Solid ink jet ink

• US 5,800,600 A
• Filed: 12/19/1996
• Issued: 09/01/1998
• Est. Priority Date: 07/14/1994
• Status: Expired due to Term

• Current Assignee: Tonejet Limited
• Original Assignee: Tonejet Corporation Pty., Ltd.
• Inventors: Lawson, Terence Michael, Nicholls, Stephen Lansell, Lima-Marques, Luis
• Primary Examiner(s): JONES, DEBORAH D
• Application Number:
  US08/750,831
• Time in Patent Office: 621 Days
• Field of Search: 106/31.29, 106/31.61, 106/31.32, 106/31.62, 106/31.35, 106/31.67, 106/31.41, 106/31.73
• US Class Current: 106/31.29
• CPC Class Codes: C09D 11/34 Hot-melt inks

Abstract

A solid ink jet ink composition which is suitable for hot melt applications having a carrier having an electrical resistivity of at least 10⁸ Ohm.cm, insoluble marking particles and a particle charging agent dispersed in it. The marking particle may be a pigment, an insoluble dyestuff, a polymer or mixture thereof. The particle charging agent may be a metal soap, a fatty acid, lecithin, an organic phosphorous compound, a succinimide, a sulphosuccinate, petroleum sulphonates, a soluble or partially soluble resin such as a modified rosin ester, an acrylic, a vinyl a hydrocarbon or a mixture thereof. The solid ink jet ink composition may further include a viscosity controller. The ink may be capable of being heated to 155° C. and have at that temperature a viscosity of between 5 to 150 cps.

Claims

1. A solid ink jet composition comprising a carrier having an electrical resistivity of at least 10⁸ Ohm.cm, insoluble marking particles and a particle charging agent dispersed therein, wherein said marking particles are capable of being agglomerated and ejected from the bulk ink as discrete droplets in the presence of an electrostatic field when the viscosity of the ink is reduced.

2. A solid ink jet ink composition as in claim 1, wherein the reduction in viscosity is done by heating and subsequent melting of the ink.

3. A solid ink jet ink composition as in claim 1, wherein the marking particle is a pigment, an insoluble dyestuff, a polymer or mixture thereof.

4. A solid ink jet ink composition as in claim 1, wherein the particle charging agent is a metal soap, a fatty acid, lecithin, an organic phosphorus compound, a succinimide, a sulphosuccinate, petroleum sulphonates or a mixture thereof.

5. A solid ink jet ink composition as in claim 1, wherein the particle charging agent is a soluble or partially soluble resin such as a modified rosin ester, an acrylic, a vinyl, a hydrocarbon or a mixture thereof.

6. A solid ink jet ink composition as in claim 1 further including a viscosity controller wherein the viscosity controller is selected from the group comprising ethylene vinyl acetate copolymers, polybutadienes, polyisobutylenes or mixtures of thereof.

7. A solid ink jet ink composition as in claim 1 wherein the carrier comprises a low melting point wax or resin.

8. A solid ink jet ink composition as in claim 7 wherein the wax or resin is selected from low molecular weight polyethylene, hydrogenated castor oil, ester wax, paraffin wax, rosins, and ethylene vinyl acetate copolymers or mixtures thereof.

9. A printing plate comprising a solid ink jet composition as in claim 1 on a substrate.

10. A solid ink jet composition as in claim 1 where the viscosity of the ink is reduced when the composition is heated to 155°

C.

11. A solid ink jet ink composition as in claim 10 where the ink has a viscosity in the range of 5 to 150 cps when heated to 155°

C.

18. A solid ink jet composition as in claim 1 wherein the ink has a viscosity of from 5 to 150 cps at a temperature of from 110°

C. to 195°

C.

19. A solid ink jet composition as in claim 18 wherein the ink has a viscosity of from 5 to 150 cps at a temperature of from 125°

C. to 155°

C.

12. A solid ink jet composition comprising a carrier having an electrical resistivity of at least 10⁸ Ohm.cm, insoluble marking particles and a particle charging agent, wherein the ink has a viscosity in the range of 5 to 150 cps at 155°

C. and the particle charging agent is selected from the group consisting of metal soaps, fatty acids, lecithin, organic phosphorous compounds, succinimides, sulphosuccinates, petroleum sulphonates, soluble or partially soluble resins, and mixtures thereof.

16. A solid ink jet composition as in claim 12 wherein said resins are selected from the group consisting of modified resin esters, acrylic esters, vinyl esters, and mixtures thereof.

13. A solid ink jet composition comprising a carrier having an electrical resistivity of at least 10⁸ Ohm.cm, insoluble marking particles and a particle charging agent, wherein the ink is capable of being heated to 135°

C. and has a viscosity in the range of 20 to 50 cps at that temperature and the particle charging agent is selected from the group consisting of metal soaps, fatty acids, lecithin, organic phosphorous compounds, succinimides, sulphosuccinates, petroleum sulphonates, soluble or partially soluble resins, and mixtures thereof.

17. A solid ink jet composition as in claim 13 wherein said resins are selected from the group consisting of modified resin esters, acrylic esters, vinyl esters, and mixtures thereof.

14. A solid ink jet ink comprising;

(a) 80 to 98.9% of a carrier having an electrical resistivity of at least 10⁸ Ohm.cm and which is solid at room temperature and which has a viscosity in the range of 5 to 150 cps at 155°

C.,

(b) 1 to 10% of insoluble marking particles, and

(c) 0.1 to 5% of a particle charging agent.

15. A solid ink jet ink comprising;

(a) 80 to 98.9% of a carrier which is solid at room temperature and which has a viscosity in the range of 5 to 150 cps at 155°

C.,

(b) 1 to 10% of insoluble marking particles, and

(c) 0.1 to 5% of a particle charging agent, the resultant ink having an electrical resistivity of at least 10⁸ Ohm.cm.