Silicone pressure sensitive adhesive compositions
First Claim
1. A silicone pressure sensitive adhesive composition obtained by a method comprising the steps of(I) reacting a mixture comprising:
- (A)(i) at least one hydroxyl-terminated polydiorganosiloxane having a viscosity of from 100 to 100,000,000 mm2 /s at 25°
C. or(ii) a mixture of(a) a hydroxyl-terminated polydiorganosiloxane and(b) a polydiorganosiloxane selected from(i) polydiorganosiloxanes terminated with monovalent hydrocarbon radicals free of aliphatic unsaturation or(ii) alkenyl-terminated polydiorganosiloxanes wherein said mixture has a viscosity of from 100 to 100,000,000 mm2 /s at 25°
C.;
(B) at least one soluble silicone resin consisting essentially of at least one R3 SiO1/2 unit and at least one SiO4/2 unit, wherein R is independently selected from a monovalent hydrocarbon or halohydrocarbon radical free of aliphatic unsaturation and having from 1 to 20 carbon atoms, an alkenyl radical, or a hydroxyl radical wherein the molar ratio of R3 SiO1/2 units to SiO4/2 units is from 0.5;
1 to 1.2;
1; and
(C) at least one solvent or plasticizer selected from the group consisting of carboxylic acids having at least six carbon atoms and having a boiling point of at least 200°
C. and amines having at least 9 carbon atoms and having a boiling point of at least 200°
C. to form a reaction product; and
(II) adding (D) an organic peroxide or azo compound to the reaction product of (I).
1 Assignment
0 Petitions
Accused Products
Abstract
This invention relates to pressure sensitive adhesive compositions which are obtained by a method comprising reacting a mixture comprising at least one polydiorganosiloxane, at least one silicone resin copolymer, at least one solvent or plasticizer selected from the group consisting of carboxylic acids having at least six carbon atoms and having a boiling point of at least 200°C. and amines having at least 9 carbon atoms and having a boiling point of at least 200°C. to form a reaction product, and then adding an organic peroxide or azo compound to the resultant reaction product. The silicone pressure sensitive adhesives of this invention are useful in preparing articles such as pressure sensitive tapes, labels, emblems and other decorative or informational signs.
-
Citations
30 Claims
-
1. A silicone pressure sensitive adhesive composition obtained by a method comprising the steps of
(I) reacting a mixture comprising: -
(A)(i) at least one hydroxyl-terminated polydiorganosiloxane having a viscosity of from 100 to 100,000,000 mm2 /s at 25°
C. or(ii) a mixture of (a) a hydroxyl-terminated polydiorganosiloxane and (b) a polydiorganosiloxane selected from (i) polydiorganosiloxanes terminated with monovalent hydrocarbon radicals free of aliphatic unsaturation or (ii) alkenyl-terminated polydiorganosiloxanes wherein said mixture has a viscosity of from 100 to 100,000,000 mm2 /s at 25°
C.;(B) at least one soluble silicone resin consisting essentially of at least one R3 SiO1/2 unit and at least one SiO4/2 unit, wherein R is independently selected from a monovalent hydrocarbon or halohydrocarbon radical free of aliphatic unsaturation and having from 1 to 20 carbon atoms, an alkenyl radical, or a hydroxyl radical wherein the molar ratio of R3 SiO1/2 units to SiO4/2 units is from 0.5;
1 to 1.2;
1; and(C) at least one solvent or plasticizer selected from the group consisting of carboxylic acids having at least six carbon atoms and having a boiling point of at least 200°
C. and amines having at least 9 carbon atoms and having a boiling point of at least 200°
C. to form a reaction product; and(II) adding (D) an organic peroxide or azo compound to the reaction product of (I). - View Dependent Claims (2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22)
-
3. A composition according to claim 1, wherein (b)(i) is selected from Me3 SiO(Me2 SiO)a SiMe3, Me3 SiO(Me2 SiO)0.95a (MeViSiO)0.05a SiMe3, or Me3 SiO(Me2 SiO)0.5a (MePhSiO)0.5a SiMe3 wherein Me, Vi, and Ph denote methyl, vinyl and phenyl, respectively, and a has a value such that the viscosity of the polydiorganosiloxane ranges from 1,000 to 500,000 mm2 /s when measured at 25°
- C.
-
4. A composition according to claim 1, wherein (b)(ii) is selected from ViMe2 SiO(Me2 SiO)a SiMe2 Vi, ViMe2 SiO(Me2 SiO)0.95a (MePhSiO)0.05a SiMe2 Vi, ViMe2 SiO(Me2 SiO)0.98a (MeViSiO)0.02a SiMe2 Vi, PhMeViSiO(Me2 SiO)a SiPhMeVi, or PhMeViSiO(Me2 SiO)0.8a (MePhSiO)0.1a (Ph2 SiO)0.1a SiPhMeVi, wherein Me, Vi, and Ph denote methyl, vinyl and phenyl, respectively, and a has a value such that the viscosity of the polydiorganosiloxane ranges from 1,000 to 500,000 mm2 /s when measured at 25°
- C.
-
5. A composition according to claim 1, wherein R is independently selected from methyl, phenyl, vinyl, or hydroxyl, the molar ratio of R3 SiO1/2 units to SiO4/2 units is from 0.6:
- 1 to 1;
1, and (B) has a number average molecular weight of 3,000 to 7,500.
- 1 to 1;
-
6. A composition according to claim 1, wherein (C) is a carboxylic acid having at least six carbon atoms and having a boiling point of at least 200°
- C.
-
7. A composition according to claim 6, wherein the carboxylic acid is selected from the group consisting of nonanoic acid, caproic acid, caprylic acid, oleic acid, linoleic acid, linolenic acid, and N-coco-beta-aminobutyric acid.
-
8. A composition according to claim 1, wherein (C) is an amine having at least 9 carbon atoms and having a boiling point of at least 200°
- C.
-
9. A composition according to claim 8, wherein the amine is selected from the group consisting of dodecylamine, hexadecylamine, octadecylamine, dimethyldodecylamine, dicocoamine, methyldicocoamine, dimethyl cocoamine, dimethyltetradecylamine, dimethylhexadecylamine, dimethyloctadecylamine, dimethyl tallow amine, dimethylsoyaamine, dimethyl nonylamine, di(hydrogenated-tallow)amine, and methyldi(hydrogenated-tallow)amine.
-
10. A composition according to claim 1, wherein (C) is a combination of a carboxylic acid having at least six carbon atoms and having a boiling point of at least 200°
- C. and an amine having at least 9 carbon atoms and having a boiling point of at least 200°
C.
- C. and an amine having at least 9 carbon atoms and having a boiling point of at least 200°
-
11. A composition according to claim 1, wherein the mixture of step (I) further comprises (E) at least one solvent or plasticizer having a boiling point of at least 200°
- C. selected from the group consisting of aliphatic hydrocarbons, glycol ethers, esters, alcohols, ester alcohols, ketones, kerosenes, naphthas, and petrolatums.
-
12. A composition according to claim 11, wherein (E) is selected from the group consisting of dodecane, tridecane, tetradecane, 1-tetradecene, pentadecane, hexadecane, octadecane, nonadecane, diethylene glycol ethyl ether, diethylene glycol butyl ether, triethylene glycol methyl ether, triethylene glycol ethyl ether, triethylene glycol butyl ether, ethylene glycol phenyl ether, propylene glycol phenyl ether, aromatic based glycol ethers, diethylene glycol butyl ether acetate, pine oil, mineral seal oil, tridecyl alcohol, trimethyl pentane diol isobutyrate, and isophorone.
-
13. A composition according to claim 1, wherein the mixture of step (I) further comprises a rare earth metal salt of a fatty acid.
-
14. A composition according to claim 11, wherein the mixture of step (I) further comprises a rare earth metal salt of a fatty acid.
-
15. A composition according to claim 1, wherein the mixture of step (I) further comprises a solvent having a boiling point of less than 200°
- C.
-
16. A composition according to claim 11, wherein the mixture of step (I) further comprises a solvent having a boiling point of less than 200°
- C.
-
17. A composition according to claim 13, wherein the mixture of step (I) further comprises a solvent having a boiling point of less than 200°
- C.
-
18. A composition according to claim 15, wherein the solvent is selected from benzene, toluene, xylene, alcohols, naphtha, cyclic polysiloxanes, or mineral spirits.
-
19. A composition according to claim 16, wherein the solvent is selected from benzene, toluene, xylene, alcohols, naphtha, cyclic polysiloxanes, or mineral spirits.
-
20. A composition according to claim 17, wherein the solvent is selected from benzene, toluene, xylene, alcohols, naphtha, cyclic polysiloxanes, or mineral spirits.
-
21. A composition according to claim 1, wherein (D) is selected from the group consisting of benzoyl peroxide, dichlorobenzoyl peroxide, 2,4-dimethyl-4-methoxyvaleronitrile, and azobisisobutyronitrile.
-
22. A composition according to claim 1, wherein the reaction product of step (I) has a solids content of at least 60% and a viscosity of up to 200,000 millipascal-seconds (mPa·
- s).
-
-
23. An article of manufacture obtained by a method comprising
(I) applying a silicone pressure sensitive adhesive composition to at least one surface of a substrate, wherein the silicone pressure sensitive adhesive composition is obtained by a method comprising the steps of (i) reacting a mixture comprising: -
(A)(i) at least one hydroxyl-terminated polydiorganosiloxane having a viscosity of from 100 to 100,000,000 mm2 /s at 25°
C. or(ii) a mixture of (a) a hydroxyl-terminated polydiorganosiloxane and (b) a polydiorganosiloxane selected from (i) polydiorganosiloxanes terminated with monovalent hydrocarbon radicals free of aliphatic unsaturation or (ii) alkenyl-terminated polydiorganosiloxanes wherein said mixture has a viscosity of from 100 to 100,000,000 mm2 /s at 25°
C.;(B) at least one soluble silicone resin consisting essentially of at least one R3 SiO1/2 unit and at least one SiO4/2 unit, wherein R is independently selected from a monovalent hydrocarbon or halohydrocarbon radical free of aliphatic unsaturation and having from 1 to 20 carbon atoms, an alkenyl radical, or a hydroxyl radical wherein the molar ratio of R3 SiO1/2 units to SiO4/2 units is from 0.5;
1 to 1.2;
1; and(C) at least one solvent or plasticizer selected from the group consisting of carboxylic acids having at least six carbon atoms and having a boiling point of at least 200°
C. and amines having at least 9 carbon atoms and having a boiling point of at least 200°
C. to form a reaction product; and(ii) adding (D) an organic peroxide or azo compound to the reaction product of (i); and (II) heating the silicone pressure sensitive adhesive composition and the substrate to cure the composition. - View Dependent Claims (24, 25, 26, 27, 28, 29, 30)
-