Optical disk and method for its manufacture

• US 5,770,348 A
• Filed: 03/27/1996
• Issued: 06/23/1998
• Est. Priority Date: 03/29/1995
• Status: Expired due to Fees

• Current Assignee: Victor Company of Japan Limited (JVC Kenwood Corporation)
• Original Assignee: Victor Company of Japan Limited (JVC Kenwood Corporation)
• Inventors: Kondo, Tetsuya
• Primary Examiner(s): McPherson, John A.
• Application Number:
  US08/622,392
• Time in Patent Office: 818 Days
• Field of Search: 430/270.11, 430/321, 430/945, 369/283, 369/284, 428/64.4, 428/64.7, 428/65.2, 427/510, 427/164, 264/106, 264/107, 264/1.33, 264/1.36, 264/1.38, 264/1.7
• US Class Current: 430/321
• CPC Class Codes: G11B 7/24 Record carriers characterised by shape, structure or physical properties, or by the selection of the material characterised by the arrangement of information on the carrier G11B7/007
• CPC Class Codes: G11B 7/245 containing a polymeric component
• CPC Class Codes: G11B 7/26 Apparatus or processes specially adapted for the manufacture of record carriers
• CPC Class Codes: Y10S 430/146 Laser beam

Abstract

This invention provides an optical disk whose recorded information cannot be easily copied to other recording media, with practically no degradation of strength. The optical disk of this invention has a ring-shaped signal layer made of radiation curable resin on a transparent substrate, a reflective layer formed on this signal layer, and a protective layer formed on this reflective layer; moreover, the above mentioned signal layer has a peel strength against the above mentioned transparent substrate in the range of about 20/100 to about 80/100 according to the JIS-K5400 test method; and if the outer and inner diameters of the mentioned signal layer are represented by Os and Is respectively, the outer and inner diameters of the mentioned reflective layer are represented by Or and Ir respectively, and the outer and inner diameters of the mentioned protective layer are represented by Op and Ip respectively, these diameters satisfy the relationships,

Os<Or<Op

and

Ip<Ir<Is.

Claims

1. An optical disk comprising:

a transparent substrate;

a ring-shaped signal layer, on top of said transparent substrate, which is made of radiation curable resin and has a peel strength against said transparent substrate in the range of about 20/100 to about 80/100 in the test method JIS-K5400;

a reflective layer that is formed on top of said signal layer; and

a protective layer that is formed on top of said reflective layer;

wherein the outer and inner diameters of said signal layer are represented by Os and Is respectively, the outer and inner diameters of said reflective layer are represented by Or and Ir respectively, and the outer and inner diameters of said protective layer are represented by Op and Ip respectively, these diameters satisfy the relationships,

space="preserve" listing-type="equation">Os<

Or<

Op

and

space="preserve" listing-type="equation">Ip<

Ir<

Is.

2. An optical disk according to claim 1, wherein

said transparent substrate is polycarbonate;

the radiation curable resin that constitutes said signal layer comprises a compound made by mixing a photoinitiator with one or several of the sensitive unsaturated resins shown in C8 to C11 below;

##STR3## wherein m+n=4,

X is an acryloyl group and

Y is a methacryloyl group.

3. A method for manufacturing optical disks comprising:

a step of forming a ring-shaped signal layer on top of a transparent substrate from radiation curable resin that has a peel strength in the range of about 20/100 to about 80/100 according to the test method JIS-K5400;

a step of forming a reflective layer on top of said signal layer; and

a step of forming a protective layer on top of said reflective layer;

wherein the outer and inner diameters of said signal layer are represented by Os and Is respectively, the outer and inner diameters of said reflective layer are represented by Or and Ir respectively, and the outer and inner diameters of said protective layer are represented by Op and Ip respectively, these diameters satisfy the relationships,

space="preserve" listing-type="equation">Os<

Or<

Op

and Ip<

Ir<

Is.

4.

4. A method for manufacturing optical disks according to claim 3, wherein

said transparent substrate is polycarbonate;

the radiation curable resin that constitutes said signal layer comprises a compound made by mixing a photoinitiator with one or several of the sensitive unsaturated resins shown in C12 to C15 below;

##STR4## wherein m+n=4,

X is an acryloyl group and

Y is a methacryloyl group.

5. An optical disk comprising:

a transparent substrate; and

multiple recording sections formed from a ring-shaped signal layer, a reflective layer formed on top of said signal layer, and a protective layer formed on top of said reflective layer;

wherein said signal layer of at least one of said multiple recording sections has a peel strength against the layer beneath it in the range of about 20/100 to about 80/100 according to the test method JIS-K5400;

wherein if the outer and inner diameters of said signal layer are represented by Os and Is respectively, the outer and inner diameters of said reflective layer on said signal layer are represented by Or and Ir respectively, and the outer and inner diameters of said protective layer on said reflective layer are represented by Op and Ip respectively, these diameters satisfy the relationships,

space="preserve" listing-type="equation">Os<

Or<

Op

and

space="preserve" listing-type="equation">Ip<

Ir<

Is.

6. An optical disk according to claim 5, wherein

the protective layer of said recording section also functions as the signal layer of the recording section directly above it.

7. An optical disk according to claim 5, wherein

the signal layer of the bottommost recording section in said multiple recording sections is a crenulated surface formed in the surface of the transparent substrate of the optical disk.

8. An optical disk according to claim 5, wherein

the reflective layers of the recording sections except for the uppermost recording component of said multiple recording sections is semitransparent.