Method of producing .epsilon.-caprolactam, MFI zeolite catalysts on whose surface symmetrically arranged OH groups are present and to a method of producing them

• US 5,741,904 A
• Filed: 05/06/1996
• Issued: 04/21/1998
• Est. Priority Date: 05/04/1995
• Status: Expired due to Term

• Current Assignee: Sumitomo Chemical Company Limited
• Original Assignee: Degussa AG (Rag-Stiftung)
• Inventors: Hoelderich, Wolfgang, Arntz, Dietrich, Roeseller, Joerg
• Primary Examiner(s): BOND, ROBERT
• Application Number:
  US08/647,438
• Time in Patent Office: 715 Days
• Field of Search: 540/536
• US Class Current: 540/536
• CPC Class Codes: C07D 201/04 from or via oximes by Beckmann rearrangement
• CPC Class Codes: Y02P 20/52 using catalysts, e.g. selective catalysts

Abstract

A method of producing ε-caprolactam from cyclohexanone in the gaseous phase using MFI catalysts on whose surface symmetrically arranged OH groups are present.

Claims

1. A method of producing ε

-caprolactam comprising the Beckmann rearrangement of cyclohexanone oxime in the gaseous phase in a temperature range of 250°

to 450°

C. on MFI zeolite catalysts, wherein said MFI zeolite catalysts have OH groups symmetrically arranged in relation to each other on the surface of said MFI zeolite catalysts due to the lack of central metal atoms.

2. The method according to claim 1, wherein said MFI zeolite catalysts are produced by the method comprising contacting a MFI zeolite having central metal atoms at a temperature of 20°

C. to 150°

C. under autogenous pressure in an autoclave with a solution of ammonia salts and/or aqueous ammonia solution to thereby remove some or all of said central metal atoms wherein said MFI zeolite catalyst have OH groups symmetrically arranged in relation to each other on the surface of said MFI zeolite catalyst due to the lack of central metal atoms.

3. The method according to claim 2, wherein said central metal atoms are Si, Al, B, Fe, Ga, Cr, Be, As, Sb, Bi, Ge, Ti, Zr or Hf.

4. The method according to claim 2, wherein said MFI zeolite catalysts have an orthorhombic structure.

5. The method according to claim 2, wherein said central metal atoms are B.

6. The method according to claim 5, wherein the ratio of Si:

B is between 5 to 40;

1.

7. The method according to claim 2, wherein said MFI zeolite catalysts have a primary particle size less than 5 μ

m.

8. The method according to claim 7, wherein said MFI zeolite catalysts have a primary particle size less than 2 μ

m.

9. The method according to claim 8, wherein said MFI zeolite catalysts have a primary particle size less than 1 μ

m.

10. The method according to claim 9, wherein said MFI zeolite catalysts have a primary particle size of 0.05 to 0.5 μ

m.

11. The method according to claim 2, wherein more than 2.5 moles water are used per mole cyclohexanone oxime.

12. The method according to claim 2, said contacting is carried out at a pressure in a range of 0.01 to 1 bar and a temperature of 280°

to 310°

C.