Large pore synthetic polymer membranes

• US 5,846,422 A
• Filed: 06/11/1996
• Issued: 12/08/1998
• Est. Priority Date: 03/04/1994
• Status: Expired due to Term

• Current Assignee: USF Filtration and Separations Group, Inc. (Siemens AG)
• Original Assignee: Memtec America Corporation (Danaher Corporation)
• Inventors: Morris, Richard A., Ditter, Jerome, Zepf, Robert
• Primary Examiner(s): FORTUNA, ANA M
• Application Number:
  US08/661,839
• Time in Patent Office: 910 Days
• Field of Search: 210/490, 210/500.41, 210/500.22, 210/500.27, 264/41, 264/49
• US Class Current: 210/500.41
• CPC Class Codes: B01D 2323/08 Specific temperatures applied
• CPC Class Codes: B01D 2323/12 Specific ratios of components used
• CPC Class Codes: B01D 2325/022 Asymmetric membranes
• CPC Class Codes: B01D 2325/04 Characteristic thickness
• CPC Class Codes: B01D 2325/20 Specific permeability or cut-off range
• CPC Class Codes: B01D 2325/34 Molecular weight or degree of polymerisation
• CPC Class Codes: B01D 61/14 Ultrafiltration; Microfiltration
• CPC Class Codes: B01D 61/147 Microfiltration
• CPC Class Codes: B01D 67/0009 by phase separation, sol-gel transition, evaporation or solvent quenching
• CPC Class Codes: B01D 67/0011 Casting solutions therefor
• CPC Class Codes: B01D 67/0013 Casting processes
• CPC Class Codes: B01D 69/02 characterised by their properties
• CPC Class Codes: B01D 71/68 Polysulfones; Polyethersulfones
• CPC Class Codes: B32B 5/32 at least two layers being foamed and next to each other
• CPC Class Codes: C12H 1/061 Separation by centrifugation
• CPC Class Codes: G01N 33/54366 Apparatus specially adapted for solid-phase testing
• CPC Class Codes: G01N 33/54388 based on lateral flow
• CPC Class Codes: G01N 33/558 using diffusion or migration of antigen or antibody immunochromatographic test strips G01N33/54387

Abstract

Highly asymmetric polymeric membranes with large pores which yield bubble points in the range of 0.5 to 25 psid and superior flow characteristics. The membranes can be cast from both metastable dispersions and from homogenous casting formulations. The technique of synthesis involves exposure of the cast membrane to humid air to create large surface pores on the exposed side.

Claims

1. An integral microporous polymer membrane comprising a first porous skin surface, a second surface, and a porous supporting structure therebetween, wherein the first surface comprises a relatively open pore structure and the second surface comprises a more open pore structure and wherein the supporting structure comprises an isotropic region adjacent the skin, the isotropic region having substantially constant pore size, the porous support further comprising an asymmetric region adjacent the isotropic region, the asymmetric region possessing a high degree of asymmetry and extending through at least 50% of the supporting structure but no more than 80% of the supporting structure.

2. The membrane of claim 1, wherein the polymer is a polysulfone.

3. The membrane according to claim 1, having a bubble point of from about 0.5 psid to about 25 psid.

4. The membrane of claim 3, wherein the bubble point is from about 5 psid to about 15 psid.

5. The membrane according to claim 1, having a mean aqueous flow rate of from about 4.5 to 25 cm/min psid.

6. The membrane of claim 1, having a bubble point not greater than about 25 psid.

7. filter unit, comprising the polymer membrane of claim 1.

8. An integral microporous polymer membrane comprising a first porous skin surface, a second porous surface, and a porous supporting structure having a thickness therebetween, wherein the supporting structure has a generally isotropic structure of substantially constant pore size from the first surface to a point at about one-quarter of the thickness of the supporting structure and a generally asymmetric structure of gradually increasing pore sizes from the point to the second surface.

9. The membrane of claim 8, wherein the polymer is a polysulfone.

10. The membrane according to claim 8, having a bubble point of from about 0.5 psid to about 25 psid.

11. The membrane of claim 10, wherein the bubble point is from about 5 psid to about 15 psid.

12. The membrane according to claim 8, having a mean aqueous flow rate of from about 4.5 to 25 cm/min psid.

13. The membrane of claim 8, having a bubble point not greater than about 25 psid.

14. A filter unit, comprising the polymer membrane of claim 8.

15. An integral microporous polymer membrane comprising a first porous skin surface, a second porous surface, and a supporting structure having a thickness therebetween, the supporting structure defining porous flow channels between the first and second surface, wherein the flow channels have a substantially constant mean diameter from the first surface to a point at about one-quarter of the thickness of the supporting structure and a gradually increasing mean diameter from the point to the second surface.

16. The membrane of claim 15, wherein the polymer is a polysulfone.

17. The membrane according to claim 15, having a bubble point of from about 0.5 psid to about 25 psid.

18. The membrane of claim 17, wherein the bubble point is from about 5 psid to about 15 psid.

19. The membrane according to claim 15, having a mean aqueous flow rate of from about 4.5 to 25 cm/min psid.

20. The membrane of claim 15, having a bubble point not greater than about 25 psid.

21. A filter unit, comprising the polymer membrane of claim 15.

22. An integral microporous polymer membrane suitable for isolating a liquid fraction from a suspension, comprising:

an integral microporous skin, lying at one face of the membrane, wherein substantially all of the pores of the skin have diameters greater than about 1.2 microns; and

a support region of the membrane lying between the skin face of the membrane and an opposite face of the membrane, the support region being separated into a first and a second zone, the first zone lying adjacent to the skin having a generally isotropic structure of substantially constant pore size and the second zone lying adjacent to the first zone having an asymmetric structure, the asymmetric structure having gradually increasing pore sizes in a direction from the first zone to the opposite face of the membrane.

23. The membrane of claim 22, wherein the polymer is a polysulfone.

24. The membrane according to claim 22, having a bubble point of from about 0.5 psid to about 25 psid.

25. The membrane of claim 24, wherein the bubble point is from about 5 psid to about 15 psid.

26. The membrane according to claim 22, having a mean aqueous flow rate of from about 4.5 to 25 cm/min psid.

27. The membrane of claim 22, having a bubble point not greater than about 25 psid.

28. A filter unit, comprising the polymer membrane of claim 22.

29. In an integral microporous asymmetric polymer membrane having a first porous skin surface, a second porous surfaces and a porous supporting structure therebetween and having a thickness, the improvement comprising:

a region of generally isotropic structure from the first surface to a point at about one-quarter of the thickness of the supporting structure the isotropic structure having substantially constant pore size.

30. A filter unit, comprising the polymer membrane of claim 29.