Polysulfone semipermeable membrane and method of manufacturing the same

• US 5,888,605 A
• Filed: 10/25/1996
• Issued: 03/30/1999
• Est. Priority Date: 10/31/1995
• Status: Expired due to Fees

• Current Assignee: Nitto Denko Corporation
• Original Assignee: Nitto Denko Corporation
• Inventors: Ikeda, Kenichi, Hachisuka, Hisao
• Primary Examiner(s): Achutamurthy, Ponnathapura
• Assistant Examiner(s): PARK, HANKYEL
• Application Number:
  US08/738,267
• Time in Patent Office: 886 Days
• Field of Search: 428/71, 428/215, 428/318.8, 428/319.3, 210/500.41
• US Class Current: 428/71
• CPC Class Codes: B01D 39/1623 of synthetic origin
• CPC Class Codes: B01D 39/2017 the material being filamentary or fibrous
• CPC Class Codes: Y10T 428/233 Foamed or expanded material encased
• CPC Class Codes: Y10T 428/24967 Absolute thicknesses specified
• CPC Class Codes: Y10T 428/249989 Integrally formed skin
• CPC Class Codes: Y10T 428/249991 Synthetic resin or natural rubbers

Abstract

The semipermeable membrane of polysulfone resin is formed of a continuous structure of a homogeneous skin layer part having an average thickness of 5 to 1000 nm and a porous layer which is made of the same material as that of the homogeneous skin layer and is thicker than the homogeneous skin layer, and the porous layer is formed of a structure having voids having an average pore diameter less than 3 μm. Therefore, a gas separation membrane that has high permeation flux and requires practically satisfactory cost can be provided. Diethylene glycol dimethyl ether was added to polysulfone for dissolution, and the resultant solution was defoamed for preparation. The solution was cast on a support layer of polyester non-woven fabric using an applicator, dipped in water as a solidifying liquid, and dried. As a result, a semipermeable membrane comprising a homogeneous skin layer part and a porous layer is obtained. A crosslinking silicone resin solution may be applied to the surface of the membrane to form a protective film.

Claims

1. A polysulfone semipermeable membrane comprising a semipermeable membrane of polysulfone resin formed of a continuous structure of a homogeneous skin layer having an average thickness of 5 to 1000 nm and a porous layer which is made of the same material as that of said homogeneous skin layer and is thicker than said homogeneous skin layer, wherein said porous layer is formed of a structure having voids with an average pore diameter less than 3 μ

m.

2. The polysulfone semipermeable membrane according to claim 1, wherein, in the void structure, when the thickness of the homogeneous skin layer is (L1), and a length (Lx) and width (Ly) are the external rectangular dimensions of a pore in a porous layer having thickness (L2=L1×

10), at least 70% of the opening parts satisfy 10 nm≦

Lx≦

1000 nm and 10 nm≦

Ly≦

1000 nm respectively.

3. The polysulfone semipermeable membrane according to claim 1, wherein, when the homogeneous skin layer having thickness (L1) is observed at ×

50,000 magnification using a scanning electron microscope with a field emission electron gun (FE-SEM) to produce a binary image in monochrome 256 gradation, the average luminance in 256 gradation of the skin layer is 100 or more, and the standard deviation is 50 or less.

4. The polysulfone semipermeable membrane according to claim 1, wherein, when the thickness of the homogeneous skin layer is (L1), when the porous layer having thickness (L2=L1×

10) is observed at ×

50,000 magnification using a scanning electron microscope with a field emission electron gun (FE-SEM) to produce a binary image in monochrome 256 gradation, and when a part obtained by image analysis which has an average boundary value (threshold) or less in 256 gradation in the image is a pore part, 40% or more of the porous layer is occupied by the pore part.

5. The polysulfone semipermeable membrane according to claim 1, wherein, when the homogeneous skin layer having thickness (L1) and the porous layer having thickness (L2=L1×

10) are observed at ×

50,000 magnification using a scanning electron microscope with a field emission electron gun (FE-SEM) to produce a binary image in monochrome 256 gradation, the average luminance ratio in 256 gradation of the (L1) part to the (L2) part (=luminance (L1)/luminance (L2)) is 1.5 or more.

6. The polysulfone semipermeable membrane according to claim 1, wherein a protective thin film of elastomer polymer is further formed on the skin layer of the polysulfone semipermeable membrane.

7. The polysulfone semipermeable membrane according to claim 6, wherein the protective thin film of elastomer polymer is a layer in which a crosslinkable silicone resin is crosslinked.