Electrochromic layer and devices comprising same

• US 5,888,431 A
• Filed: 03/15/1996
• Issued: 03/30/1999
• Est. Priority Date: 07/22/1994
• Status: Expired due to Term

• Current Assignee: Gentex Corporation
• Original Assignee: Gentex Corporation
• Inventors: Tonar, William L., Anderson, John S., Byker, Harlan J., Ash, Kevin L., Siegrist, Kathy E.
• Primary Examiner(s): TUCKER, PHILIP C
• Application Number:
  US08/616,275
• Time in Patent Office: 1,110 Days
• Field of Search: 252/583, 252/586, 359/265, 359/270, 359/273, 359/275
• US Class Current: 252/583
• CPC Class Codes: C09K 2211/1029 containing one nitrogen atom as the heteroatom
• CPC Class Codes: C09K 9/02 Organic tenebrescent materials
• CPC Class Codes: G02F 1/1503 caused by oxidation-reduction reactions in organic liquid solutions, e.g. viologen solutions
• CPC Class Codes: G02F 2001/1502 complementary cell
• CPC Class Codes: G02F 2001/15145 the electrochromic layer comprises a mixture of anodic and cathodic compounds
• CPC Class Codes: G02F 2202/022 polymeric

Abstract

The present invention provides improved electrochromic layers, which comprise polymeric matrices with electrochromic solutions interspersed therein. Varying an electrical potential difference across a layer of the invention results in reversible variation in the transmittance of light across the layer because of electrochemical processes in the electrochromic solution of the layer. The invention further provides electrochromic devices, in which the electrochromic layers of the invention provide reversibly variable transmittance to light, and various apparatus in which the devices of the invention provide light-filtering or light-color modulation. Such apparatus include windows, including those for use inside and on the outside walls of buildings and in sunroofs for automobiles, and variable reflectance mirrors, especially rearview mirrors for automobiles.

Claims

1. An electrochromic layer of reversibly variable transmittance to light, comprising a cross-linked polymer matrix, a solvent, and at least one electrochromic compound in solution with said solvent and interspersed in the polymer matrix, where said polymer matrix results from crosslinked polymer chains, where said polymer matrix comprises less than about 50 percent by weight of said electrochromic layer.

2. The electrochromic layer according to claim 1 where, prior to crosslinking, said polymer chains are substantially linear.

3. The electrochromic layer according to claim 1, where said polymer chains have a hydroxyl functionality of at least 2 and are covalently cross-linked through hydroxyl groups.

4. The electrochromic layer according to claim 1 where said polymer chains are the product of monomers going through a chain-lengthening polymerization within said solvent.

5. The electrochromic layer according to claim 4 where said polymer chain lengthening takes place in the presence of an azo thermal initiator.

6. The electrochromic layer according to claim 5, where said polymer chains contain acrylate and hydroxide functional groups.

7. The electrochromic layer according to claim 6 where said polymer chains are formed from a mono hydroxy caprolactone acrylate.

8. The electrochromic layer according to claim 4 where said polymer chains contain functional groups selected from the group consisting of ester, acrylate, vinyl and ether.

9. The electrochromic layer according to claim 8 where said polymer chains are cross-linked by reaction with a compound selected from the group consisting of a polyisocyanate with an isocyanate functionality of at least 2, a metal alkoxide with an alkoxide functionality of at least 2, and a bisketene, provided that, if the hydroxyl functionality of said polymer chains is 2, the reaction is with a compound selected from the group consisting of a polyisocyanate with an isocyanate functionality of more than 2 and a metal alkoxide with a functionality greater than 2.

10. The electrochromic layer according to claim 9 where said at least one electrochromic compound comprises a cathodic electrochromic compound, which is a salt of a dication selected from the group consisting of N, N'"'"'-substituted 4,4'"'"'-dipyridyls with hydrogen at all of the 2, 2'"'"', 6, and 6'"'"' positions and with the N and N'"'"' substituents being the same or different and each being selected from the group consisting of alkyl groups of 1-10 carbons, phenyl, benzyl, 2-phenylethyl, 3-phenyl(n-propyl), and 4-phenyl(n-butyl) and N, N'"'"'-substituted dipyridyls with an alkyl group of 1-4 carbons at each of the 2, 2'"'"', 6, and 6'"'"' positions and with the N and N'"'"' substituents being the same or different and each being selected from the group consisting of alkyl groups of 1-10 carbons, benzyl, 2-phenylethyl, 3-phenyl(n-propyl), and 4-phenyl(n-butyl).

11. The electrochromic layer according to claim 10 where said at least one electrochromic compound further comprises an anodic electrochromic compound, which is selected from the group consisting of 5,10-dihydro-5,10-dimethylphenazine, N,N,N'"'"',N'"'"'-tetramethyl-p-phenylene-diamine, N,N,N'"'"',N'"'"'-tetraphenyl-p-phenylene-diamine, bis-3,3'"'"'-diethyl-2,2'"'"'-benzothiazole azine, and tetrathiafulvalene.

12. The electrochromic layer according to claim 10 where said at least one electrochromic compound further comprises an anodic electrochromic compound, which is 5,10-dihydro-5,10-dimethylphenazine.

13. The electrochromic layer according to claim 12 where said cathodic electrochromic compound is a salt of 1,1 '"'"'-di(3-phenyl(n-propyl))-4,4'"'"'-dipyridinium.

14. The electrochromic layer according to claim 13 where the salt is a fluoroborate.

15. The electrochromic layer according to claim 13 where said solvent is propylene carbonate.

16. An electrochromic device which comprises, as the medium of reversibly variable transmittance to light, the electrochromic layer of claim 14.

17. A variable transmittance electrochromic window which comprises, as the medium of reversibly variable transmittance to light, the electrochromic layer of claim 13.

18. An electrochromic layer according to claim 8 where said polymer chains are cross-linked by reaction with a polyisocyanate.

19. The electrochromic layer according to claim 18 where said polyisocyanate is selected from the group consisting of isophorone diisocyanate, a polyisocyanate containing biuret groups, and a polyisocyanate containing an isocyanurate ring, and said polyol is selected from the group consisting of polyester polyols and polyether polyols.

20. The electrochromic layer according to claim 19 where said polymer chains are selected from the group consisting of a polyol made from diethylene glycol and adipic acid, and a polyol made from diethylene glycol, adipic acid and trimethylol propane.

21. The electrochromic layer according to claim 18 where the reaction between said polymer chains and said polyisocyanate is catalyzed by a catalyst selected from the group consisting of tin-based polyurethane polymerization catalysts, platinum-based polyurethane polymerization catalysts, and amine-based polyurethane polymerization catalysts.

22. The electrochromic layer according to claim 21 where said catalyst is selected from the group consisting of dibutyltin dilaurate and dibutyltin diacetate.

23. An electrochromic device which comprises, as the medium of reversibly variable transmittance to light, the electrochromic layer of claim 22.

24. A variable transmittance electrochromic window which comprises, as the medium of reversibly variable transmittance to light, the electrochromic layer of claim 22.

25. The electrochromic layer according to claim 8 where said polymer chains are cross-linked by reaction with a metal alkoxide.

26. The electrochromic layer according to claim 25 where the metal alkoxide is tetramethyl orthosilicate.

27. The electrochromic layer according to claim 26 where said polymer chains are formed from a mono hydroxy caprolactone acrylate, in the presence of an azo thermal initiator.

28. An electrochromic device which comprises, as the medium of reversibly variable transmittance to light, the electrochromic layer of claim 26.

29. A variable transmittance electrochromic window which comprises, as the medium of reversibly variable transmittance to light, the electrochromic layer of claim 26.

30. The electrochromic layer according to claim 8 where said polymer chain lengthening takes place in the presence of an azo thermal initiator.

31. The electrochromic layer according to claim 30 where said polymer chain is a polyacrylate polyol.

32. The electrochromic layer according to claim 31 where said polymer chains are formed from a mono hydroxy caprolactone acrylate.

33. The electrochromic layer according to claim 8 where said polymer chains have a hydroxyl functionality greater than 2 and are cross-linked by reaction with a bisketene.

34. The electrochromic layer according to claim 33 where said bisketene is 9,10 -hydroanthracene-9,10-bisketene.

35. The electrochromic layer according to claim 34 where said cross-linked polymer matrix is catalyst-free.

36. An electrochromic device which comprises, as the medium of reversibly variable transmittance to light, the electrochromic layer of claim 35.

37. A variable transmittance electrochromic window which comprises, as the medium of reversibly variable transmittance to light, the electrochromic layer of claim 35.

38. The electrochromic layer according to claim 8 where said solvent is a liquid at room temperature and is selected from the group consisting of acetonitrile, propionitrile, dimethylformamide, dimethylsulfoxide, glutaronitrile, propylene carbonate, isobutylene carbonate, gamma-butyrolactone, gamma-valerolactone, any homogeneous mixture that is liquid at room temperature of any two or more of propylene carbonate, isobutylene carbonate, gamma-butyrolactone, and gamma-valerolactone, and any homogenous mixture that is liquid at room temperature of any one or more of propylene carbonate, isobutylene carbonate, gamma-butyrolactone, and gamma-valerolactone with ethylene carbonate.

39. The electrochromic layer according to claim 38 where said solvent and said at least one electrochromic compound comprise between at least 50% by weight of said electrochromic layer and less than the percentage by weight at which room temperature formation of a free-standing gel does not occur.

40. The electrochromic layer according to claim 8 which is self-erasing.

41. An electrochromic device which comprises, as the medium of reversibly variable transmittance to light, the electrochromic layer of claim 8.

42. A variable transmittance electrochromic window which comprises, as the medium of reversibly variable transmittance to light, the electrochromic layer of claim 8.

43. The electrochromic window according to claim 42 where said monomers are polymerized to form said polymer chains prior to insertion into said electrochromic window and where said polymer chains are crosslinked within said window to form said polymer matrix.

44. An electrochromic layer of reversibly variable transmittance to light which comprises:

(a) a catalyst-free polymer matrix of a polyol polymer; and

(b) an electrochromic solution which comprises at least one electrochromic compound interspersed in the polymer matrix.

45. The electrochromic layer according to claim 44 where said polyol polymer has a hydroxyl functionality greater than 2 and the polyol polymer chains are cross-linked by reaction with a bisketene.

46. The electrochromic layer according to claim 45 where said bisketene is 9,10-hydroanthracene-9,10-bisketene.