Soft multi-ply tissue paper having a surface deposited strengthening agent

• US 5,851,352 A
• Filed: 05/12/1997
• Issued: 12/22/1998
• Est. Priority Date: 05/12/1997
• Status: Expired due to Term

• Current Assignee: The Procter & Gamble Company
• Original Assignee: The Procter & Gamble Company
• Inventors: Vinson, Kenneth Douglas, Ficke, Jonathan Andrew, Deason, Howard Thomas
• Primary Examiner(s): Chin, Peter
• Application Number:
  US08/854,397
• Time in Patent Office: 589 Days
• Field of Search: 162/109, 162/111, 162/112, 162/113, 162/123, 162/127, 162/132, 162/133, 162/125, 162/129, 162/169, 156/291, 156/324, 428/153, 428/154
• US Class Current: 162/112
• CPC Class Codes: B32B 2255/12 on paper layer
• CPC Class Codes: B32B 2555/00 Personal care
• CPC Class Codes: B32B 29/005 next to another layer of paper or cardboard layer
• CPC Class Codes: B32B 29/06 specially treated, e.g. surfaced, parchmentised
• CPC Class Codes: D21H 21/18 Reinforcing agents
• CPC Class Codes: D21H 27/32 with materials applied between the sheets attaching together paper or cardboard sheets B31F5/00; adhesives C09J

Abstract

Strong and soft multi-ply tissue paper products useful as absorbent sanitary products such as bath tissue, facial tissue, and absorbent towels are disclosed. At least one internal surface of the tissue paper product has a surface deposited strengthening agent.

Claims

1. A strong and soft multi-ply tissue paper product, said multi-ply tissue paper product comprising at least two plies in face to face relationship, wherein each of said plies has an interior surface oriented toward the interior of said multi-ply tissue paper product, wherein at least one of said interior surfaces of said plies has a surface deposited strengthening agent, said strengthening agent being deposited on said surface in a first relatively diffiuse pattern essentially covering the entirety of said surface and in a second relatively uniform sparse pattern which is deposited on said surface at a frequency of between about 0.2 and about 2 deposits per inch, said second deposits having a diameter of at least 1000 microns wherein said strengthening agent comprises from about 0.5 to about 10% of said tissue paper product by weight based on the dry weight of said strengthening agent compared to the dry weight of said multiply tissue product.

2. The multi-ply tissue paper product of claim 1 wherein said strengthening agent is selected from a group consisting of starch, polyvinyl alcohol, polyamide resins, polyacrylamide resins, acrylic polymers, styrene-butadiene copolymers, vinyl acetate polymers, ethylene-vinyl acetate copolymers, vinyl chloride polymers, vinylidene chloride polymers, vinyl chloride-vinylidene copolymers, acrylo-nitrile copolymers, ethylene-acrylic copolymers and mixtures thereof.

3. The multi-ply tissue paper product of claim 2 wherein said strengthening agent comprises from about 2% to about 5% of said tissue paper product by weight based on the dry weight of said strengthening agent compared to the dry weight of said tissue paper product.

4. The multi-ply tissue paper product of claim 3 wherein said multi-ply tissue paper product has two plies.

5. The multi-ply tissue paper product of claim 4 wherein said plies comprise a wire side and a felt side wherein said felt side of both of said plies is oriented such that they comprise interior surfaces of said multi-ply tissue paper product.

6. The multi-ply tissue paper product of claim 5 wherein said strengthening agent comprises an elastomeric polymer with a glass transition temperature between about -30 degrees C. and about 10 degrees C.

7. The multi-ply tissue paper product of claim 6 wherein said elastomeric polymer is an acrylic polymer.

8. The multi-ply tissue paper product of claim 7 wherein said plies comprise through-air dried tissue paper webs.

9. The multi-ply tissue paper product of claim 8 wherein said acrylic polymer is distributed over essentially the entire surface of at least one of said interior surfaces of the tissue paper webs comprising said multi-ply tissue paper product.

10. A process for producing a soft, strong multi-ply tissue paper product, said process comprising the steps of

a) applying by surface deposition a fluidized strengthening agent onto the surface of a tissue paper web thereby forming a surface strengthened tissue paper web comprising from about 0.5% to about 10% of said strengthening agent wherein said strengthening agent is applied to said surface in a first relatively diffuse pattern essentially covering the entirety of said surface and in a second relatively uniform sparse pattent which is deposited on said surface at a frequency of between about 0.2 and about 2 deposits per inch said second deposits having a diameter of at least 1000 microns ;

and

b) combining said surface strengthened tissue paper web of step (a) with at least one additional tissue paper web to form a multiply tissue paper product, orienting said surface strengthened tissue paper web being oriented such that the surface comprising the strengthening agent forms an interior surface of said multi-ply tissue paper product;

wherein said multi-ply tissue paper product comprises tissue paper webs which remain unbonded over at least a majority of the surface of said webs.

11. The process of claim 10 wherein said fluidized strengthening agent is non-uniformly deposited such that a uniform sparse pattern of relatively concentrated areas of fluidized strengthening agent is deposited within a uniformly applied, relatively diffuse pattern of fluidized strengthening agent and wherein said combining step (b) is effected by applying a combining pressure sufficient to substantially join said surface strengthened tissue paper web to said additional tissue paper web by binding via the concentrated areas of strengthening agent said combining pressure being insufficient to effect binding by the areas of strengthening agent residing in the uniform relatively diffuse field.

12. The process of claim 11 wherein the process step comprising depositing said strengthening agent is effected by printing.

13. The process of claim 12 wherein said fluidized strengthening agent is a latex emulsion.

14. The process of claim 13 wherein said latex emulsion has a solids content between about 10% and about 50%.

15. The process of claim 14 wherein said latex emulsion comprises a polymer having a glass transition temperature between about -30 degrees C. and about 10 degrees C.

16. The process of claim 15 wherein said latex emulsion comprises an acrylic emulsion.

17. The process of claim 10 wherein said multi-ply tissue paper product is a two-ply tissue paper product.

18. The process of claim 17 wherein the process step comprising depositing said strengthening agent is effected by a printing step.

19. The process of claim 18 wherein said printing step is effected by use of a direct gravure process.

20. The process of claim 18 wherein said fluidized strengthening agent is a latex emulsion.

21. The process of claim 19 wherein said latex emulsion comprises a polymer having a glass transition temperature between about -30 degrees C. and about 10 degrees C.

22. The process of claim 20 wherein said latex emulsion comprises an acrylic emulsion.

23. The process of claim 21 wherein said latex emulsion is non-uniformly printed such that a uniform sparse pattern of relatively concentrated areas of latex is deposited within a uniformly applied, relatively diffuse pattern of latex emulsion and wherein said combining step (b) is effected by applying a combining pressure sufficient to substantially join said surface strengthened tissue paper web to said additional tissue paper web by binding via the concentrated areas of latex solids said combining pressure being insufficient to effect binding by the areas of latex solids residing in the uniform relatively diffuse field.