Composite metal membrane

• US 5,738,708 A
• Filed: 06/07/1995
• Issued: 04/14/1998
• Est. Priority Date: 06/07/1995
• Status: Expired due to Fees

• Current Assignee: Los Alamos National Security LLC (Government of the United States of America)
• Original Assignee: Regents of the University of California (University of California)
• Inventors: Peachey, Nathaniel M., Birdsell, Stephan A., Dye, Robert C., Snow, Ronny C.
• Primary Examiner(s): SPITZER, ROBERT H
• Application Number:
  US08/484,801
• Time in Patent Office: 1,042 Days
• Field of Search: 95/55, 95/56, 96/4, 96/11, 427/250, 427/405, 427/532-534, 427/566, 427/597, 428/548, 428/606, 428/607, 428/615, 428/662, 428/663, 428/670, 428/938
• US Class Current: 95/56
• CPC Class Codes: B01D 2323/10 Specific pressure applied
• CPC Class Codes: B01D 53/228 characterised by specific membranes
• CPC Class Codes: B01D 69/1216 Three or more layers
• CPC Class Codes: B01D 71/0221 Group 4 or 5 metals
• CPC Class Codes: B01D 71/02231 Palladium
• CPC Class Codes: C01B 2203/0405 Purification by membrane separation
• CPC Class Codes: C01B 3/503 characterised by the membrane
• CPC Class Codes: C01B 3/505 Membranes containing palladium
• CPC Class Codes: Y10S 428/938 Vapor deposition or gas diffusion
• CPC Class Codes: Y10T 428/12028 Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, etc.]
• CPC Class Codes: Y10T 428/12819 Group VB metal-base component
• CPC Class Codes: Y10T 428/12826 Group VIB metal-base component

Abstract

A composite metal membrane including a first metal layer of Group IVB met or Group VB metals, the first metal layer sandwiched between two layers of an oriented metal of palladium, platinum or alloys thereof is provided together with a process for the recovery of hydrogen from a gaseous mixture including contacting a hydrogen-containing gaseous mixture with a first side of a nonporous composite metal membrane including a first metal of Group IVB metals or Group VB metals, the first metal layer sandwiched between two layers of an oriented metal of palladium, platinum or alloys thereof, and, separating hydrogen from a second side of the nonporous composite metal membrane.

Claims

1. A process for the recovery of hydrogen from a gaseous mixture comprising:

contacting a hydrogen-containing gaseous mixture with a first side of a nonporous composite metal membrane including a first metal layer selected from the group consisting of Group IVB metals and Group VB metals, said first metal layer sandwiched between two layers of an oriented metal selected from the group consisting of palladium, platinum and alloys thereof; and

,

separating hydrogen from a second side of said nonporous composite metal membrane.

2. The process of claim 1 wherein said contacting of said hydrogen-containing gaseous mixture with said composite metal membrane is at a pressure on a feed side of said membrane that is elevated relative to the pressure on a permeate side of said membrane.

3. The process of claim 1 wherein said two layers of oriented metal are continuous.

4. The process of claim 3 wherein said two layers of oriented metal have an orientation characterized as (111).

5. The process of claim 3 wherein said two layers of metal are from about 0.1 microns to about 25 microns in thickness.

6. The process of claim 5 wherein said metal layer selected from the group consisting of Group IVB metals and Group VB metals is from about 10 microns to about 250 microns in thickness.

7. The process of claim 1 wherein said layer of Group IVB or Group VB metal is oriented.

8. A composite metal membrane comprising a first metal layer selected from the group consisting of Group IVB metals and Group VB metals, said first metal layer sandwiched between two layers of an oriented metal selected from the group consisting of palladium, platinum and alloys thereof.

9. The membrane of claim 8 wherein said two layers of oriented metal selected from the group consisting of palladium, platinum and alloys thereof are continuous, nonporous layers from about 0.1 microns to about 25 microns in thickness.

10. The membrane of claim 9 wherein said two layers of oriented metal have an orientation characterized as (111).

11. The membrane of claim 9 wherein said metal layer selected from the group consisting of Group IVB metals and Group VB metals is from about 10 microns to about 250 microns in thickness.

12. The membrane of claim 8 wherein said layer of Group IVB or Group VB metal is oriented.

13. A process of forming a composite metal membrane comprising

ion milling an oriented metal film selected from the group consisting of Group IVB metals and Group VB metals to remove surface oxides and surface imperfections from the oriented metal film;

and,

depositing layers of an oriented metal selected from the group consisting of palladium, platinum and alloys thereof upon the ion milled surfaces of said Group IVB or Group VB metal film.

14. The process of claim 13 wherein said ion milling and said depositing are conducted under vacuum in a single chamber and said vacuum is maintained throughout both said milling and said depositing.