Biodegradable polyester with improved molding characteristics and its production

• US 5,886,093 A
• Filed: 05/28/1998
• Issued: 03/23/1999
• Est. Priority Date: 06/03/1997
• Status: Expired due to Fees

• Current Assignee: Klaus Schmidt
• Original Assignee: Klaus Schmidt
• Inventors: Qureshi, Naseer Mohammed, Keane, Barry, Woodfine, Barry, Davies, Martin Thomas
• Primary Examiner(s): Acquah, Samuel A.
• Application Number:
  US09/084,929
• Time in Patent Office: 299 Days
• Field of Search: 528/354, 528/355, 528/357, 528/359, 528/361, 524/755, 524/765, 524/783, 524/784
• US Class Current: 524/755
• CPC Class Codes: C08G 63/823 for the preparation of polylactones or polylactides
• CPC Class Codes: C08G 64/30 using carbonates

Abstract

The invention relates to a method for preparing a biodegradable aliphatic polyester, which comprises polymerization of a precursor of the polyester in the presence of a polyesterification catalyst in an amount of up to 0.1% by weight, based on the weight of the cyclic precursor, and a co-catalyst comprising glycerol or butyrolactone in a weight proportion of not more than three times that of the catalyst.

The invention also relates to the use of the resulting biodegradable aliphatic polyester in polymer processing, such as injection molding or compression/press molding.

Claims

1. A method for preparing a biodegradable aliphatic polyester, which comprises polymerization of a precursor of the polyester in the presence of a polyesterification catalyst in an amount of from 0.0001% to 0.1% by weight, based on the weight of the precursor, and a co-catalyst comprising glycerol or butyrolactone in a weight proportion of not more than three times that of the catalyst.

2. A method according to claim 1, which comprises ring-opening polymerization of a cyclic precursor of the polyester in the presence of a ring-opening polyesterification catalyst.

3. A method according to claim 1, in which the precursor is a cyclic lactone.

4. A method according to claim 1, in which the precursor is lactide, glycolide, trimethylene carbonate or caprolactone, or any mixture thereof.

5. A method according to claim 1, in which the catalyst is a metal carboxylate, an organometal carboxylate, a metal oxide or a metal halide.

6. A method according to claim 5, in which the metal is tin or zinc.

7. A method according to claim 6, in which the catalyst is tin (II) octoate, triphenyltin acetate or tin oxide.

8. A method according to claim 7, in which the catalyst is present in an amount of from 0.0005% to 0.01% by weight, based on the weight of the cyclic precursor.

9. A method according to claim 1, in which the co-catalyst is present in an amount of from 25% to 300% by weight, based on the weight of the catalyst.

10. A method according to claim 9, in which the co-catalyst is present in an amount of from 75% to 200% by weight, based on the weight of the catalyst.

12. A biodegradable product comprising a biodegradable aliphatic polyester prepared by a method according to claim 1.

11. A catalyst composition for polymerization of a precursor of a biodegradable aliphatic polyester, comprising of a polyesterification catalyst and a co-catalyst comprising glycerol or butyrolactone in a weight proportion of not more than three times that of the catalyst.

13. In a method of polymerizing a precursor of a biodegradable aliphatic polyester catalyzed by a polyesterification catalyst, wherein the improvement comprises using glycerol or butyrolactone as a co-catalyst.

14. In a method of processing a polymer, wherein the improvement comprises using a biodegradable aliphatic polyester produced by a method which comprises polymerization of a precursor of the polyester in the presence of a polyesterification catalyst in an amount of from 0.0001% to 0.1% by weight, based on the weight of the precursor, and a co-catalyst comprising glycerol or butyrolactone in a weight proportion of not more than three times that of the catalyst.

15. A processing method according to claim 14 which is injection molding or compression/press molding.

16. A method according to claim 14 wherein the biodegradable aliphatic polyester is polylactic acid or polyglycolic acid.

17. A method according to claim 14 wherein the biodegradable aliphatic polyester is polylactic acid, and the catalyst/co-catalyst is tin octoate:

glycerol in a weight ratio of from 0.3;

1 to 2;

1 biodegradable polymer is prepared by injection molding.