Method for increasing hydrophilicity of contact lenses

• US 5,726,733 A
• Filed: 06/11/1996
• Issued: 03/10/1998
• Est. Priority Date: 12/21/1993
• Status: Expired due to Term

• Current Assignee: Bausch & Lomb Incorporated (Bausch Health Cos., Inc.)
• Original Assignee: Bausch & Lomb Incorporated (Bausch Health Cos., Inc.)
• Inventors: Lai, Yu-Chin, Valint, Paul L. Jr.
• Primary Examiner(s): DUDASH, DIANA L
• Application Number:
  US08/661,803
• Time in Patent Office: 637 Days
• Field of Search: 427/2.1, 427/558, 427/557, 427/164, 427/493, 623/4, 623/5, 623/6, 351/160 R, 351/160 H, 523/107, 523/108
• US Class Current: 351/160.00R
• CPC Class Codes: G02B 1/043 Contact lenses

Abstract

A method for increasing hydrophilicity of a contact lens, so as to improve surface wettability of the lens, comprises contacting a surface of the contact lens with an aqueous solution including a hydrophilic monomer, and heating the solution while in contact with the surface of the contact lens to effect polymerization.

Claims

1. A method for increasing hydrophilicity of a contact lens consisting essentially of:

contacting a surface of the contact lens with an aqueous solution including a hydrophilic monomer and a thermal polymerization initiator; and

heating the solution while in contact with the surface of the contact lens to effect polymerization of said hydrophilic monomer.

2. The method of claim 1, wherein the hydrophilic monomer is selected from the group consisting of ethylenically unsaturated carboxylic acids, (meth)acrylic substituted alcohols or glycols, vinyl lactams, and acrylamides.

3. The method of claim 1, wherein the hydrophilic monomer is N-vinylpyrrolidone.

4. The method of claim 1, wherein the aqueous solution includes buffered saline.

5. The method of claim 1, further comprising exposing the solution to ultraviolet light while in contact with the surface of the contact lens.

6. The method of claim 1, wherein the solution further comprises a crosslinking monomer.

7. The method of claim 6, wherein the crosslinking monomer is methacryloxyethyl vinylcarbonate.

8. The method of claim 1, wherein the contact lens is formed of a silicone-containing material.

9. The method of claim 8, wherein the contact lens is formed of a rigid, gas permeable material.

10. The method of claim 8, wherein the contact lens is formed of a silicone hydrogel material.

11. A contact lens treated by the method of claim 1.