Aqueous binder dispersion for physically drying coating agents and their use

• US 5,854,337 A
• Filed: 10/22/1997
• Issued: 12/29/1998
• Est. Priority Date: 10/30/1996
• Status: Expired due to Fees

• Current Assignee: Herberts Gesellschaft Mit Beschrankter Haftung
• Original Assignee: Herberts Gesellschaft Mit Beschrankter Haftung
• Inventors: Wiggershaus, Stefan, Wandelmaier, Klaus
• Primary Examiner(s): NILAND, PATRICK DENNIS
• Application Number:
  US08/955,696
• Time in Patent Office: 433 Days
• Field of Search: 524/591, 524/839, 524/840, 524/539
• US Class Current: 524/591
• CPC Class Codes: C08L 75/04 Polyurethanes
• CPC Class Codes: C09D 175/04 Polyurethanes

Abstract

The invention relates to an aqueous binder dispersion for physically drying coating agents, which contains a mixture of

A) 20-80 wt. % of one or more, carbonate group-containing polyurethanes with a number average molecular weight (Mn) of 70,000 to 500,000 in the form of an aqueous dispersion, and

B) 20-80 wt. % of one or more carbonate group-free and preferably urea group-free polyurethane resins containing ionic groups, with a number average molecular weight (Mn) of 10,000 to 300,000 and an acid value of 5 to 50, in the form of an aqueous dispersion,

the wt. % of the components A) and B), in each case referred to the resin solids, amounting to 100%.

Claims

1. An aqueous binder dispersion for physically drying coating agents containing a mixture of:

A) 20-80 wt. % of one or more, carbonate group-containing polyurethanes with a number average molecular weight (Mn) of 70,000 to 500,000, in the form of an aqueous dispersion, obtained by reacting

a) 10-40 wt. % of one or more organic polyisocyanates that have no hydrophilic groups or groups that will convert into hydrophilic groups,

b) 40-80 wt. % of one or more high molecular weight organic polyhydroxy compounds that have no hydrophilic groups or groups that will convert into hydrophilic groups, and which comprise at least 50 wt. % of one or more polyhydroxy polycarbonates,

c) 0.2-18 wt. % of one or more low molecular weight compounds that have at least two groups that will react with isocyanate groups, but have no hydrophilic groups or groups that will convert into hydrophilic groups,

d) 1-12 wt. % of one or more compounds that have at least one anionic group or at least one group that will convert into an anionic group, and at least one hydrogen atom that will react with isocyanate groups, and

e) 0-8 wt. % of one or more non-ionic hydrophilic compounds that have at least one isocyanate group or at least one group that will react with isocyanate groups, the sum of the components a) to e) being 100 wt. %,

and

B) 20-80 wt. % of one or more carbonate group-free polyurethane resins containing ionic groups, with a number average molecular weight (Mn) of 10,000 to 300,000 and an acid value of 5 to 50, in the form of an aqueous dispersion obtained by preparing a OH group-containing polyurethane prepolymer with a OH number of 5 to 75 and a number average molecular weight (Mn) of 5,000 to 50,000, by reacting in an organic medium

f) one or more compounds reactive with isocyanate and having an acid value of 0 to 10, in the form of

f1) 70 to 100 wt. % of one or more polyester polyols and/or polyether polyols with a molecular weight of 500 to 6,000, together with

f2) 0 to 30 wt. % of one or more compounds different from f1) having at least two groups reactive with isocyanate, with a molecular weight of 60 to 400, the sum of the components f1) and f2) being 100 wt. %, with

g) at least one compounds with two groups reactive with isocyanate and at least one anionic group or a group that will form anions, the component g) being able to be used separately or in the form of a reaction product g1) of component g) and one or more organic diisocyanates g2), the molar ratio of the groups of g) reactive with isocyanate groups to the isocyanate groups of g2) being 1;

1.5 to 1;

2.5, and the reaction product g1) being prepared in the presence of component f), and the component g) or the reaction product g1) being used in such an amount that the prepared polyurethane resins have the desired acid value, and

h) one or more polyisocyanates with at least two free isocyanate groups per molecule, in such an amount that the molar ratio of the OH groups of component f) to the NCO groups of the components g) and h) is 1.01;

1 to 3;

1,

following which the prepolymer obtained from f), g) and h) is, before or after the partial or complete neutralisation of existing groups that will convert into ionic groups, subjected to a chain extension in the organic medium or after conversion into the aqueous phase, by reaction with

i) one or more polyfunctional isocyanates having a functionality of free NCO groups of at least 1.8, in such proportions that the prepared polyurethane resins have the desired number average molecular weight,

the weight percentages of components A) and B) in each case referring to the resin solids and making up 100%.

2. A binder dispersion according to claim 1, wherein the component A) contains per 100 g of solid resin at least 200 milliequivalents of carbonate groups of the formula --O--CO--O--.

3. A binder dispersion according to claim 1 wherein it contains 40 to 60 wt. % of A) and 40 to 60 wt. % of B), the total amounting to 100 wt. %.

4. An aqueous coating agent comprising

8-20 wt. % of one or more binder dispersions according to claim 1,

to 90 wt. % of water,

0.1 to 20 wt. % of one or more effect pigments and/or colour-imparting pigments and/or fillers,

the sum of the constituents amounting to 100 wt. %.

5. A method for the preparation of a base layer of a multi-layer lacquer comprising applying an aqueous coating agent of claim 4 to a substrate and drying the coating agent to form the base layer.

6. An aqueous binder dispersion according to claim 1 wherein the polyurethane resin component B) is free of urea groups.

7. An aqueous binder dispersion according to claim 1 wherein the polyester polyol component f1) is free of carboxylic acid groups.

8. An aqueous coating agent according to claim 4 further comprising up to 20 wt. % of one or more organic solvents and the sum of the constituents includes the organic solvents.

9. An aqueous coating agent according to claim 4 further comprising one or more additives or auxiliary substances, and the sum of the constituents includes the additives or auxiliary substances.