Use of waste glass in concrete

• US 5,810,921 A
• Filed: 03/03/1997
• Issued: 09/22/1998
• Est. Priority Date: 03/03/1997
• Status: Expired due to Fees

• Current Assignee: Trustees Of Columbia University In The City Of New York (Columbia University)
• Original Assignee: Trustees Of Columbia University In The City Of New York (Columbia University)
• Inventors: Jin, Weihua, Baxter, Steven Z., Meyer, Christian
• Primary Examiner(s): GREEN, ANTHONY J
• Application Number:
  US08/810,558
• Time in Patent Office: 568 Days
• Field of Search: 106/711, 106/737, 106/814, 106/716
• US Class Current: 106/711
• CPC Class Codes: C03C 13/001 Alkali-resistant fibres
• CPC Class Codes: C04B 14/22 Glass ; Devitrified glass
• CPC Class Codes: C04B 14/42 Glass
• CPC Class Codes: C04B 2111/10 Compositions or ingredients thereof characterised by the absence or the very low content of a specific material
• CPC Class Codes: C04B 2111/2023 Resistance against alkali-aggregate reaction

Abstract

The present invention relates generally to a glass formula for incorporation in glass-concrete compositions. The glass contains chromium. A detrimental reaction between the cement and the chromium glass and/or a reactive aggregate glass is suppressed in the set glass-concrete compositions.

Claims

1. A set glass-concrete composition which comprises chromium glass particles and reactive aggregate dispersed in hydrated cement, wherein said chromium glass particles have a green color and have an average diameter of less than 0.5 mm and comprise a sufficient amount of chromium to suppress a detrimental chemical reaction between the hydrated cement and the reactive aggregate, wherein the chromium glass particles do not contain an amount of zirconium which is sufficient to impart enhanced alkali resistant properties to the chromium glass particles.

3. A set glass-concrete composition according to claim 1, wherein the reactive aggregate comprises silica, and the detrimental chemical reaction is an alkali silica reaction.

5. A set glass-concrete composition according to claim 3, wherein the chromium glass particles contain trace amounts of zirconium.

7. A set glass-concrete composition according to claim 3, wherein the chromium glass particles are fibers.

10. A set glass-concrete composition according to claim 1, wherein the chromium glass particles comprise soda-lime glass comprising from 0.1% to 2.0% by weight of chromium oxide.

11. A set glass-concrete composition according to claim 3, wherein the composition comprises from 0.5% by weight to 20% by weight chromium glass particles by total weight of cement.

2. A set glass-concrete composition which comprises chromium glass particles dispersed in hydrated cement, wherein said chromium glass particles have a green color and have an average diameter of greater than 0.5 mm and comprise a sufficient amount of chromium to suppress a detrimental chemical reaction between the hydrated cement and the chromium glass particles, wherein the chromium glass particles do not contain an amount of zirconium which is sufficient to impart enhanced alkali resistant properties to the chromium glass particles.

4. A set glass-concrete composition according to claim 2, wherein the detrimental chemical reaction is an alkali silica reaction.

6. A set glass-concrete composition according to claim 4, wherein the chromium glass particles contain trace amounts of zirconium.

8. A set glass-concrete composition according to claim 4, wherein the chromium glass particles are fibers.

9. A set glass-concrete composition according to claim 2, wherein the chromium glass particles comprise soda-lime glass comprising from 0.1% to 2.0% by weight of chromium oxide.

12. A set glass-concrete composition according to claim 4, wherein the combination of reactive aggregate and chromium glass particles comprises from 0.5% by weight to 100% by weight chromium glass particles.

13. A process for making a set glass-concrete composition which comprises mixing dry cement, water, a reactive aggregate and chromium glass particles having a green color and having an average diameter of less than 0.5 mm and comprising a sufficient amount of chromium to suppress a detrimental chemical reaction between the cement and the reactive aggregate, wherein the chromium glass particles do not contain an amount of zirconium which is sufficient to impart enhanced alkali resistant properties to the chromium glass particles.

15. A process according to claim 13, wherein the reactive aggregate comprises silica, and the reaction is an alkali silica reaction.

18. A set glass-concrete composition according to claim 13, wherein the chromium glass particles comprise soda-lime glass comprising from 0.1% to 2.0% by weight of chromium oxide.

19. A process according to claim 15, wherein the chromium glass particles are fibres.

21. The set glass-concrete composition provided by the process according to claim 13.

23. A set glass-concrete composition according to claim 21, wherein the chromium glass particles are fibers.

14. A process for making a set glass-concrete composition which comprises mixing dry cement, water, and chromium glass particles having a green color and having an average diameter of greater than 0.5 mm and comprising a sufficient amount of chromium effective to suppress a detrimental chemical reaction between the cement and the chromium glass particles, wherein the chromium glass particles do not contain an amount of zirconium which is sufficient to impart enhanced alkali resistant properties to the chromium glass particles.

16. A process according to claim 14, wherein the reaction is an alkali silica reaction.

17. A process according to claim 16, wherein the chromium glass particles comprise soda-lime glass comprising from 0.1% to 2.0% by weight of chromium oxide.

20. A process according to claim 16, wherein the chromium glass particles are fibres.

22. The set glass-concrete composition provided by the process according to claim 14.

24. A set glass-concrete composition according to claim 22, wherein the chromium glass particles are fibers.