Oxide coated cutting tool with increased wear resistance and method of manufacture thereof

• US 5,902,671 A
• Filed: 07/03/1996
• Issued: 05/11/1999
• Est. Priority Date: 07/14/1995
• Status: Expired due to Fees

• Current Assignee: Sandvik Intellectual Property AB (Sandvik AB)
• Original Assignee: Sandvik AB
• Inventors: Kutscher, Åsa
• Primary Examiner(s): TURNER, ARCHENE A
• Application Number:
  US08/675,678
• Time in Patent Office: 1,042 Days
• Field of Search: 407/117, 51/307, 51/309, 428/216, 428/212, 428/457, 428/469, 428/697, 428/698, 428/701, 428/702, 427/255, 427/255.2, 427/255.3, 427/255.7, 427/419.2, 427/419.7, 427/126.1
• US Class Current: 428/216
• CPC Class Codes: C23C 16/403 of aluminium, magnesium or beryllium
• CPC Class Codes: C23C 30/005 on hard metal substrates
• CPC Class Codes: Y10T 407/27 comprising tool of specific chemical composition
• CPC Class Codes: Y10T 428/24942 including components having same physical characteristic in differing degree
• CPC Class Codes: Y10T 428/24975 No layer or component greater than 5 mils thick
• CPC Class Codes: Y10T 428/31678 Of metal
• CPC Class Codes: Y10T 428/31815 Of bituminous or tarry residue

Abstract

An oxide coated cutting tool including a body coated with refractory single- or multilayers one of which consists of single-phase κ-Al₂ O₃ characterized by controlled microstructure with crystal planes preferably grown in the (210)-direction with respect to the exposed surface of the coated body. The oxide coated cutting tool exhibits increased wear properties when machining ball bearing steel.

Claims

1. A coated cutting tool body at least partially coated with one or more refractory layers of which at least one is alumina, said alumina layer having a coating thickness of 0.5-25 μ

m and consisting essentially of single-phase κ

-Al₂ O₃ textured in the (210)-direction with a texture coefficient larger than 1.5, the texture coefficient being defined as below;

##EQU2## where I(hkl)=measured intensity of the (hkl) reflection

I₀ (hkl)=standard intensity of the ASTM standard powder pattern diffraction data; and

n=number of reflections used in the calculation, (hkl) reflections used are;

(002), (112), (013), (122), (113), (032), (210), (222), (050).

2. The coated cutting tool body according to claim 1, wherein said alumina layer is the outermost layer.

3. The coated cutting tool body according to claim 1, wherein said alumina layer is in contact with a TiC_x N_y O_z layer.

4. The coated cutting tool body according to claim 3, wherein said TiC_x N_y O_z layer is an innermost layer of the coating.

5. The coated cutting tool body according to claim 1, wherein on top of said alumina layer is a ≦

1 μ

m thick TiN-layer.

6. The coated cutting tool body according to claim 1, wherein said body is a cutting tool of cemented carbide, titanium based carbonitride or ceramics.

7. The coated cutting tool according to claim 1, wherein TC(210) is larger than 2.5.

8. The coated cutting tool according to claim 1, wherein TC(210) is larger than 3.0.

9. The coated cutting tool according to claim 1, wherein the alumina coating has a thickness of 1-10 μ

m and/or grain size of 0.5-6 μ

m.

10. A method of coating a body with a κ

-alumina coating, according to claim 1 the method comprising introducing the body into a reactor, contacting the body with process gases including a hydrogen carrier gas containing one or more halides of aluminum and a hydrolyzing and/or oxidizing agent at high temperature and depositing the κ

-alumina coating on the body, the process gases having a low oxidation potential prior to nucleation of the alumina coating by maintaining a total concentration of H₂ O or other oxidizing species below 5 ppm, the nucleation of alumina being initiated by controlled sequencing of the process gases such that HCl first enters the reactor in a H₂ atmosphere followed by AlCl₃ and then CO₂, the amount of HCl being controlled to be 2.5-10% by volume, the temperature being between 950-1000°

C. during the nucleation and a sulphur containing gas being added during the growth of the Al₂ O₃.

11. The method of coating a body with a κ

-alumina coating according to claim 10, wherein the body comprises a cutting tool insert and the amount of HCl is controlled to be 3.5-5% by volume.

12. The method of coating a body with a κ

-alumina coating according to claim 10, the alumina coating being subjected to a post-treatment.

13. The method of coating a body with a κ

-alumina coating according to claim 10, wherein the sulfur containing gas comprises H₂ S.

14. The method of coating a body with a κ

-alumina coating according to claim 10, wherein the body comprises a cutting tool body and the alumina coating has a thickness of 0.5-25 μ

m and consists essentially of single-phase κ

-Al₂ O₃ textured in the (210)-direction with a texture coefficient larger than 1.5, the texture coefficient being defined as below;

##EQU3## where I(hkl)=measured intensity of the (hkl) reflection

I₀ (hkl)=standard intensity of the ASTM standard powder pattern diffraction data; and

n=number of reflections used in the calculation, (hkl) reflections used are;

(002), (112), (013), (122), (113), (032), (210), (222), (050).

15. The method of coating a body with a κ

-alumina coating according to claim 10, wherein the alumina coating is an outermost layer.

16. The method of coating a body with a κ

-alumina coating according to claim 10, wherein the alumina coating is in contact with a TiC_x N_y O_z layer.

17. The method of coating a body with a κ

-alumina coating according to claim 16, wherein the TiC_x N_y O_z layer is an innermost layer.

18. The method of coating a body with a κ

-alumina coating according to claim 10, wherein on top of the alumina coating is a ≦

1 μ

m thick TiN-layer.

19. The method of coating a body with a κ

-alumina coating according to claim 10, wherein the body is a cutting tool of cemented carbide, titanium based carbonitride or ceramics.

20. The coated cutting tool body according to claim 1, prepared by coating a body with a κ

-alumina coating, the method comprising introducing the body into a reactor, contacting the body with process gases including a hydrogen carrier gas containing one or more halides of aluminum and a hydrolyzing and/or oxidizing agent at high temperature and depositing the κ

-alumina coating on the body, the process gases having a low oxidation potential prior to nucleation of the alumina coating by maintaining a total concentration of H₂ O or other oxidizing species below 5 ppm, the nucleation of alumina being initiated by controlled sequencing of the process gases such that HCl first enters the reactor in a H₂ atmosphere followed by AlCl₃ and then CO₂, the amount of HCl being controlled to be 2.5-10% by volume, the temperature being between 950-1000°

C. during the nucleation and a sulphur containing gas being added during the growth of the Al₂ O₃.