or cones which obstruct the whole diameter of the tube, the flow changing from axial in radial and again in axial
• CPC Class Codes: B01F 25/45212 the elements comprising means for adjusting the orifices
• CPC Class Codes: C08G 18/0866 the dispersing or dispersed phase being an aqueous medium
• CPC Class Codes: Y10T 428/2982 Particulate matter [e.g., sphere, flake, etc.]

Abstract

A method is described for the preparation of aqueous coating compositions based on resin binders containing isocyanate-reactive hydrogen atoms and polyisocyanates, by mixing the components with water, wherein the mixture is forced at a pressure of from 1 to 30 MPa through a nozzle of small size in at least one dimension.

Claims

1. A bimodal aqueous coating composition containing in dispersed form as binder an isocyanate-reactive component and a polyisocyanate component, in which these components have a particle size distribution having a first distribution maximum at a particle size of 40 to 200 nm and a second distribution maximum at a particle size of 200 to 2,000 nm, provided that the particle sizes of the distribution maxima differ by a factor of at least 2.

2. The coating composition of claim 1, wherein 99% by weight of the dispersed components have a particle size of less than 5000 nm.

3. A process for the preparation of an aqueous coating composition containing an isocyanate-reactive component and a polyisocyanate component by mixing the components with water and forcing the mixture at a pressure of 1 to 30 MPa through one or more nozzles having an opening of about 0.2 to 1 mm in at least one dimension.

4. The process of claim 3 wherein the nozzle size in the direction of flow is one to three times the size of said opening.

5. The process of claim 3 wherein the pressure is 1 to 8 MPa.

6. The process of claim 3 wherein the pressure is 2 to 6 MPa.

7. The process of claim 3 which comprises forcing the mixture at a pressure of 1 to 30 MPa through up to three nozzles in succession, each nozzle having an opening of about 0.2 to 1 mm in at least one dimension.

8. The process of claim 7 wherein the nozzle size in the direction of flow is one to three times the size of said opening.

9. The process of claim 7 wherein the pressure is 1 to 8 MPa.

10. The process of claim 7 wherein the pressure is 2 to 6 MPa.

11. The process of claim 3 which comprises forcing the mixture at a pressure of 1 to 30 MPa through two nozzles arranged such that their openings are arranged opposite to each other, each nozzle having an opening of about 0.2 to 1 mm in at least one dimension.

12. The process of claim 11 wherein the nozzle size in the direction of flow is one to three times the size of said opening.

13. The process of claim 11 wherein the pressure is 1 to 8 MPa.

14. The process of claim 11 wherein the pressure is 2 to 6 MPa.